The evolutionary density and the scatter of densities of the short fatigue cracks on the surface of 1Cr18Ni9Ti pipe-weld metal were observed by local and overall viewpoints, respectively. The local viewpoint, which is...The evolutionary density and the scatter of densities of the short fatigue cracks on the surface of 1Cr18Ni9Ti pipe-weld metal were observed by local and overall viewpoints, respectively. The local viewpoint, which is in accordance with a so-called "effectively short fatigue crack criterion", paid attention to the dominant effective short fatigue crack (DESFC) initiation zone and the zones ahead of the DESFC tips. The overall viewpoint focused on the whole test piece of specimen. The results revealed that the density and scatter evolution exhibited a significant character of microstructural short crack and physical short crack stages. The evolutionary behavior by the local viewpoint was sensitive to the increase of DESFC size and tip location. The mechanism of the short crack growth associated with the general test observations that the DESFC acted gradually as a long crack and the scatter of DESFC growth rates tended gradually to that of a long crack was well revealed. Intrinsic causes of the random cyclic strain-life relations and stress-strain responses are appropriately given. In contrast, the evolutionary behavior by the overall viewpoint was non-sensitive and violated the general test observations. Therefore, the intrinsic localization and randomization of material evolutionary fatigue damage should be more appropriately revealed from the observations by the local viewpoint.展开更多
Size evolution of the surface short fatigue cracks of lCrl8Ni'9Ti weld metal was investigated. A local viewpoint is applied to be agreement with a so-called 'effectively short fatigue crack criterion'. Att...Size evolution of the surface short fatigue cracks of lCrl8Ni'9Ti weld metal was investigated. A local viewpoint is applied to be agreement with a so-called 'effectively short fatigue crack criterion'. Attention was paid to the dominant effectively short fatigue crack (DESFC) initiation zone and the zones ahead of the DESFC tips. The results revealed that the evolutionary size shows a significant character of microstructural short crack (MSC) and physical short crack (PSC) stages. In the MSC stage, fatigue damage is due to mainly the initiation and irregular growth of the effectively short fatigue cracks (ESFCs). In the PSC stage, the damage is conversely due to mainly the DESFC growth and partially, the growth of the ESFCs and the coalescence of the ESFCs themselves with the DESFC. The process involves from a non-ordered/chaotic state in the initiation of MSC stage, gradually to an independently random state at the transition point between the MSC and PSC stages and then, to an ordered/history-dependent random state. Interactive effect of the collective cracks is stronger and shows an increase in the MSC stage, it reaches a maximum value at the transition point and then, tends to a decrease in the PSC stage. The DESFC acts as a result of the interactive cracks and thus, is deemed suitable to describe the behaviour of collective cracks.展开更多
文摘The evolutionary density and the scatter of densities of the short fatigue cracks on the surface of 1Cr18Ni9Ti pipe-weld metal were observed by local and overall viewpoints, respectively. The local viewpoint, which is in accordance with a so-called "effectively short fatigue crack criterion", paid attention to the dominant effective short fatigue crack (DESFC) initiation zone and the zones ahead of the DESFC tips. The overall viewpoint focused on the whole test piece of specimen. The results revealed that the density and scatter evolution exhibited a significant character of microstructural short crack and physical short crack stages. The evolutionary behavior by the local viewpoint was sensitive to the increase of DESFC size and tip location. The mechanism of the short crack growth associated with the general test observations that the DESFC acted gradually as a long crack and the scatter of DESFC growth rates tended gradually to that of a long crack was well revealed. Intrinsic causes of the random cyclic strain-life relations and stress-strain responses are appropriately given. In contrast, the evolutionary behavior by the overall viewpoint was non-sensitive and violated the general test observations. Therefore, the intrinsic localization and randomization of material evolutionary fatigue damage should be more appropriately revealed from the observations by the local viewpoint.
基金Present work is supported by the National Natural Science Foundation of China (50075073), the Special Foundation for the Authors of National Excellent Ph.D. Theses (2002067), the Excellent Young Teachers Program of MOE, PRO (EYTP 2101) and the Provincial
文摘Size evolution of the surface short fatigue cracks of lCrl8Ni'9Ti weld metal was investigated. A local viewpoint is applied to be agreement with a so-called 'effectively short fatigue crack criterion'. Attention was paid to the dominant effectively short fatigue crack (DESFC) initiation zone and the zones ahead of the DESFC tips. The results revealed that the evolutionary size shows a significant character of microstructural short crack (MSC) and physical short crack (PSC) stages. In the MSC stage, fatigue damage is due to mainly the initiation and irregular growth of the effectively short fatigue cracks (ESFCs). In the PSC stage, the damage is conversely due to mainly the DESFC growth and partially, the growth of the ESFCs and the coalescence of the ESFCs themselves with the DESFC. The process involves from a non-ordered/chaotic state in the initiation of MSC stage, gradually to an independently random state at the transition point between the MSC and PSC stages and then, to an ordered/history-dependent random state. Interactive effect of the collective cracks is stronger and shows an increase in the MSC stage, it reaches a maximum value at the transition point and then, tends to a decrease in the PSC stage. The DESFC acts as a result of the interactive cracks and thus, is deemed suitable to describe the behaviour of collective cracks.