The Sm^（3＋）-doped SrO-Al2O3-SiO2（SAS） glass-ceramics with excellent luminescence properties were prepared by batch melting and heat treatment. The crystallization behavior and luminescent properties of the glass-...The Sm^（3＋）-doped SrO-Al2O3-SiO2（SAS） glass-ceramics with excellent luminescence properties were prepared by batch melting and heat treatment. The crystallization behavior and luminescent properties of the glass-ceramics were investigated by DTA, XRD, SEM and luminescence spectroscopy. The results indicate that the crystal phase precipitated in this system is monocelsian（SrAl2Si2O） and with the increase of nucleation/crystallization temperature, the crystallite increases from 66 % to 79 %. The Sm（3＋）-doped SAS glass-ceramics emit green, orange and red lights centered at 565, 605, 650 and 715 nm under the excitation of 475 nm blue light which can be assigned to the 4 G5/2→6 Hj/2（j=5, 7, 9, 11） transitions ofSm^（3＋）, respectively. Besides, by increasing the crystallization temperature or the concentration ofSm^（3＋）, the emission lights of the samples located at 565, 605 and 650 nm are intensified significantly. The present results demonstrate that theSm^（3＋）-doped SAS glassceramics are promising luminescence materials for white LED devices by fine controlling and combining of these three green, orange and red lights in appropriate proportion.展开更多
Single crystal of Li2Zn2（MoO4）3 has been grown from a flux of Li2MoO4 by the top-seeded solution-growth method, and its stnicture was refined by the Rietveld method. It belongs to the orthorhombic system, space grou...Single crystal of Li2Zn2（MoO4）3 has been grown from a flux of Li2MoO4 by the top-seeded solution-growth method, and its stnicture was refined by the Rietveld method. It belongs to the orthorhombic system, space group Pnma with a = 5.1114, b = 10.4906 and c = 17.6172A. Good agreement between the experimental and calculated profile （Rp = 6.69%, Rwp = 9.73% and Rexp = 6.58%） was reached.展开更多
Sm2O3 containing zinc-borosilicate glass and glass ceramics were prepared by melt quenching method, and the effect of Sm2O3 and micro-crystallization on the chemical stability of borosilicate glass was explored. DTA a...Sm2O3 containing zinc-borosilicate glass and glass ceramics were prepared by melt quenching method, and the effect of Sm2O3 and micro-crystallization on the chemical stability of borosilicate glass was explored. DTA analysis showed that the endothermic peak and exothermic peak of basic glass changed from 635 ℃ and 834 ℃ to 630 ℃ and 828 ℃ respectively as a result of the doping of Sm2O3. XRD analysis showed the promoting effect of Sm2O3 on crystallization ability of this glass. The cumulative mass loss of base glass, Sm2O3 containing glass, glass ceramic and Sm2O3 containing glass ceramic was 0.289, 0.253, 0.329, 0.269 mg/mm2 respectively after 26 days corrosion in alkali solution, and 1.293, 1.290, 0.999, 1.040 mg/mm2 respectively in acidic erosion medium. Micro-crystallization decreased and improved the alkali and acid resistance of borosilicate glass respectively, the addition of Sm2O3 increased the alkali resistance of base glass and glass ceramics, and the slight effect of Sm2O3 on the acid resistance of borosilicate glass was also observed.展开更多
X-ray powder diffraction and Fourier transform infrared spectroscopy were applied for characterization of Li2O-Al2O3-SiO2 glass-ceramic powders doped with Eu2O3,Gd2O3 and Er2O3,respectively,in the conditions of differ...X-ray powder diffraction and Fourier transform infrared spectroscopy were applied for characterization of Li2O-Al2O3-SiO2 glass-ceramic powders doped with Eu2O3,Gd2O3 and Er2O3,respectively,in the conditions of different heat-treatment temperatures and with various amounts.The powders were derived from the polyacrylamide gel method.The results show that,the wet gels prepared by polyacrylamide perform a unique crystallization behavior in the process of drying,comparing with some customary preparation such as melt processing.The main crystal phase and crystallization sequence of Li2O-Al2O3-SiO2 micro-powders have no distinct with addition of Eu2O3,Gd2O3 or Er2O3,while the crystallization temperature of the β-spodumene decreased and the amount of the β-spodumene increased.展开更多
