Two new Gd Ⅲ complexes with nitrilotriacetic acid(nta) and trans-1,2-cyclohexanediaminetetraacetic acid(Cydta) ligands were synthesized. Their crystal structures were determined by single-crystal X-ray structure anal...Two new Gd Ⅲ complexes with nitrilotriacetic acid(nta) and trans-1,2-cyclohexanediaminetetraacetic acid(Cydta) ligands were synthesized. Their crystal structures were determined by single-crystal X-ray structure analyses. The crystal data are as follows: K 3[Gd Ⅲ(nta) 2·(H 2O)]·6H 2O, monoclinic system, C2/c space group, a=1.534 81(15) nm, b=1.292 05(12) nm, c=2.610 8(3) nm, β=96.244(2)°, V=5.146 7(9) nm 3, Z=8, M=776.87, D c=2.005 g/cm 3, μ= 3.149 mm -1 and \{F(000)=\}3 080, R=0.024 5, wR=0.064 3 for 4 455 unique reflections and R= 0.028 9, wR=0.067 2 for all 10 305 reflections. The Gd ⅢN 2O 7 part in the [Gd Ⅲ(nta) 2(H 2O)] 3- anion is a pseudo-monocapped square antiprismatic nine-coordination structure.(NH 4)[Gd Ⅲ(Cydta)(H 2O) 2]·5H 2O, triclinic system, P1 space group, a=0.866 2(3) nm, b=1.006 7(3) nm, c= 1.444 8(5) nm, α= 88.282(5)°, β=75\^190(5)°, γ=88.317(4)°, V=1.217 2(7) nm 3, Z=2, M=643.69, D c=1.756 g/cm 3, μ=2.798 mm -1 and F(000)=650, R=0.030 3, wR=0.080 9 for 4 273 unique reflections and R=0.033 2, wR=0.082 5 for all 5 062 reflections. The Gd ⅢN 2O 6 part in the [Gd Ⅲ(Cydta)(H 2O) 2] - anion has a pseudo-square antiprismatic eight-coordination structure.展开更多
A series of V2O5‐WO3/TiO2‐ZrO2,V2O5‐WO3/TiO2‐CeO2,and V2O5‐WO3/TiO2‐CeO2‐ZrO2 catalysts were synthesized to improve the selective catalytic reduction(SCR)performance and the K‐poisoning resistance of a V2O5‐W...A series of V2O5‐WO3/TiO2‐ZrO2,V2O5‐WO3/TiO2‐CeO2,and V2O5‐WO3/TiO2‐CeO2‐ZrO2 catalysts were synthesized to improve the selective catalytic reduction(SCR)performance and the K‐poisoning resistance of a V2O5‐WO3/TiO2 catalyst.The physicochemical properties were investigated by using XRD,BET,NH3‐TPD,H2‐TPR,and XPS,and the catalytic performance and K‐poisoning resistance were evaluated via a NH3‐SCR model reaction.Ce^4+and Zr^4+co‐doping were found to enhance the conversion of NOx,and exhibit the best K‐poisoning resistance owing to the largest BET‐specific surface area,pore volume,and total acid site concentration,as well as the minimal effects on the surface acidity and redox ability from K poisoning.The V2O5‐WO3/TiO2‐CeO2‐ZrO2 catalyst also presents outstanding H2O+SO2 tolerance.Finally,the in situ DRIFTS reveals that the NH3‐SCR reaction over the V2O5‐WO3/TiO2‐CeO2‐ZrO2 catalyst follows an L‐H mechanism,and that K poisoning does not change the reaction mechanism.展开更多
A new compound K6Ti0.67Nb15.33O42 was prepared for the first time by solid state reaction in K2O-Ni2O3-Nb2O5 ternary system. The new compound was characterized by electron probe, X-ray powder diffraction and DTA. The ...A new compound K6Ti0.67Nb15.33O42 was prepared for the first time by solid state reaction in K2O-Ni2O3-Nb2O5 ternary system. The new compound was characterized by electron probe, X-ray powder diffraction and DTA. The result of X-ray powder diffraction shows that K6Ti0.67Nb15.33O42 crystallizes the hexagonal system with unit cell parameters a = 9. 1341(5) A ,c=12. 090(1)A . and space group P62/mcm(193 ).展开更多
