Laser crystal Yb：KYW was grown by the Kyropoulos method. A grown crystal was identified as β-Yb：KYW by XRD. By TG-DTA the melting point and transition point of the crystal are 1045 and 1010 ℃, respectively. Infrar...Laser crystal Yb：KYW was grown by the Kyropoulos method. A grown crystal was identified as β-Yb：KYW by XRD. By TG-DTA the melting point and transition point of the crystal are 1045 and 1010 ℃, respectively. Infrared spectrum and Raman speetrum were measured, and the vibrational frequencies of infrared and Raman active modes for Yb：KYW crystal were assigned. Absorption spectrum of Yb：KYW shows that there are two intensive absorption peaks at 940 and 980 nm, respectively, and the absorption cross section is 1.34 × 10^- 19 cm^2 at chief peak of 980 nm. There exist three intensive emission peaks in Yb：KYW at 990, 1010 and 1030 nm, respectively, and the emission line width of the chief peak 1030 nm runs up to 16 nm. It was calculated that the peak emission cross section is 3.1 × 10^-20 cm^2 at 1030 nm.展开更多
The 10 at.% Er3+-doped KYb(WO4)2(KEr0.1Yb0.9(WO4)2) laser crystal with dimensions up to 25 mm×15 mm×10 mm was grown by the Kyropoulos method.The crystal structure was identified as β-KEr0.1Yb0.9(WO4)2 by XR...The 10 at.% Er3+-doped KYb(WO4)2(KEr0.1Yb0.9(WO4)2) laser crystal with dimensions up to 25 mm×15 mm×10 mm was grown by the Kyropoulos method.The crystal structure was identified as β-KEr0.1Yb0.9(WO4)2 by XRD analysis.Through TG-DTA curves,the melting point and transition point of the crystal were determined to be 1058 and 1031 °C,respectively.Infrared spectrum and Raman spectrum were measured,and the vibration frequencies of infrared and Raman active modes for the crystal were assigned.The absorption cross ...展开更多
The Nd^3＋ 3.2% （atom fraction）：KGd（WO4）2 crystal was grown by Kyropoulos method. The absorption spectrum and fluorescence spectrum of Nd^3 ＋ ： KGW crystal were measured. The absorption cross sections at 808 nm...The Nd^3＋ 3.2% （atom fraction）：KGd（WO4）2 crystal was grown by Kyropoulos method. The absorption spectrum and fluorescence spectrum of Nd^3 ＋ ： KGW crystal were measured. The absorption cross sections at 808 nm（0. 6799 × 10^-20 cm^2） were calculated, and the output wavelength of fluorescence is 1064 and 1351 nm. The diode-pumped laser was operated both in the free-running and passively Q-switched operating modes. The maximum laser output（1064 nm） is 326 mW with 62.7 % slope efficiency when input energy is 900 mW. The beam quality factor M^2 ≈ 1.1. The green light of 532 nm is obtained in frequency doubling operation. The laser is passively Q-switched by using Cr^4＋ ：LuAG as saturable absorber. The pulse width is 170 ns at repetitive frequency of 15 kHZ.展开更多
文摘Laser crystal Yb：KYW was grown by the Kyropoulos method. A grown crystal was identified as β-Yb：KYW by XRD. By TG-DTA the melting point and transition point of the crystal are 1045 and 1010 ℃, respectively. Infrared spectrum and Raman speetrum were measured, and the vibrational frequencies of infrared and Raman active modes for Yb：KYW crystal were assigned. Absorption spectrum of Yb：KYW shows that there are two intensive absorption peaks at 940 and 980 nm, respectively, and the absorption cross section is 1.34 × 10^- 19 cm^2 at chief peak of 980 nm. There exist three intensive emission peaks in Yb：KYW at 990, 1010 and 1030 nm, respectively, and the emission line width of the chief peak 1030 nm runs up to 16 nm. It was calculated that the peak emission cross section is 3.1 × 10^-20 cm^2 at 1030 nm.
基金supported by Jilin Provincial Education Department (2009JYT15)Jilin Provincial Science and Technology Department (20090709)Changchun Science and Technology Bureau (2009110)
文摘The 10 at.% Er3+-doped KYb(WO4)2(KEr0.1Yb0.9(WO4)2) laser crystal with dimensions up to 25 mm×15 mm×10 mm was grown by the Kyropoulos method.The crystal structure was identified as β-KEr0.1Yb0.9(WO4)2 by XRD analysis.Through TG-DTA curves,the melting point and transition point of the crystal were determined to be 1058 and 1031 °C,respectively.Infrared spectrum and Raman spectrum were measured,and the vibration frequencies of infrared and Raman active modes for the crystal were assigned.The absorption cross ...
文摘The Nd^3＋ 3.2% （atom fraction）：KGd（WO4）2 crystal was grown by Kyropoulos method. The absorption spectrum and fluorescence spectrum of Nd^3 ＋ ： KGW crystal were measured. The absorption cross sections at 808 nm（0. 6799 × 10^-20 cm^2） were calculated, and the output wavelength of fluorescence is 1064 and 1351 nm. The diode-pumped laser was operated both in the free-running and passively Q-switched operating modes. The maximum laser output（1064 nm） is 326 mW with 62.7 % slope efficiency when input energy is 900 mW. The beam quality factor M^2 ≈ 1.1. The green light of 532 nm is obtained in frequency doubling operation. The laser is passively Q-switched by using Cr^4＋ ：LuAG as saturable absorber. The pulse width is 170 ns at repetitive frequency of 15 kHZ.