Samples of manganese oxides La（1-x）2/3Ca1/3MnO3（x 〈 0.10） with Lavacancy were prepared by standard solid-state reaction method. All the samples are single phase, with orthorhombic symmetry （Pnma ）, analyzed by ...Samples of manganese oxides La（1-x）2/3Ca1/3MnO3（x 〈 0.10） with Lavacancy were prepared by standard solid-state reaction method. All the samples are single phase, with orthorhombic symmetry （Pnma ）, analyzed by XRD and with Rietveld Refinement. The effect of different La-site vacancies concentration on electronic transport of La（1-x）2/3Ca1/3MnO3 was investigated. The insulator-metal transition temperature （about 267 K） nearly remains unchanged with the increase of vacancy concentration, which indicates that small La-vacancy does not destroy the double exchange interaction. But the electronic resistance increases and MR value decreases with La-vacancy content x 〉 0.04. The maximum of the MR value （8 T） is about 220% at transition temperature （TMI）.展开更多
文摘Samples of manganese oxides La（1-x）2/3Ca1/3MnO3（x 〈 0.10） with Lavacancy were prepared by standard solid-state reaction method. All the samples are single phase, with orthorhombic symmetry （Pnma ）, analyzed by XRD and with Rietveld Refinement. The effect of different La-site vacancies concentration on electronic transport of La（1-x）2/3Ca1/3MnO3 was investigated. The insulator-metal transition temperature （about 267 K） nearly remains unchanged with the increase of vacancy concentration, which indicates that small La-vacancy does not destroy the double exchange interaction. But the electronic resistance increases and MR value decreases with La-vacancy content x 〉 0.04. The maximum of the MR value （8 T） is about 220% at transition temperature （TMI）.