Crystal structure of γ-Li_xFe_2O_3,inserted Li electrochemically,was studied by Moss- bauer spectroscopy together with X-ray diffraction,XPS and electrochemical method,On the insertion of Li at low current density,th...Crystal structure of γ-Li_xFe_2O_3,inserted Li electrochemically,was studied by Moss- bauer spectroscopy together with X-ray diffraction,XPS and electrochemical method,On the insertion of Li at low current density,the crystal structure is keeping original spinel; while at higher current density or by thermal activation,owing to violent movement of Li^+ ions,part of crystal structure transforms into rock type similar to face-centered cubic structure of ferrous oxide.The transition channels during insertion of Li^+ ions and limitation of Li^+ ions inserted were discussed.展开更多
A single crystal of Li3Ba2Ho3（WO4）8 was obtained from a flux of Li2WO4 under an air atmosphere. The structure of the pure crystal was determined by single-crystal X-ray diffraction method. It crystallizes in the mon...A single crystal of Li3Ba2Ho3（WO4）8 was obtained from a flux of Li2WO4 under an air atmosphere. The structure of the pure crystal was determined by single-crystal X-ray diffraction method. It crystallizes in the monoclinic system, space group C2/c with a = 5.240（4）, b = 12.790（10）, c = 19.247（15）, β = 91.921（15）°, V = 1289.1（18）3, Z = 2, Mr = 2773.09, Dc = 7.144 g/cm3, μ = 47.732 mm-1, Rint = 0.0693, F（000） = 2340, the final R = 0.0472 and wR = 0.1221 for 1535 observed reflections （I 2σ（I））. The Li3Ba2Ho3（WO4）8 has a high structure disorder with one 8f site shared by Li（1） and Ho ions with occupancy of 0.25 and 0.75, respectively. The fundamental structure is constituted by distorted square antiprisms Ho/Li（1）O8 with C1 symmetry, distorted Li（2）O6 octahedra and BaO10 polyhedra. The optical properties were investigated by IR and absorption spectroscopy, and the emission cross sections and gain cross sections of 5I7 → 5I8 of Ho3＋ were calculated.展开更多
基金Funded by the National Natural Science Foundation of China(No.5137217)Hubei Province Foreign Science and Technology Project(No.2016AHB027)Science and Technology Planning Project of Hubei Province(No.2014BAA136)
文摘The Sm^（3＋）-doped SrO-Al2O3-SiO2（SAS） glass-ceramics with excellent luminescence properties were prepared by batch melting and heat treatment. The crystallization behavior and luminescent properties of the glass-ceramics were investigated by DTA, XRD, SEM and luminescence spectroscopy. The results indicate that the crystal phase precipitated in this system is monocelsian（SrAl2Si2O） and with the increase of nucleation/crystallization temperature, the crystallite increases from 66 % to 79 %. The Sm（3＋）-doped SAS glass-ceramics emit green, orange and red lights centered at 565, 605, 650 and 715 nm under the excitation of 475 nm blue light which can be assigned to the 4 G5/2→6 Hj/2（j=5, 7, 9, 11） transitions ofSm^（3＋）, respectively. Besides, by increasing the crystallization temperature or the concentration ofSm^（3＋）, the emission lights of the samples located at 565, 605 and 650 nm are intensified significantly. The present results demonstrate that theSm^（3＋）-doped SAS glassceramics are promising luminescence materials for white LED devices by fine controlling and combining of these three green, orange and red lights in appropriate proportion.
基金the National Natural Science Foundation of China (No. 50672123)
文摘Single crystal of Li2Zn2（MoO4）3 has been grown from a flux of Li2MoO4 by the top-seeded solution-growth method, and its stnicture was refined by the Rietveld method. It belongs to the orthorhombic system, space group Pnma with a = 5.1114, b = 10.4906 and c = 17.6172A. Good agreement between the experimental and calculated profile （Rp = 6.69%, Rwp = 9.73% and Rexp = 6.58%） was reached.
