The Nd^3＋：LiGd（WO4） 2 crystal with dimensions of 25mm×28mm×16mm was grown by the top-seeded solution growth method from the 60 mol% Li2W2O7 flux. LiGd（WO4） 2 crystallizes in the tetragonal system with ...The Nd^3＋：LiGd（WO4） 2 crystal with dimensions of 25mm×28mm×16mm was grown by the top-seeded solution growth method from the 60 mol% Li2W2O7 flux. LiGd（WO4） 2 crystallizes in the tetragonal system with space group I41/a（C4h^6） and cell parameters： a = 5.1986 and c = 11.2652A. The hardness is about 5.0 Mohs＇ scale. The specific heat is 0.40 J·g^-1·K^-1 at 50 oC. The thermal expansion coefficients for a-and c-axes are 1.314×10^-5 and 2.052×10^-5 K^-1,respectively. The room-temperature polarized absorption and emission spectra and the fluorescence decay curve was measured. The parameters of oscillator strengths,the spontaneous transition probabilities,the fluorescence branching ratios,the radiative lifetimes,and the emission cross sections have been investigated based on Judd-Ofelt theory and Füchtbauer-Ladenburg method. The absorption cross-section is 5.19×10^-20 cm^2 at 805 nm for π-polarization and its line width is 15 nm; the emission cross section is 1.726×10^-19 cm^2 at 1060.5 nm for π-polarization. The fluorescence and radiative lifetimes are 86 and 158 μs,respectively. The fluorescence quantum efficiency is 54.43%.展开更多
采用熔盐顶部籽晶法从K 2 Mo 3 O 10-B 2 O 3助熔剂中生长出尺寸为20 mm的优质GdAl 3(BO 3)4(简称GAB)和Nd^3+激活的自变频激光晶体。确定了GAB晶体的透光波长范围、折射率和倍频系数随波长的变化,结果表明其在整个透光范围内均可实现...采用熔盐顶部籽晶法从K 2 Mo 3 O 10-B 2 O 3助熔剂中生长出尺寸为20 mm的优质GdAl 3(BO 3)4(简称GAB)和Nd^3+激活的自变频激光晶体。确定了GAB晶体的透光波长范围、折射率和倍频系数随波长的变化,结果表明其在整个透光范围内均可实现相位匹配。测定了Nd^3+∶GAB晶体在室温下的偏振吸收、荧光光谱和荧光寿命,进行了光谱计算,测试了晶体的自变频激光性能,实现了紫外-可见光-红外-中红外多波段激光输出。展开更多
Growth and morphology of neodymium or ytterbium doped calcium gadolinium yttrium oxoborate (Re∶Ca 4Gd x Y 1- x O(BO 3) 3(Re∶GdYCOB)Re =Nd,Yb; x =0-1)were systematically studied. Polycrystalline materials used for Re...Growth and morphology of neodymium or ytterbium doped calcium gadolinium yttrium oxoborate (Re∶Ca 4Gd x Y 1- x O(BO 3) 3(Re∶GdYCOB)Re =Nd,Yb; x =0-1)were systematically studied. Polycrystalline materials used for Re∶GdYCOB single crystals growth were synthesized by multistage solid phase reaction method.Re∶GdYCOB single crystals were grown by Czochralski technique.The pulling rates are 0.5-2mm/h and the rotation rates are 10-30r/min.Usually 65-75% polycrystalline materials can be transformed into good quality single crystals under our growth conditions. The structures of some as grown Re∶GdYCOB single crystals were measured by using a four circle diffractometer.The results measured show that the space group of the crystals is C 3 s Cm.The determined lattice constants of 8 at% Nd doped Ca 4YO(BO 3) 3 single crystal are a =0.8076nm, b =1.6020nm, c =0.3527nm , β =101.23°.展开更多
