Top and bottom NiO-pinning spin valves of Si/Ta/NiO/Co/Cu/Co/Ta and Si/Ta/Co/Cu/Co/NiO/Ta were prepared by magnetron sputtering, and X-ray diffraction and giant magnetoresistance （GMR） ratio were measured in the tem...Top and bottom NiO-pinning spin valves of Si/Ta/NiO/Co/Cu/Co/Ta and Si/Ta/Co/Cu/Co/NiO/Ta were prepared by magnetron sputtering, and X-ray diffraction and giant magnetoresistance （GMR） ratio were measured in the temperature range from 5 to 300 K. For the bottom spin valve, the interracial roughness at NiO/Co is much smaller than that of Co/NiO in the top one. The Co/Cu and Cu/Co interfaces have the same roughness in the bottom and the top spin valves. NiO, Co, and Cu layers have （111） preferred orientations in the top one and random orientations in the bottom one. The GMR ratio of the bottom spin valve is larger than that of the top one at all temperatures and their difference increases with decreasing temperature.展开更多
基金the National Natural Science Foundation of China （Grant No. 10174014, 60271013, 10321003, 60490290） the State Key Project of Fundamental Research （No. 001CB610602 , 2002CB613504） the Hong Kong RGC Grant （HKUST6165/01P）.
文摘Top and bottom NiO-pinning spin valves of Si/Ta/NiO/Co/Cu/Co/Ta and Si/Ta/Co/Cu/Co/NiO/Ta were prepared by magnetron sputtering, and X-ray diffraction and giant magnetoresistance （GMR） ratio were measured in the temperature range from 5 to 300 K. For the bottom spin valve, the interracial roughness at NiO/Co is much smaller than that of Co/NiO in the top one. The Co/Cu and Cu/Co interfaces have the same roughness in the bottom and the top spin valves. NiO, Co, and Cu layers have （111） preferred orientations in the top one and random orientations in the bottom one. The GMR ratio of the bottom spin valve is larger than that of the top one at all temperatures and their difference increases with decreasing temperature.