基金Funded by the National Natural Science Foundation of China(51025416,51202104 and 51362019)the Natural Science Foundation of the Inner Mongolia Autonomous Region(2012MS0807)+1 种基金the Program for Young Talents of Science and Technology in Universities of Inner Mongolia Autonomous Region,the Talent Incubation Funding of School of Materials and Metallurgy(2014CY012)the Talent Incubation Funding of School of Materials and Metallurgy(2014CY012)
文摘Sm2O3 containing zinc-borosilicate glass and glass ceramics were prepared by melt quenching method, and the effect of Sm2O3 and micro-crystallization on the chemical stability of borosilicate glass was explored. DTA analysis showed that the endothermic peak and exothermic peak of basic glass changed from 635 ℃ and 834 ℃ to 630 ℃ and 828 ℃ respectively as a result of the doping of Sm2O3. XRD analysis showed the promoting effect of Sm2O3 on crystallization ability of this glass. The cumulative mass loss of base glass, Sm2O3 containing glass, glass ceramic and Sm2O3 containing glass ceramic was 0.289, 0.253, 0.329, 0.269 mg/mm2 respectively after 26 days corrosion in alkali solution, and 1.293, 1.290, 0.999, 1.040 mg/mm2 respectively in acidic erosion medium. Micro-crystallization decreased and improved the alkali and acid resistance of borosilicate glass respectively, the addition of Sm2O3 increased the alkali resistance of base glass and glass ceramics, and the slight effect of Sm2O3 on the acid resistance of borosilicate glass was also observed.
文摘X-ray powder diffraction and Fourier transform infrared spectroscopy were applied for characterization of Li2O-Al2O3-SiO2 glass-ceramic powders doped with Eu2O3,Gd2O3 and Er2O3,respectively,in the conditions of different heat-treatment temperatures and with various amounts.The powders were derived from the polyacrylamide gel method.The results show that,the wet gels prepared by polyacrylamide perform a unique crystallization behavior in the process of drying,comparing with some customary preparation such as melt processing.The main crystal phase and crystallization sequence of Li2O-Al2O3-SiO2 micro-powders have no distinct with addition of Eu2O3,Gd2O3 or Er2O3,while the crystallization temperature of the β-spodumene decreased and the amount of the β-spodumene increased.
文摘Crystal structure of γ-Li_xFe_2O_3,inserted Li electrochemically,was studied by Moss- bauer spectroscopy together with X-ray diffraction,XPS and electrochemical method,On the insertion of Li at low current density,the crystal structure is keeping original spinel; while at higher current density or by thermal activation,owing to violent movement of Li^+ ions,part of crystal structure transforms into rock type similar to face-centered cubic structure of ferrous oxide.The transition channels during insertion of Li^+ ions and limitation of Li^+ ions inserted were discussed.
基金supported by the National Natural Science Foundation of China(20971123,51002153,21007070,51102232,61106004 and 21103191)
文摘A single crystal of Li3Ba2Ho3（WO4）8 was obtained from a flux of Li2WO4 under an air atmosphere. The structure of the pure crystal was determined by single-crystal X-ray diffraction method. It crystallizes in the monoclinic system, space group C2/c with a = 5.240（4）, b = 12.790（10）, c = 19.247（15）, β = 91.921（15）°, V = 1289.1（18）3, Z = 2, Mr = 2773.09, Dc = 7.144 g/cm3, μ = 47.732 mm-1, Rint = 0.0693, F（000） = 2340, the final R = 0.0472 and wR = 0.1221 for 1535 observed reflections （I 2σ（I））. The Li3Ba2Ho3（WO4）8 has a high structure disorder with one 8f site shared by Li（1） and Ho ions with occupancy of 0.25 and 0.75, respectively. The fundamental structure is constituted by distorted square antiprisms Ho/Li（1）O8 with C1 symmetry, distorted Li（2）O6 octahedra and BaO10 polyhedra. The optical properties were investigated by IR and absorption spectroscopy, and the emission cross sections and gain cross sections of 5I7 → 5I8 of Ho3＋ were calculated.