用电子探针分析 LaMgAl_(11)O_(19):Nd^(3+)晶体和夹杂物中的成分,结果表明,夹杂物由主成分不同组成所构成,晶体成分整体偏离化学比。进一步用 X 射线荧光技术分析 Al_2O_3过量所生长的晶体成分,得到了生长优质晶体的组分。设计特殊温场...用电子探针分析 LaMgAl_(11)O_(19):Nd^(3+)晶体和夹杂物中的成分,结果表明,夹杂物由主成分不同组成所构成,晶体成分整体偏离化学比。进一步用 X 射线荧光技术分析 Al_2O_3过量所生长的晶体成分,得到了生长优质晶体的组分。设计特殊温场,用提拉法生长出φ25×120mm、无解理α方向的 LaMgAl_(11)O_(19):Nd^(3+)大单晶。展开更多
基金Supported by the National Natural Science Foundation of China (No.60808033)Natural Science Foundation of Jiangxi Province (No.2008GZW0012)
文摘The Nd^3＋：LiGd（WO4） 2 crystal with dimensions of 25mm×28mm×16mm was grown by the top-seeded solution growth method from the 60 mol% Li2W2O7 flux. LiGd（WO4） 2 crystallizes in the tetragonal system with space group I41/a（C4h^6） and cell parameters： a = 5.1986 and c = 11.2652A. The hardness is about 5.0 Mohs＇ scale. The specific heat is 0.40 J·g^-1·K^-1 at 50 oC. The thermal expansion coefficients for a-and c-axes are 1.314×10^-5 and 2.052×10^-5 K^-1,respectively. The room-temperature polarized absorption and emission spectra and the fluorescence decay curve was measured. The parameters of oscillator strengths,the spontaneous transition probabilities,the fluorescence branching ratios,the radiative lifetimes,and the emission cross sections have been investigated based on Judd-Ofelt theory and Füchtbauer-Ladenburg method. The absorption cross-section is 5.19×10^-20 cm^2 at 805 nm for π-polarization and its line width is 15 nm; the emission cross section is 1.726×10^-19 cm^2 at 1060.5 nm for π-polarization. The fluorescence and radiative lifetimes are 86 and 158 μs,respectively. The fluorescence quantum efficiency is 54.43%.
文摘采用熔盐顶部籽晶法从K 2 Mo 3 O 10-B 2 O 3助熔剂中生长出尺寸为20 mm的优质GdAl 3(BO 3)4(简称GAB)和Nd^3+激活的自变频激光晶体。确定了GAB晶体的透光波长范围、折射率和倍频系数随波长的变化,结果表明其在整个透光范围内均可实现相位匹配。测定了Nd^3+∶GAB晶体在室温下的偏振吸收、荧光光谱和荧光寿命,进行了光谱计算,测试了晶体的自变频激光性能,实现了紫外-可见光-红外-中红外多波段激光输出。
文摘Growth and morphology of neodymium or ytterbium doped calcium gadolinium yttrium oxoborate (Re∶Ca 4Gd x Y 1- x O(BO 3) 3(Re∶GdYCOB)Re =Nd,Yb; x =0-1)were systematically studied. Polycrystalline materials used for Re∶GdYCOB single crystals growth were synthesized by multistage solid phase reaction method.Re∶GdYCOB single crystals were grown by Czochralski technique.The pulling rates are 0.5-2mm/h and the rotation rates are 10-30r/min.Usually 65-75% polycrystalline materials can be transformed into good quality single crystals under our growth conditions. The structures of some as grown Re∶GdYCOB single crystals were measured by using a four circle diffractometer.The results measured show that the space group of the crystals is C 3 s Cm.The determined lattice constants of 8 at% Nd doped Ca 4YO(BO 3) 3 single crystal are a =0.8076nm, b =1.6020nm, c =0.3527nm , β =101.23°.
基金This work supported by the Natural Science Foundation of Fujian Province (No.60378031)Key Project of Science andTechnology of Fujian Province (No.2001F004).