Controlled oxidation experiments were performed on Kovar alloy by changing oxidation atmosphere, temperature, and exposure time to produce films with different oxide type and thickness. The results indicated that sing...Controlled oxidation experiments were performed on Kovar alloy by changing oxidation atmosphere, temperature, and exposure time to produce films with different oxide type and thickness. The results indicated that single Fe3O4 and single FeO were respectively obtained when Kovar alloy was oxidized in N2-2.31%H2O-0.95%H2 at 500℃ and in N2-2.31%H2O-0.5%H2 at 1000℃, and all kinetic curves followed linear relation; mixed oxides of FeO and Fe3O4 formed when Kovar was oxidized in N2-2.31%H2O at 1000℃and parabolic kinetics were obeyed. Analysis of metallographic cross section of oxides indicated that oxygen diffusion inward through the oxide scale is responsible for intergranular oxide, which had formed beneath the oxide scales when the oxide products were mixed oxides of FeO and Fe3O4, and which did not occur when the oxide was single FeO or Fe3O4. The oxidation model was also established.展开更多
The effect of Kovar alloy oxidized in simulated field atmosphere on its sealing with glass was studied in this article. After Kovar plates and pins were preoxidized in N2 with 0℃, 10℃ and 20℃ dew points at 1000℃ f...The effect of Kovar alloy oxidized in simulated field atmosphere on its sealing with glass was studied in this article. After Kovar plates and pins were preoxidized in N2 with 0℃, 10℃ and 20℃ dew points at 1000℃ for different times, Fe304 and Fe203 existed in the oxidation products on Kovar surface, and the quantity of Fe203 increased with increasing dew point and oxidation time. Then they were sealed with borosilicate glass insulator at 1030℃ for 20 rain. The results indicated that the type and quantity of oxidation products would directly influence the quality of glass-to-metal seals. With the increase of oxidation products, gas bubbles in the glass insulator were more serious, the climbing height of glass along the pins was higher, and corrosion of Kovar pins caused from the molten glass was transformed from uniform to the localized.展开更多
The oxidation of Kovar alloy was investigated, the wetting and spreading behavior of hard and soft glasses on Kovar alloy were studed by using the sessile drop method, and the quality and the seal strength of glass-Ko...The oxidation of Kovar alloy was investigated, the wetting and spreading behavior of hard and soft glasses on Kovar alloy were studed by using the sessile drop method, and the quality and the seal strength of glass-Kovar seals were tested. The experimental results indicated that the preoxidation of Kovar alloy for approximately 10 min at 700℃ in air resulted in excellent adherence in glass-Kovar seals. The wetting and spreading behavior of glass on preoxidized Kovar alloy were superior to that on nonoxidized Kovar alloy. The wetting ability of ASF110 glass, at 950℃ and 980℃ in Ar and N2 atmospheres, was significantly superior to that of ASF200R and ASF700 glasses. The seal quality of the glass-preoxidized Kovar seal was superior to that of the glass-nonoxidized Kovar seal. The shear strength of the ASFll0 glass-preoxidized Kovar seal, which was prepared at 980℃ for 20 min in an Ar atmosphere, was approximately 3.9 MPa.展开更多
基金supported by the National Natural Science Foundation of China(No. 50671014).
文摘Controlled oxidation experiments were performed on Kovar alloy by changing oxidation atmosphere, temperature, and exposure time to produce films with different oxide type and thickness. The results indicated that single Fe3O4 and single FeO were respectively obtained when Kovar alloy was oxidized in N2-2.31%H2O-0.95%H2 at 500℃ and in N2-2.31%H2O-0.5%H2 at 1000℃, and all kinetic curves followed linear relation; mixed oxides of FeO and Fe3O4 formed when Kovar was oxidized in N2-2.31%H2O at 1000℃and parabolic kinetics were obeyed. Analysis of metallographic cross section of oxides indicated that oxygen diffusion inward through the oxide scale is responsible for intergranular oxide, which had formed beneath the oxide scales when the oxide products were mixed oxides of FeO and Fe3O4, and which did not occur when the oxide was single FeO or Fe3O4. The oxidation model was also established.
文摘The effect of Kovar alloy oxidized in simulated field atmosphere on its sealing with glass was studied in this article. After Kovar plates and pins were preoxidized in N2 with 0℃, 10℃ and 20℃ dew points at 1000℃ for different times, Fe304 and Fe203 existed in the oxidation products on Kovar surface, and the quantity of Fe203 increased with increasing dew point and oxidation time. Then they were sealed with borosilicate glass insulator at 1030℃ for 20 rain. The results indicated that the type and quantity of oxidation products would directly influence the quality of glass-to-metal seals. With the increase of oxidation products, gas bubbles in the glass insulator were more serious, the climbing height of glass along the pins was higher, and corrosion of Kovar pins caused from the molten glass was transformed from uniform to the localized.
文摘The oxidation of Kovar alloy was investigated, the wetting and spreading behavior of hard and soft glasses on Kovar alloy were studed by using the sessile drop method, and the quality and the seal strength of glass-Kovar seals were tested. The experimental results indicated that the preoxidation of Kovar alloy for approximately 10 min at 700℃ in air resulted in excellent adherence in glass-Kovar seals. The wetting and spreading behavior of glass on preoxidized Kovar alloy were superior to that on nonoxidized Kovar alloy. The wetting ability of ASF110 glass, at 950℃ and 980℃ in Ar and N2 atmospheres, was significantly superior to that of ASF200R and ASF700 glasses. The seal quality of the glass-preoxidized Kovar seal was superior to that of the glass-nonoxidized Kovar seal. The shear strength of the ASFll0 glass-preoxidized Kovar seal, which was prepared at 980℃ for 20 min in an Ar atmosphere, was approximately 3.9 MPa.