The long afterglow fluorescent material of M1-3xAl2O4:Eu2+ x/Dy3+2x(M2+= Sr2+, Ca2+ and Ba2+) phosphors are successfully synthesized by calcining precursor obtained via co-precipitation method at 1300oC for 4 h with r...The long afterglow fluorescent material of M1-3xAl2O4:Eu2+ x/Dy3+2x(M2+= Sr2+, Ca2+ and Ba2+) phosphors are successfully synthesized by calcining precursor obtained via co-precipitation method at 1300oC for 4 h with reducing atmosphere (20% H2 and 80% N2). The phase evolution, morphology and afterglow fluorescent properties are systematically studied by the various instruments of XRD, FE-SEM, PLE/PL spectroscopy and fluorescence decay analysis. The PL spectra shows that the Sr1-3xAl2O4:Eu2+x/Dy3+ 2x phosphors display vivid green emission at s519 nm (4f65d1!4f7 transition of Eu2+) with monitoring of the maximum excitation wavelength at s334 nm (8S7=2!6IJ transition of Eu2+), among which the optimal concentration of Eu2+ and Dy3+ is 15 at.% and 30 at.%, respectively. The color coordinates and temperature of Sr1-3xAl2O4:Eu2+ x/Dy3+ 2x phosphors are approximately at (s0.27, s0.57) and s6700 K, respectively. On the above basis, the M0:55Al2O4:Eu2+ 0:15/Dy3+ 0:3 (M2+= Ca2+ and Ba2+) phosphors is obtained by the same method. The PL spectra of these phosphors shows the strongest blue emission at s440 nm and cyan emission at s499 nm under s334 nm wavelength excitation, respectively, which are blue shifted comparing to Sr1??3xAl2O4:Eu2+ x/Dy3+ 2x phosphors. The color coordinates and temperatures of M0:55Al2O4:Eu2+ 0:15/Dy3+ 0:3 (M2+= Ca2+ and Ba2+) phosphors are approximately at (s0.18, s0.09), s2000 K and (s0.18, s0.42), s11600 K, respectively. In this work, long afterglow materials of green, blue and cyan aluminates phosphors with excellent properties have been prepared, in order to obtain wide application in the field of night automatic lighting and display.展开更多
The synthesis process for La 1- x Sr x Mn 1- y Co y O 3- δ ( x = 0.2, 0.3; y = 0.2, 0.8, designated as LSMC below) perovskite oxides prepared by solid state reaction was investigated using DSC/TG, XRD, EPMA and parti...The synthesis process for La 1- x Sr x Mn 1- y Co y O 3- δ ( x = 0.2, 0.3; y = 0.2, 0.8, designated as LSMC below) perovskite oxides prepared by solid state reaction was investigated using DSC/TG, XRD, EPMA and particle size analysis methods. It was found that LSMCs were all of single phase and the synthesis process might be divided into three stages: the decomposition of reactants, the formation of LaMn(Co)O 3 based oxides, and the formation of LSMC solid solution. Typical average and the peak value of particle size, and the specific surface area are 14.65?μm, 16.4?μm and 1.38?m 2/mL, respectively, for mixed reactants and are 23.81?μm, 32.11?μm and 0.5?m 2/mL, respectively, for powder synthesized at 1?200?℃ for 8?h in air.展开更多
In an effort to improve the performance of superconductors in the field and high temperatures it is important to study the superconducting mechanism. For this reason, the cation substitution can be conducted. One of t...In an effort to improve the performance of superconductors in the field and high temperatures it is important to study the superconducting mechanism. For this reason, the cation substitution can be conducted. One of the high Tc superconductors Gd1Ba2Cu3O7−δ phase with Sr substitution has been synthesized, i.e. Gd1(Ba2−xSrx)Cu3O7−δ compound. The sample was synthesized by using a solid-state reaction method with a wet mixing, sintered for 12 hours at temperature 900°C. The synthesis results are characterized by using XRD. The results of Match-3 software analysis showed high (higher 85%) Gd1Ba2Cu3O7−δ phase was formed. The Sr substitution causes changes to the structure, i.e. the lattice parameters a, b and c, where the orthorhombicity tends to decrease with increasing Sr content. Refinement results show that based on the oxygen occupancy, the total oxygen content tends to increase.展开更多
The X ray diffraction spectra and X ray photoelectron spectroscopy were measured for Sr doped La 1- x Sr x CoO 3 materials with perovskite structure prepared by the solid state reaction method. The in...The X ray diffraction spectra and X ray photoelectron spectroscopy were measured for Sr doped La 1- x Sr x CoO 3 materials with perovskite structure prepared by the solid state reaction method. The influence of heat treatment temperature on the average crystal size of La 1- x Sr x CoO 3 was studied. The surface chemical states of La 1- x Sr x CoO 3 cathodes with different Sr doped content were discussed. The experimental results show that average crystal size of La 1- x Sr x CoO 3 under the condition of heat treatment in the range of 900～1200 ℃ is larger than that at other temperatures, which is of benefit to forming porous electrodes. When La is replaced by Sr gradually, the oxygen vacancy concentration increases. It is of benefit to enhancing the transport property of oxygen ion.展开更多
基金the National Natural Science Foundation of China (No. 51602126)the National Key Research and Development Plan of China (No. 2016YFB0303505)+1 种基金China and University of Jinan Postdoctoral Science Foundation (No. 2017M622118 and XBH1716)the 111 Project of International Corporation on Advanced Cement-based Materials (D17001).
