The spectral parameters of Nd3+ ions in Nd3+:Klu(WO4)2 crystal were calculated based on Judd-Ofelt theory and obtained as follows: for the oscillator strengths ?λ: ?2 = 7.5029×10-20 cm2, ?4 = 7.1837×10-20...The spectral parameters of Nd3+ ions in Nd3+:Klu(WO4)2 crystal were calculated based on Judd-Ofelt theory and obtained as follows: for the oscillator strengths ?λ: ?2 = 7.5029×10-20 cm2, ?4 = 7.1837×10-20 cm2 and ?6 = 3.1189×10-20 cm2; the radiative lifetime is 123 μs; the quantum efficiency is equal to 64.55%; and β1 = 0.5498, β2 = 0.3943, β3 = 0.0551 and β4 = 0.0027 for the fluorescence branch ratios.展开更多
The laser host crystals of KLu(WO4)2(KLuW) with large sizes up to 43 × 35 × 16 mm3 have been grown along, [110], b, and c crystallographic directions, respectively, by the top-seeded solution growth (TSSG) s...The laser host crystals of KLu(WO4)2(KLuW) with large sizes up to 43 × 35 × 16 mm3 have been grown along, [110], b, and c crystallographic directions, respectively, by the top-seeded solution growth (TSSG) slow-cooling method. The macro defects are observed using optical microscopy. The main defects found were cracks, inclusions, growth striations, sector boundaries and twin boundaries. The formation mechanism and approaches to reduce or eliminate the defects have been analyzed.展开更多
Optical absorption and emission intensities of Nd3+ ion in KLu(WO4)2 crystal were investigated. Based on the Judd-Offelt theory, we calculated the following spectral parameters: phenomenological intensity parameters ...Optical absorption and emission intensities of Nd3+ ion in KLu(WO4)2 crystal were investigated. Based on the Judd-Offelt theory, we calculated the following spectral parameters: phenomenological intensity parameters Ω2=5.567×10–20, Ω4=3.597×10–20, and Ω6= 3.800×10–20 cm2. The radiative lifetime of levels 4F3/2 was 182.58 μs. The fluorescence branching ratio for the transition 4F3/2→4I11/2 was 46.98%. In addition, the radiative transition probabilities AJ,J’, oscillator strengths PJ,J’ and the values of inte...展开更多
基金This work was supported by the National Natural Science Foundation of China (50272066) and Key Project of Science and Technology of Fujian Province (2001F004)
文摘The spectral parameters of Nd3+ ions in Nd3+:Klu(WO4)2 crystal were calculated based on Judd-Ofelt theory and obtained as follows: for the oscillator strengths ?λ: ?2 = 7.5029×10-20 cm2, ?4 = 7.1837×10-20 cm2 and ?6 = 3.1189×10-20 cm2; the radiative lifetime is 123 μs; the quantum efficiency is equal to 64.55%; and β1 = 0.5498, β2 = 0.3943, β3 = 0.0551 and β4 = 0.0027 for the fluorescence branch ratios.
文摘The laser host crystals of KLu(WO4)2(KLuW) with large sizes up to 43 × 35 × 16 mm3 have been grown along, [110], b, and c crystallographic directions, respectively, by the top-seeded solution growth (TSSG) slow-cooling method. The macro defects are observed using optical microscopy. The main defects found were cracks, inclusions, growth striations, sector boundaries and twin boundaries. The formation mechanism and approaches to reduce or eliminate the defects have been analyzed.
基金Project supported by Program for New Century Excellent Talents in University (NCET-08-0722)
文摘Optical absorption and emission intensities of Nd3+ ion in KLu(WO4)2 crystal were investigated. Based on the Judd-Offelt theory, we calculated the following spectral parameters: phenomenological intensity parameters Ω2=5.567×10–20, Ω4=3.597×10–20, and Ω6= 3.800×10–20 cm2. The radiative lifetime of levels 4F3/2 was 182.58 μs. The fluorescence branching ratio for the transition 4F3/2→4I11/2 was 46.98%. In addition, the radiative transition probabilities AJ,J’, oscillator strengths PJ,J’ and the values of inte...