Ink-jet printing of ceramic thick films is one of low cost on-site ceramic pattern fabrication methods.It is necessary to investigate the rheological behaviour of ceramic inks and drying behaviour of droplets.Two kind...Ink-jet printing of ceramic thick films is one of low cost on-site ceramic pattern fabrication methods.It is necessary to investigate the rheological behaviour of ceramic inks and drying behaviour of droplets.Two kinds of BaTiO3 ceramic inks were prepared by mechanical mixing and sol-gel methods,respectively.The effect of preparation parameters,such as quantity of polyacrylic acid(PAA)and solid content,on physicochemical and rheologic properties of the ceramic inks was investigated.The results show that they satisfy the requirements of continuous ink-jet printing.The appearances of printed dots and single printed layers were observed by SEM.The SEM images indicate that dots printed with mixing method ink are in ring shape,and dots printed with sol-gel method ink are in pancake shape,so the printed layer surface with the latter ink is smoother.The causes of these phenomena were discussed.展开更多
Cu_(2)ZnSnS_(4)薄膜因其元素地壳含量丰富、无毒且具有优异的光电性能,受到研究者的广泛关注。本文基于纳米墨水法用Cd部分取代Zn制成了Cu_(2)(Cd x Zn_(1-x))SnS_(4)(CCZTS)薄膜,研究退火时间和后退火温度对薄膜及其太阳电池性能的影...Cu_(2)ZnSnS_(4)薄膜因其元素地壳含量丰富、无毒且具有优异的光电性能,受到研究者的广泛关注。本文基于纳米墨水法用Cd部分取代Zn制成了Cu_(2)(Cd x Zn_(1-x))SnS_(4)(CCZTS)薄膜,研究退火时间和后退火温度对薄膜及其太阳电池性能的影响。研究结果表明,所制备的薄膜为CCZTS相,无其他杂相,薄膜表面平整且致密,结晶性较好。随着退火时间增加,薄膜的晶粒尺寸有所增大,薄膜太阳电池的pn结质量得到提升,其性能也随之提高。通过对薄膜太阳电池进行后退火处理,分析了吸收层的元素扩散对电池性能的影响,在Cd元素形成梯度分布时,电池性能有所提高。随着后退火温度的增加,其电池性能和pn结质量呈现先提高后下降的趋势。经后退火300℃处理后,电池转换效率最佳,为3.13%。展开更多
基金Project(106151)supported by the Major Program of the Ministry of Education of ChinaProject(59842001)supported by the National Natural Science Foundation of China
文摘Ink-jet printing of ceramic thick films is one of low cost on-site ceramic pattern fabrication methods.It is necessary to investigate the rheological behaviour of ceramic inks and drying behaviour of droplets.Two kinds of BaTiO3 ceramic inks were prepared by mechanical mixing and sol-gel methods,respectively.The effect of preparation parameters,such as quantity of polyacrylic acid(PAA)and solid content,on physicochemical and rheologic properties of the ceramic inks was investigated.The results show that they satisfy the requirements of continuous ink-jet printing.The appearances of printed dots and single printed layers were observed by SEM.The SEM images indicate that dots printed with mixing method ink are in ring shape,and dots printed with sol-gel method ink are in pancake shape,so the printed layer surface with the latter ink is smoother.The causes of these phenomena were discussed.
文摘Cu_(2)ZnSnS_(4)薄膜因其元素地壳含量丰富、无毒且具有优异的光电性能,受到研究者的广泛关注。本文基于纳米墨水法用Cd部分取代Zn制成了Cu_(2)(Cd x Zn_(1-x))SnS_(4)(CCZTS)薄膜,研究退火时间和后退火温度对薄膜及其太阳电池性能的影响。研究结果表明,所制备的薄膜为CCZTS相,无其他杂相,薄膜表面平整且致密,结晶性较好。随着退火时间增加,薄膜的晶粒尺寸有所增大,薄膜太阳电池的pn结质量得到提升,其性能也随之提高。通过对薄膜太阳电池进行后退火处理,分析了吸收层的元素扩散对电池性能的影响,在Cd元素形成梯度分布时,电池性能有所提高。随着后退火温度的增加,其电池性能和pn结质量呈现先提高后下降的趋势。经后退火300℃处理后,电池转换效率最佳,为3.13%。