SiC-MgAl_(2)O_(4) composites with SiAlON polytypoids(12H and 21R)as the bonding phases were prepared using SiC fine powder,MgAl_(2)O_(4)fine powder and Al powder as raw materials.The effects of the firing temperature ...SiC-MgAl_(2)O_(4) composites with SiAlON polytypoids(12H and 21R)as the bonding phases were prepared using SiC fine powder,MgAl_(2)O_(4)fine powder and Al powder as raw materials.The effects of the firing temperature and the mass ratio of SiC to MgAl_(2)O_(4) on the formation of SiAlON polytypoids as well as on the properties of samples were studied.The formation mechanism of SiAlON polytypoids was discussed.The results show that firing at 1650℃in the nitrogen atmosphere,SiC-MgAl_(2)O_(4) composites with SiAlON polytypoids can be obtained.With the gradual increase of the mass ratio of SiC to MgAl_(2)O_(4) in the raw materials,12H forms first,and then coexists with 21H,finally,all 12H converts into 21R in samples.Both phases are plate crystals with flat and smooth edges.Compared with 21R,12H is conducive to improving the density and the cold mechanical properties of materials.After firing at 1650℃in the nitrogen atmosphere,with the mass ratio of SiC to MgAl_(2)O_(4) of 6:4,the sample has the cold modulus of rupture of 27 MPa,showing the optimal performance.展开更多
Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part i...Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part icles were characterized by powder X ray diffraction(XRD),thermal analysis(TGA DSC), infrared spectroscopy(FT IR),transmission electron microscopy(SEM) and scanning electron microscopy(TEM). The size distribution in whisker like and nanocrystalline materials arein the range of 10～50μm and 10～20nm respectively. The whisker MOS is metastable phase in MgSO4 NaOH H2O system at 140℃,whereas nanometer MOS is stable phase.展开更多
文摘SiC-MgAl_(2)O_(4) composites with SiAlON polytypoids(12H and 21R)as the bonding phases were prepared using SiC fine powder,MgAl_(2)O_(4)fine powder and Al powder as raw materials.The effects of the firing temperature and the mass ratio of SiC to MgAl_(2)O_(4) on the formation of SiAlON polytypoids as well as on the properties of samples were studied.The formation mechanism of SiAlON polytypoids was discussed.The results show that firing at 1650℃in the nitrogen atmosphere,SiC-MgAl_(2)O_(4) composites with SiAlON polytypoids can be obtained.With the gradual increase of the mass ratio of SiC to MgAl_(2)O_(4) in the raw materials,12H forms first,and then coexists with 21H,finally,all 12H converts into 21R in samples.Both phases are plate crystals with flat and smooth edges.Compared with 21R,12H is conducive to improving the density and the cold mechanical properties of materials.After firing at 1650℃in the nitrogen atmosphere,with the mass ratio of SiC to MgAl_(2)O_(4) of 6:4,the sample has the cold modulus of rupture of 27 MPa,showing the optimal performance.
文摘Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part icles were characterized by powder X ray diffraction(XRD),thermal analysis(TGA DSC), infrared spectroscopy(FT IR),transmission electron microscopy(SEM) and scanning electron microscopy(TEM). The size distribution in whisker like and nanocrystalline materials arein the range of 10～50μm and 10～20nm respectively. The whisker MOS is metastable phase in MgSO4 NaOH H2O system at 140℃,whereas nanometer MOS is stable phase.
