The aim of this paper was to study the reaction between a Ti-6Al-4V alloy and boron nitride based investment shell molds used for investment casting titanium. In BN based investment shell molds, the face coatings are ...The aim of this paper was to study the reaction between a Ti-6Al-4V alloy and boron nitride based investment shell molds used for investment casting titanium. In BN based investment shell molds, the face coatings are made of pretreated hexagonal boron nitride （hBN） with a few yttria （Y2O3） and colloidal yttria as binder. The Ti-6Al-4V alloy was melted in a controlled atmosphere induction furnace with a segment water-cooled copper crucible. The cross-section of reaction interface between Ti alloys and shell mold was investigated by electron probe micro-analyzer （EPMA） and microhardness tester. The results show that the reaction is not serious, the thickness of the reacting layer is about 30-50 μm, and the thickness of α-case is about 180-200 pro. Moreover the α-case formation mechanism was also discussed.展开更多
At present, most TiAl components are produced by an investment casting process. Environmental and economic pressures have, however, resulted in a need for the industry to improve the current casting quality, reduce ma...At present, most TiAl components are produced by an investment casting process. Environmental and economic pressures have, however, resulted in a need for the industry to improve the current casting quality, reduce manufacturing costs and explore new markets for the process. Currently, the main problems for investment casting of TiAl alloys are cracks, porosities, and surface defects. To solve these problems, many studies have been conducted around the world, and it is found that casting defects can be reduced by improving composition and properties of the shell molds. It is important to make a summary for the related research progress for quality improvement of TiAl castings. So, the development on refractory composition of shell molds for TiAl alloy investment castings was reviewed, and research progress on deformability of shell mold for TiAl alloy castings both at home and abroad in recent years was introduced. The existing methods for deformability characterization and methods for improving the deformability of shell molds were summarized and discussed. The updated advancement in numerical simulation of TiAl alloy investment casting was presented, showing the necessity for considering the deformability of shell mold during simulation. Finally, possible research points for future studies on deformability of shell mold for TiAl alloy investment casting were proposed.展开更多
文摘The aim of this paper was to study the reaction between a Ti-6Al-4V alloy and boron nitride based investment shell molds used for investment casting titanium. In BN based investment shell molds, the face coatings are made of pretreated hexagonal boron nitride （hBN） with a few yttria （Y2O3） and colloidal yttria as binder. The Ti-6Al-4V alloy was melted in a controlled atmosphere induction furnace with a segment water-cooled copper crucible. The cross-section of reaction interface between Ti alloys and shell mold was investigated by electron probe micro-analyzer （EPMA） and microhardness tester. The results show that the reaction is not serious, the thickness of the reacting layer is about 30-50 μm, and the thickness of α-case is about 180-200 pro. Moreover the α-case formation mechanism was also discussed.
基金financially supported by the Technical Development Foundation of China Academy of Machinery Science and Technology under project:Investment Casting Technology Research for TiAl Alloy Turbocharger Turbine
文摘At present, most TiAl components are produced by an investment casting process. Environmental and economic pressures have, however, resulted in a need for the industry to improve the current casting quality, reduce manufacturing costs and explore new markets for the process. Currently, the main problems for investment casting of TiAl alloys are cracks, porosities, and surface defects. To solve these problems, many studies have been conducted around the world, and it is found that casting defects can be reduced by improving composition and properties of the shell molds. It is important to make a summary for the related research progress for quality improvement of TiAl castings. So, the development on refractory composition of shell molds for TiAl alloy investment castings was reviewed, and research progress on deformability of shell mold for TiAl alloy castings both at home and abroad in recent years was introduced. The existing methods for deformability characterization and methods for improving the deformability of shell molds were summarized and discussed. The updated advancement in numerical simulation of TiAl alloy investment casting was presented, showing the necessity for considering the deformability of shell mold during simulation. Finally, possible research points for future studies on deformability of shell mold for TiAl alloy investment casting were proposed.