Kiln phosphoric acid(KPA)technology could produce P2O5 with high purity and has been applied in thermal phosphoric acid industry;however the formation of fouling in the high-temperature rotary kiln restricts the stabl...Kiln phosphoric acid(KPA)technology could produce P2O5 with high purity and has been applied in thermal phosphoric acid industry;however the formation of fouling in the high-temperature rotary kiln restricts the stable and long-term operation.In this paper,the reaction of phosphate ores with gaseous P2O5 was investigated in a high-temperature reactor,and the Ca O-SiO2-P2O5 ternary phase diagram was analyzed to understand the fouling formation mechanism.The results showed that the low-melting-point products,such as Ca(PO3)2and Ca2P2O7,are responsible for the fouling in the KPA process.In addition,a small amount of impurities,e.g.,aluminum and iron,could facilitate the generation of the low-melting-point products and cause serious fouling.Based on the high-temperature SiO2-P2O5 and CaO-SiO2-P2O5 phase diagram analysis,the control of Si/Ca molar ratio(e.g.,Si/Ca=2.0)was found to avoid fouling formation in the kiln.These results could provide the operation parameters of reaction temperature and feeds composition to suppress the fouling in the kiln reactor for the phosphoric acid production in industry.展开更多
Through the comparison of calcination conditions between cement preclinkering technology and cement precalcining technology,we studied the characteristics of temperature field distribution of cement preclinkering tech...Through the comparison of calcination conditions between cement preclinkering technology and cement precalcining technology,we studied the characteristics of temperature field distribution of cement preclinkering technology systems including cyclone preheater,preclinkering furnace,and rotary kiln.We used numericalsimulation method to obtain data of temperature field distribution.Some results are found by system study.The ratio of tailcoalof cement preclinkering technology is about 70%,and raw mealtemperature can reach 1070 ℃.Shorter L/D kiln type of preclinkering technology can obtain more stable calcining zone temperature.The highest solid temperature of cement preclinkering technology is higher than 80 ℃,and high temperature region（〉1450 ℃）length is 2 times,which is beneficialfor calcining clinker and higher clinker quality.So cement preclinkering technology can obtain more performance temperature filed,which improves both the solid-phase reaction and liquid-phase reaction.展开更多
基金support from the National Key R&D Program of China(2018YFC1900201)the Provincial Key R&D Program of Shanxi(201603D31212003)。
文摘Kiln phosphoric acid(KPA)technology could produce P2O5 with high purity and has been applied in thermal phosphoric acid industry;however the formation of fouling in the high-temperature rotary kiln restricts the stable and long-term operation.In this paper,the reaction of phosphate ores with gaseous P2O5 was investigated in a high-temperature reactor,and the Ca O-SiO2-P2O5 ternary phase diagram was analyzed to understand the fouling formation mechanism.The results showed that the low-melting-point products,such as Ca(PO3)2and Ca2P2O7,are responsible for the fouling in the KPA process.In addition,a small amount of impurities,e.g.,aluminum and iron,could facilitate the generation of the low-melting-point products and cause serious fouling.Based on the high-temperature SiO2-P2O5 and CaO-SiO2-P2O5 phase diagram analysis,the control of Si/Ca molar ratio(e.g.,Si/Ca=2.0)was found to avoid fouling formation in the kiln.These results could provide the operation parameters of reaction temperature and feeds composition to suppress the fouling in the kiln reactor for the phosphoric acid production in industry.
基金Funded by the Major State Basic Research Perelopment Program of China(973 Program)(No.2009CB623102)the Key Fund Project of Sichuan Provincial Department of Education(No.14ZA0086)the Key Fund Project of Professional Scientific Research Innovation Team of Southwest University of Science and Technology(No.14tdfk01)
文摘Through the comparison of calcination conditions between cement preclinkering technology and cement precalcining technology,we studied the characteristics of temperature field distribution of cement preclinkering technology systems including cyclone preheater,preclinkering furnace,and rotary kiln.We used numericalsimulation method to obtain data of temperature field distribution.Some results are found by system study.The ratio of tailcoalof cement preclinkering technology is about 70%,and raw mealtemperature can reach 1070 ℃.Shorter L/D kiln type of preclinkering technology can obtain more stable calcining zone temperature.The highest solid temperature of cement preclinkering technology is higher than 80 ℃,and high temperature region（〉1450 ℃）length is 2 times,which is beneficialfor calcining clinker and higher clinker quality.So cement preclinkering technology can obtain more performance temperature filed,which improves both the solid-phase reaction and liquid-phase reaction.