A new compound K6FeNb15O42 u(?) prepared for the first time by solid state reaction in K2O-Fe2O3-Nb2O5 ternary system. The XRD data of the title compound was determined. K6FeNb15O42 crystallizes the hexagonal system w...A new compound K6FeNb15O42 u(?) prepared for the first time by solid state reaction in K2O-Fe2O3-Nb2O5 ternary system. The XRD data of the title compound was determined. K6FeNb15O42 crystallizes the hexagonal system with unit cell parameters a=9. 1320(4) A,c=12. 0670(9) A, and space group P63/mcm(193) , 2=1. The calculated and measured densities are 4. 489 g/ cm3 and 4. 485 g. cm3, respectively.展开更多
A new compound K6FeNb15O42 was prepared for the first time by solid state reaction in K2O-Fe2O3-Nb2O5 ternary system. The X-ray powder diffraction data of the title compound was measured. K6FeNb15 O42 crystallizes in ...A new compound K6FeNb15O42 was prepared for the first time by solid state reaction in K2O-Fe2O3-Nb2O5 ternary system. The X-ray powder diffraction data of the title compound was measured. K6FeNb15 O42 crystallizes in the hexagonal system with unit cell parameters, a = 9. 1320(4) A ,c = 12. 0670(9) A , and space group P63/mcm (193) , z = 1. The calculated and measured densities are 4. 489 g/cm3 and 4. 485 g. cm3, respectively.展开更多
A protocol for the synthesis of some 4-Aryl-1,3,4,6,7,8-hexahydroquinazolin-2,5(1H,6H)-diones (HHQs) was developed by means of a three-component condensation reaction of an aromatic aldehyde, 1,3-cylohexadione and ure...A protocol for the synthesis of some 4-Aryl-1,3,4,6,7,8-hexahydroquinazolin-2,5(1H,6H)-diones (HHQs) was developed by means of a three-component condensation reaction of an aromatic aldehyde, 1,3-cylohexadione and urea in the presence of K3AlF6 (Al2O3/KF) as catalyst. This reaction is carried out under different conditions including 1) solvent free;2) reflux in acetonitrile;3) reflux in ethanol;4) reflux in chloroform;and 5) reflux in water. In all conditions, the desired products are obtained in high yields after relatively short reaction times. Nevertheless, the reactions proceed faster and in higher yields when they were carried out in acetonitrile. This adopted protocol for some Biginelli-type products has offered the advantages of reusability of the catalyst, high yields and ease of separation of pure products. Furthermore, the catalyst is easily prepared, stabilized and efficiently used under reaction conditions.展开更多
A series of new microwave dielectric ceramics Ba3-nLa1+nTinNb3-nO12 (n=0,1,2) were prepared in the BaO-La2O3-TiO2-Nb2O5 system by high temperature solid-state reaction route. The phase and structure of the ceramics we...A series of new microwave dielectric ceramics Ba3-nLa1+nTinNb3-nO12 (n=0,1,2) were prepared in the BaO-La2O3-TiO2-Nb2O5 system by high temperature solid-state reaction route. The phase and structure of the ceramics were characterized by X-ray diffraction, scanning electron microscope, and microwave dielectric properties measurements. These samples were identified as single phase and adopted A4B3O12-type cation-deficient hexagonal perovskite structure, which can be described as consisting of identical perovskite-like blocks, three corner-sharing BO6 octahedra thick, separated by layers of vacant octahedral. These ceramics have high dielectric constants in the range of 48-42, high quality factors (Q×f) up to 38 000 GHz, and low temperature coefficient of resonant frequencies (τf) in the range of (-40-+6)×10-6℃-1. With increasing content of La and Ti, the dielectric constants slightly decrease butτf gradually increases.展开更多