文摘The long afterglow fluorescent material of M1-3xAl2O4:Eu2+ x/Dy3+2x(M2+= Sr2+, Ca2+ and Ba2+) phosphors are successfully synthesized by calcining precursor obtained via co-precipitation method at 1300oC for 4 h with reducing atmosphere (20% H2 and 80% N2). The phase evolution, morphology and afterglow fluorescent properties are systematically studied by the various instruments of XRD, FE-SEM, PLE/PL spectroscopy and fluorescence decay analysis. The PL spectra shows that the Sr1-3xAl2O4:Eu2+x/Dy3+ 2x phosphors display vivid green emission at s519 nm (4f65d1!4f7 transition of Eu2+) with monitoring of the maximum excitation wavelength at s334 nm (8S7=2!6IJ transition of Eu2+), among which the optimal concentration of Eu2+ and Dy3+ is 15 at.% and 30 at.%, respectively. The color coordinates and temperature of Sr1-3xAl2O4:Eu2+ x/Dy3+ 2x phosphors are approximately at (s0.27, s0.57) and s6700 K, respectively. On the above basis, the M0:55Al2O4:Eu2+ 0:15/Dy3+ 0:3 (M2+= Ca2+ and Ba2+) phosphors is obtained by the same method. The PL spectra of these phosphors shows the strongest blue emission at s440 nm and cyan emission at s499 nm under s334 nm wavelength excitation, respectively, which are blue shifted comparing to Sr1??3xAl2O4:Eu2+ x/Dy3+ 2x phosphors. The color coordinates and temperatures of M0:55Al2O4:Eu2+ 0:15/Dy3+ 0:3 (M2+= Ca2+ and Ba2+) phosphors are approximately at (s0.18, s0.09), s2000 K and (s0.18, s0.42), s11600 K, respectively. In this work, long afterglow materials of green, blue and cyan aluminates phosphors with excellent properties have been prepared, in order to obtain wide application in the field of night automatic lighting and display.
文摘The synthesis process for La 1- x Sr x Mn 1- y Co y O 3- δ ( x = 0.2, 0.3; y = 0.2, 0.8, designated as LSMC below) perovskite oxides prepared by solid state reaction was investigated using DSC/TG, XRD, EPMA and particle size analysis methods. It was found that LSMCs were all of single phase and the synthesis process might be divided into three stages: the decomposition of reactants, the formation of LaMn(Co)O 3 based oxides, and the formation of LSMC solid solution. Typical average and the peak value of particle size, and the specific surface area are 14.65?μm, 16.4?μm and 1.38?m 2/mL, respectively, for mixed reactants and are 23.81?μm, 32.11?μm and 0.5?m 2/mL, respectively, for powder synthesized at 1?200?℃ for 8?h in air.
基金This report is part of the fundamental research report with contract No.486 127/UN14.2/PNL.01.03.00/2016.
文摘In an effort to improve the performance of superconductors in the field and high temperatures it is important to study the superconducting mechanism. For this reason, the cation substitution can be conducted. One of the high Tc superconductors Gd1Ba2Cu3O7−δ phase with Sr substitution has been synthesized, i.e. Gd1(Ba2−xSrx)Cu3O7−δ compound. The sample was synthesized by using a solid-state reaction method with a wet mixing, sintered for 12 hours at temperature 900°C. The synthesis results are characterized by using XRD. The results of Match-3 software analysis showed high (higher 85%) Gd1Ba2Cu3O7−δ phase was formed. The Sr substitution causes changes to the structure, i.e. the lattice parameters a, b and c, where the orthorhombicity tends to decrease with increasing Sr content. Refinement results show that based on the oxygen occupancy, the total oxygen content tends to increase.
文摘The X ray diffraction spectra and X ray photoelectron spectroscopy were measured for Sr doped La 1- x Sr x CoO 3 materials with perovskite structure prepared by the solid state reaction method. The influence of heat treatment temperature on the average crystal size of La 1- x Sr x CoO 3 was studied. The surface chemical states of La 1- x Sr x CoO 3 cathodes with different Sr doped content were discussed. The experimental results show that average crystal size of La 1- x Sr x CoO 3 under the condition of heat treatment in the range of 900～1200 ℃ is larger than that at other temperatures, which is of benefit to forming porous electrodes. When La is replaced by Sr gradually, the oxygen vacancy concentration increases. It is of benefit to enhancing the transport property of oxygen ion.