The early precipitation process of Ni（75）Al（14）Mo（11） alloy was simulated by microscopic phase-field model at different temperatures.The microstructure of the alloy,the precipitation time of Llo structure and oc...The early precipitation process of Ni（75）Al（14）Mo（11） alloy was simulated by microscopic phase-field model at different temperatures.The microstructure of the alloy,the precipitation time of Llo structure and occupation probability of the three kinds of atoms were investigated.It is indicated that the non-stoichiometric Ll0（Ⅰ/Ⅱ） phases are found in the precipitation process.With the temperature increasing,the appearance time of Ll0 is brought forward.The Ll0（Ⅱ） structure always precipitates earlier than the Ll0（Ⅰ） structure.Compared with lower temperature,higher temperature brings the formation time of Ll0 phase forward and makes Ll0 phase have a higher order degree.But lower temperature shortens the process time of the Ll0 phase to the Ll2 phase.Al and Mo atoms tend to occupy γ site,Ni atom tends to occupy a and β sites.At the same temperature,Al atom has stronger occupation ability than Mo atom in the same site.Ni,Al and Mo collectively form the composited Ll2 structure.展开更多
The pre-precipitation processes of γ＇ phase in Ni-Al-Ti alloy with different chemical compositions are investigated by microscopic phase-field dynamics model. The simulation results show that the early precip...The pre-precipitation processes of γ＇ phase in Ni-Al-Ti alloy with different chemical compositions are investigated by microscopic phase-field dynamics model. The simulation results show that the early precipitated phase with L10 structure is formed before the formation of γ＇ phase. With the increase of Al content, the composition of precipitated phase is transformed from the co-existence of γ＇ phase and material phase into single y phase. Furthermore, excessive Al content can stimulate the production of γ＇ phase, and the conversion time from L10 phase to L12 phase will lag behind other samples with lower Al con-tent. By analyzing the occupation probability of Ti, it can be found that the solid solution strengthening effect of Ti is reduced with the increase of Al component.展开更多
基金Project(51275486)supported by the National Natural Science Foundation of China
文摘The early precipitation process of Ni（75）Al（14）Mo（11） alloy was simulated by microscopic phase-field model at different temperatures.The microstructure of the alloy,the precipitation time of Llo structure and occupation probability of the three kinds of atoms were investigated.It is indicated that the non-stoichiometric Ll0（Ⅰ/Ⅱ） phases are found in the precipitation process.With the temperature increasing,the appearance time of Ll0 is brought forward.The Ll0（Ⅱ） structure always precipitates earlier than the Ll0（Ⅰ） structure.Compared with lower temperature,higher temperature brings the formation time of Ll0 phase forward and makes Ll0 phase have a higher order degree.But lower temperature shortens the process time of the Ll0 phase to the Ll2 phase.Al and Mo atoms tend to occupy γ site,Ni atom tends to occupy a and β sites.At the same temperature,Al atom has stronger occupation ability than Mo atom in the same site.Ni,Al and Mo collectively form the composited Ll2 structure.
基金National Natural Science Foundation of China(Nos.U1610123,51674226,51574207,51574206,51274175)International Cooperation Project of the Ministry of Science and Technology of China(No.2014DFA50320)Science and Technology Major Project of Shanxi Province(No.MC2016-06)
文摘The pre-precipitation processes of γ＇ phase in Ni-Al-Ti alloy with different chemical compositions are investigated by microscopic phase-field dynamics model. The simulation results show that the early precipitated phase with L10 structure is formed before the formation of γ＇ phase. With the increase of Al content, the composition of precipitated phase is transformed from the co-existence of γ＇ phase and material phase into single y phase. Furthermore, excessive Al content can stimulate the production of γ＇ phase, and the conversion time from L10 phase to L12 phase will lag behind other samples with lower Al con-tent. By analyzing the occupation probability of Ti, it can be found that the solid solution strengthening effect of Ti is reduced with the increase of Al component.