Kinetics of phase transformation from pseudocubic to tetragonal phase in Bi3NbO7 solid solution is studied by using the ac impedance method under isothermal conditions. Conductivity of the investigated compound is use...Kinetics of phase transformation from pseudocubic to tetragonal phase in Bi3NbO7 solid solution is studied by using the ac impedance method under isothermal conditions. Conductivity of the investigated compound is used to characterize the kinetic process of the transition. The Avrami exponent and the activation energy of phase transition are around 1.5 and 3.5eV, respectively. These kinetic parameters reveal that the pseudocubic-tetragonal transition in Bi3NbO7 .belongs to a three-dimensional diffusion-controlled growth with zero nucleation rate.展开更多
文摘Two new Gd Ⅲ complexes with nitrilotriacetic acid(nta) and trans-1,2-cyclohexanediaminetetraacetic acid(Cydta) ligands were synthesized. Their crystal structures were determined by single-crystal X-ray structure analyses. The crystal data are as follows: K 3[Gd Ⅲ(nta) 2·(H 2O)]·6H 2O, monoclinic system, C2/c space group, a=1.534 81(15) nm, b=1.292 05(12) nm, c=2.610 8(3) nm, β=96.244(2)°, V=5.146 7(9) nm 3, Z=8, M=776.87, D c=2.005 g/cm 3, μ= 3.149 mm -1 and \{F(000)=\}3 080, R=0.024 5, wR=0.064 3 for 4 455 unique reflections and R= 0.028 9, wR=0.067 2 for all 10 305 reflections. The Gd ⅢN 2O 7 part in the [Gd Ⅲ(nta) 2(H 2O)] 3- anion is a pseudo-monocapped square antiprismatic nine-coordination structure.(NH 4)[Gd Ⅲ(Cydta)(H 2O) 2]·5H 2O, triclinic system, P1 space group, a=0.866 2(3) nm, b=1.006 7(3) nm, c= 1.444 8(5) nm, α= 88.282(5)°, β=75\^190(5)°, γ=88.317(4)°, V=1.217 2(7) nm 3, Z=2, M=643.69, D c=1.756 g/cm 3, μ=2.798 mm -1 and F(000)=650, R=0.030 3, wR=0.080 9 for 4 273 unique reflections and R=0.033 2, wR=0.082 5 for all 5 062 reflections. The Gd ⅢN 2O 6 part in the [Gd Ⅲ(Cydta)(H 2O) 2] - anion has a pseudo-square antiprismatic eight-coordination structure.
基金supported by National 863 Program Emphasis Project (Nanometer Biology Ware Study, No.2007AA0222006)National Natural Science Foundation of P.R. China(No.30740062 and No.30872970)High School Doctor Subjec Special-purpose Scientific Research Foundation(No.20070286042)
基金supported by the National Natural Science Foundation of China(21876168,21507130)the Key Projects for Common Key Technology Innovation in Key Industries in Chongqing(cstc2016zdcy-ztzx0020-01)+2 种基金the Chongqing Science&Technology Commission(cstc2016jcyjA0070,cstckjcxljrc13)the Open Project Program of Chongqing Key Laboratory of Catalysis and Functional Organic Molecules from Chongqing Technology and Business University(1456029)the Graduate Innovation Project of Chongqing Technology and Business University(yjscxx201803-028-22)~~
文摘A series of V2O5‐WO3/TiO2‐ZrO2,V2O5‐WO3/TiO2‐CeO2,and V2O5‐WO3/TiO2‐CeO2‐ZrO2 catalysts were synthesized to improve the selective catalytic reduction(SCR)performance and the K‐poisoning resistance of a V2O5‐WO3/TiO2 catalyst.The physicochemical properties were investigated by using XRD,BET,NH3‐TPD,H2‐TPR,and XPS,and the catalytic performance and K‐poisoning resistance were evaluated via a NH3‐SCR model reaction.Ce^4+and Zr^4+co‐doping were found to enhance the conversion of NOx,and exhibit the best K‐poisoning resistance owing to the largest BET‐specific surface area,pore volume,and total acid site concentration,as well as the minimal effects on the surface acidity and redox ability from K poisoning.The V2O5‐WO3/TiO2‐CeO2‐ZrO2 catalyst also presents outstanding H2O+SO2 tolerance.Finally,the in situ DRIFTS reveals that the NH3‐SCR reaction over the V2O5‐WO3/TiO2‐CeO2‐ZrO2 catalyst follows an L‐H mechanism,and that K poisoning does not change the reaction mechanism.
