La0.8Sr0.2FeO3-δ is a new kind of cathode material for intermediate SOFC, but its electrochemical activity is relative poor for the lanthanum gallate based solid oxide fuel cell. In this paper, a novel composite cath...La0.8Sr0.2FeO3-δ is a new kind of cathode material for intermediate SOFC, but its electrochemical activity is relative poor for the lanthanum gallate based solid oxide fuel cell. In this paper, a novel composite cathode of La0.8Sr0.2FeO3-δ/La0.9Sr0.1Ga0.8Mg0.2O3-δ was prepared on the LSGM electrolyte substrate by screen-printing method. The results of cathodic polarization measurements show that the overpotential decreases significantly when the composite cathode is used instead of the La0.8Sr0.2FeO3-δ single layer cathode. The cathodic overpotential of the composite La0.8Sr0.2FeO3-δ/La0.9Sr0.1Ga0.8Mg0.2O3-δ cathode is 150 mV at the current density of 0.2 A·cm-2 at 800 ℃, while the cathodic overpotential of the La0.8Sr0.2FeO3-δ single layer cathode is higher than 260 mV at the same condition. The electrochemical impedance spectroscopy was employed to investigate the polarization resistance of the cathode. The polarization resistance of the composite cathode is 1.20 Ω·cm2 in open circuit condition, while the value of the single La0.8Sr0.2FeO3-δ cathode is 1.235 Ω·cm2.展开更多
The perovskite-type nanocrystal La0.8Sr0.2FeO3 was prepared using a sol-gel auto-combustion method with citric acid as the chelating agent. The metal ions coordination compound, obtained from nitrate and citrate, unde...The perovskite-type nanocrystal La0.8Sr0.2FeO3 was prepared using a sol-gel auto-combustion method with citric acid as the chelating agent. The metal ions coordination compound, obtained from nitrate and citrate, underwent an auto-combustion process and voluminous ashes formed when calcining the complex in the air. Some analytical methods, which consisted of FT-IR, XRD, TEM and wave-guide, were used to characterize the gel and the final products. It was shown that metal ions and carboxyl were combined to form a homogeneous organic complex base salts in the process of gelation. The nanocrystalline had dielectric loss in the microwave frequency range of measurement.展开更多
基金This work was financially supported by the National Natural Science Foundation of China (No. 90510006) and the National High-Tech Research and Development of China (No. 2003AA302440).
文摘La0.8Sr0.2FeO3-δ is a new kind of cathode material for intermediate SOFC, but its electrochemical activity is relative poor for the lanthanum gallate based solid oxide fuel cell. In this paper, a novel composite cathode of La0.8Sr0.2FeO3-δ/La0.9Sr0.1Ga0.8Mg0.2O3-δ was prepared on the LSGM electrolyte substrate by screen-printing method. The results of cathodic polarization measurements show that the overpotential decreases significantly when the composite cathode is used instead of the La0.8Sr0.2FeO3-δ single layer cathode. The cathodic overpotential of the composite La0.8Sr0.2FeO3-δ/La0.9Sr0.1Ga0.8Mg0.2O3-δ cathode is 150 mV at the current density of 0.2 A·cm-2 at 800 ℃, while the cathodic overpotential of the La0.8Sr0.2FeO3-δ single layer cathode is higher than 260 mV at the same condition. The electrochemical impedance spectroscopy was employed to investigate the polarization resistance of the cathode. The polarization resistance of the composite cathode is 1.20 Ω·cm2 in open circuit condition, while the value of the single La0.8Sr0.2FeO3-δ cathode is 1.235 Ω·cm2.
文摘The perovskite-type nanocrystal La0.8Sr0.2FeO3 was prepared using a sol-gel auto-combustion method with citric acid as the chelating agent. The metal ions coordination compound, obtained from nitrate and citrate, underwent an auto-combustion process and voluminous ashes formed when calcining the complex in the air. Some analytical methods, which consisted of FT-IR, XRD, TEM and wave-guide, were used to characterize the gel and the final products. It was shown that metal ions and carboxyl were combined to form a homogeneous organic complex base salts in the process of gelation. The nanocrystalline had dielectric loss in the microwave frequency range of measurement.