The diffusion behavior and reactions between AI and Ca in Mg alloys by diffusion couple method were investigated. Results demonstrate that Al2Ca is the only phase existing in the diffusion reaction layers. The volume ...The diffusion behavior and reactions between AI and Ca in Mg alloys by diffusion couple method were investigated. Results demonstrate that Al2Ca is the only phase existing in the diffusion reaction layers. The volume fraction of Al2Ca in diffusion reaction layers increases linearly with temperature. The standard enthalpy of formation for intermetallic compounds was rationalized on the basis of the Miedema model. Al-Ca intermetallic compounds were preferable to form in the Mg-Al-Ca ternary system under the same conditions. Over the range of 350-400℃, the structure of Al2Ca is more stable than that of Al4Ca, Al14Ca13and Al3Ca8, The growth constants of the layer I, layer II and entire diffusion reaction layers were determined. The activation energies for the growth of the layer I, layer II and entire diffusion reaction layers were （80.74 ± 3.01 ） kJ/mol, （93.45 ±2.12） kJ/mol and （83.52 ±1.50） kJ/mot, respectively. In layer I and II, AI has higher integrated interdiffusion coefficients D^i^Int,layer layer than Ca. The average effective interdiffusion coefficients D^Al^eff values are higher than D^Ca^eff in the layer I and II.展开更多
基金financial supports from the Scientific and Technological Research Program of Chongqing Municipal Education Commission (KJ1712301, KJ1601302)Chongqing Science and Technology Commission (cstc2017jcyj AX0394, cstc2017jcyj A1019)+1 种基金the Research Foundation of Yangtze Normal University (2016RYQD15, 2016XJQN32)the National Natural Science Foundation of China (51701033)
文摘The diffusion behavior and reactions between AI and Ca in Mg alloys by diffusion couple method were investigated. Results demonstrate that Al2Ca is the only phase existing in the diffusion reaction layers. The volume fraction of Al2Ca in diffusion reaction layers increases linearly with temperature. The standard enthalpy of formation for intermetallic compounds was rationalized on the basis of the Miedema model. Al-Ca intermetallic compounds were preferable to form in the Mg-Al-Ca ternary system under the same conditions. Over the range of 350-400℃, the structure of Al2Ca is more stable than that of Al4Ca, Al14Ca13and Al3Ca8, The growth constants of the layer I, layer II and entire diffusion reaction layers were determined. The activation energies for the growth of the layer I, layer II and entire diffusion reaction layers were （80.74 ± 3.01 ） kJ/mol, （93.45 ±2.12） kJ/mol and （83.52 ±1.50） kJ/mot, respectively. In layer I and II, AI has higher integrated interdiffusion coefficients D^i^Int,layer layer than Ca. The average effective interdiffusion coefficients D^Al^eff values are higher than D^Ca^eff in the layer I and II.