Electrochemical hydrogen storage properties of La_(0.95)Mg_(2.05)Ni_9 alloy prepared by mechanical alloying

The structure, microstructure, thermal stability and hydriding characteristics of amorphous La0.95-Mg2.05Ni9 have been investigated with differential thermal analysis, X-ray diffraction, scanning electron microscopy and battery test. It is found that the increase in mechanical alloying time leads to enhancement in thermal stabilities of amorphous La0.95Mg2.05Ni9 alloy. The amorphous alloy has good charge/discharge ability at room temperature(430 mA·h·g-1), but the discharge capacity decreases seriously during cycling tests due to the crystallization of amorphous and oxidization of magnesium on the particle surface in alkaline aqueous solution.

球磨La_(0.92)Mg_(2.08)Ni_9合金的结构及性能研究

用差热分析仪、X射线衍射仪、扫描电子显微镜及电池综合性能测试仪研究了球磨La0.92Mg2.08Ni9样品的组织结构、形貌、热稳定性及贮氢性能等。结果表明 :经400r/min球磨35～50h后 ,La0.92Mg2.08Ni9 样品由非晶组成 ,颗粒形状为球形或近球形 ,颗粒尺寸为0.2～5μm。随着球磨时间的延长 ,非晶样品的热稳定性能增加,颗粒尺寸减小,电化学活化性能降低。经400r/min球磨35h的样品具有较好的室温贮氢性能 ,首次电化学充放电即达到最大的放电容量405mAh.g-1。

La_(0.67)Mg_(0.33)Ni_(2.5)Cu_(0.5)贮氢合金磁热处理工艺的正交设计

利用L9(34)正交表安排实验,考察磁热处理的温度、时间及磁感应强度对La0.67Mg0.33N i2.5Cu0.5合金的吸放氢反应热力学和动力学的影响,结合极差分析和方差分析研究了各因素对考核指标的显著性影响,并得到合金磁热处理的优化工艺:热处理温度850℃,处理时间1 h和磁感应强度4 T.在此条件下处理后的合金,吸放氢的质量分数分别为1.33%和1.14%,焓变为-59.69 kJ/mol,吸热峰顶所对应的温度为86.3℃,吸放氢特征时间(tξ=0.875)分别为11.2和108.7 s.结果表明,该合金与其它工艺下的样品相比,吸氢量最大,放氢后物相结构最稳定,吸热峰顶所对应的温度最低,吸放氢速度最快.

水溶液中电沉积制备LaMg_2Ni_9储氢合金

利用水溶液电沉积法制备La Mg_2Ni_9储氢合金膜,通过测定合金膜的循环伏安曲线(CV)、交流阻抗(EIS)、Tafel极化曲线等研究其电化学性能,采用扫描电镜(SEM)、X射线衍射(XRD)、能谱(EDS)对合金膜表面形貌、结构及组成进行研究。结果表明:电沉积电流密度为40 A/dm^2时,La Mg_2Ni_9合金膜的表面粗糙并伴有裂纹,析氢电流密度为5.37A/dm^2,表观活化自由能△G~≠最低为47.26 k J/mol,证明合金膜良好的析氢性能;吸附值Q达到最大值为0.091μF·cm^(-2),表明合金膜具有较高的储氢性能。