In this study,two sandblasting textures,namely,quartz and high-chromium(Cr)stainless steel sands,were used for sandblasting of the internal surface L80-13Cr tubing and casing.The contrastive analysis on the properties...In this study,two sandblasting textures,namely,quartz and high-chromium(Cr)stainless steel sands,were used for sandblasting of the internal surface L80-13Cr tubing and casing.The contrastive analysis on the properties of the pipes before and after abrasive blasting was conducted,including the metallographic phase detection of the internal surface,simulating accelerated corrosion tests,and residual stress tests for the pipe after abrasive blasting.Based on the analysis results,it is explained why the API standard requires that no scale appears on the internal surface of L80-13Cr and iron contamination when internal sandblasting media are applied.The results show that abrasive blasting can effectively remove scales on the internal surface of L80-13Cr tubing and casing and improve corrosion resistance.The abrasive blasting process does not produce obvious residual stress on the internal surface of the tubing and casing.Also,the de-rusting effect of stainless sand is better than that of quartz sand,and the former does not produce iron contamination.展开更多
文摘In this study,two sandblasting textures,namely,quartz and high-chromium(Cr)stainless steel sands,were used for sandblasting of the internal surface L80-13Cr tubing and casing.The contrastive analysis on the properties of the pipes before and after abrasive blasting was conducted,including the metallographic phase detection of the internal surface,simulating accelerated corrosion tests,and residual stress tests for the pipe after abrasive blasting.Based on the analysis results,it is explained why the API standard requires that no scale appears on the internal surface of L80-13Cr and iron contamination when internal sandblasting media are applied.The results show that abrasive blasting can effectively remove scales on the internal surface of L80-13Cr tubing and casing and improve corrosion resistance.The abrasive blasting process does not produce obvious residual stress on the internal surface of the tubing and casing.Also,the de-rusting effect of stainless sand is better than that of quartz sand,and the former does not produce iron contamination.