基金Funded by International Centre for Diffraction Data.
文摘A new compound K6Ti0.67Nb15.33O42 was prepared for the first time by solid state reaction in K2O-Ni2O3-Nb2O5 ternary system. The new compound was characterized by electron probe, X-ray powder diffraction and DTA. The result of X-ray powder diffraction shows that K6Ti0.67Nb15.33O42 crystallizes the hexagonal system with unit cell parameters a = 9. 1341(5) A ,c=12. 090(1)A . and space group P62/mcm(193 ).
文摘A new compound K6FeNb15O42 u(?) prepared for the first time by solid state reaction in K2O-Fe2O3-Nb2O5 ternary system. The XRD data of the title compound was determined. K6FeNb15O42 crystallizes the hexagonal system with unit cell parameters a=9. 1320(4) A,c=12. 0670(9) A, and space group P63/mcm(193) , 2=1. The calculated and measured densities are 4. 489 g/ cm3 and 4. 485 g. cm3, respectively.
基金Fund by International Centre for Dlffractlon Data.
文摘A new compound K6FeNb15O42 was prepared for the first time by solid state reaction in K2O-Fe2O3-Nb2O5 ternary system. The X-ray powder diffraction data of the title compound was measured. K6FeNb15 O42 crystallizes in the hexagonal system with unit cell parameters, a = 9. 1320(4) A ,c = 12. 0670(9) A , and space group P63/mcm (193) , z = 1. The calculated and measured densities are 4. 489 g/cm3 and 4. 485 g. cm3, respectively.
文摘A protocol for the synthesis of some 4-Aryl-1,3,4,6,7,8-hexahydroquinazolin-2,5(1H,6H)-diones (HHQs) was developed by means of a three-component condensation reaction of an aromatic aldehyde, 1,3-cylohexadione and urea in the presence of K3AlF6 (Al2O3/KF) as catalyst. This reaction is carried out under different conditions including 1) solvent free;2) reflux in acetonitrile;3) reflux in ethanol;4) reflux in chloroform;and 5) reflux in water. In all conditions, the desired products are obtained in high yields after relatively short reaction times. Nevertheless, the reactions proceed faster and in higher yields when they were carried out in acetonitrile. This adopted protocol for some Biginelli-type products has offered the advantages of reusability of the catalyst, high yields and ease of separation of pure products. Furthermore, the catalyst is easily prepared, stabilized and efficiently used under reaction conditions.
基金Projects(50572078, 20571059) supported by the National Natural Science Foundation of China
文摘A series of new microwave dielectric ceramics Ba3-nLa1+nTinNb3-nO12 (n=0,1,2) were prepared in the BaO-La2O3-TiO2-Nb2O5 system by high temperature solid-state reaction route. The phase and structure of the ceramics were characterized by X-ray diffraction, scanning electron microscope, and microwave dielectric properties measurements. These samples were identified as single phase and adopted A4B3O12-type cation-deficient hexagonal perovskite structure, which can be described as consisting of identical perovskite-like blocks, three corner-sharing BO6 octahedra thick, separated by layers of vacant octahedral. These ceramics have high dielectric constants in the range of 48-42, high quality factors (Q×f) up to 38 000 GHz, and low temperature coefficient of resonant frequencies (τf) in the range of (-40-+6)×10-6℃-1. With increasing content of La and Ti, the dielectric constants slightly decrease butτf gradually increases.
文摘Kinetics of phase transformation from pseudocubic to tetragonal phase in Bi3NbO7 solid solution is studied by using the ac impedance method under isothermal conditions. Conductivity of the investigated compound is used to characterize the kinetic process of the transition. The Avrami exponent and the activation energy of phase transition are around 1.5 and 3.5eV, respectively. These kinetic parameters reveal that the pseudocubic-tetragonal transition in Bi3NbO7 .belongs to a three-dimensional diffusion-controlled growth with zero nucleation rate.