A series of oxides(La_(2-x)Ce_xCoO_(4±y)) with perovskite-like structure were prepared by the Pechini sol–gel method for dry reforming of methane reaction(DRM). The prepared catalysts were characterized by BET, ...A series of oxides(La_(2-x)Ce_xCoO_(4±y)) with perovskite-like structure were prepared by the Pechini sol–gel method for dry reforming of methane reaction(DRM). The prepared catalysts were characterized by BET, XRD,TGA, H_2-TPR and SEM. Experimental results indicate that the addition of Ce can impact both sample morphology and catalytic performance significantly compared with La_2CoO_4 catalyst, and LaCeCoO_4 presented the highest catalytic ability among all the samples. The Ce addition tends to increase the specific surface area of La_(2-x)Ce_xCoO_(4±y)from 0.2 to 8.5 m^2·g^(-1), suggesting that LaCeCoO_4 catalyst contained more well-dispersed active sites and more space to reaction. Moreover, the catalytic performance and anti-coking ability were substantially improved after Ce addition during DRM, which may be attributed to the decrease of LaCoO_3 particle size and growth of oxygen storage capacity, respectively.展开更多
A solid ternary mixture consisting of NaF,silicon and one metal oxide such as La2O3,CeO2,Pr6O11,Nd2O3,and Y2O3 was prepared and usedas de-fluorinated reagent for CF4 decomposition.The results show that 90% conversion ...A solid ternary mixture consisting of NaF,silicon and one metal oxide such as La2O3,CeO2,Pr6O11,Nd2O3,and Y2O3 was prepared and usedas de-fluorinated reagent for CF4 decomposition.The results show that 90% conversion of CF4 can be reached initially over NaF-Si-La2O3,NaF-Si-CeO2,NaF-Si-Nd2O3,and NaF-Si-Y2O3 at 850 C.The fresh and used reagents were characterized using XRD and XPS techniques.It was found that the active components of NaF and metal oxides in NaF-Si-CeO2,NaF-Si-Pr6O11,NaF-Si-Nd2O3,and NaF-Si-Y2O3 weretransformed into inert phases of mixed metal fluorides and silicates,respectively,resulting in an ineffective utilization of these de-fluorinatedreagents,whereas no inert phases from NaF and La2O3 can be observed in the used NaF-Si-La2O3,indicating the NaF-Si-La2O3 reagent couldbe utilized more efficiently than the other reagents in CF4 decomposition.展开更多
Single crystals of huntite type double borates possess excellent physical and chemical properties and are applied in laser optics.Substituted with various rare earths and Ga 3+ ,Cr 3+ or Sc 3+ ions the properties of t...Single crystals of huntite type double borates possess excellent physical and chemical properties and are applied in laser optics.Substituted with various rare earths and Ga 3+ ,Cr 3+ or Sc 3+ ions the properties of these borates can be improved. [1] For the first time double borates RGa 3(BO 3) 4(R=Y 3+ ,Sm 3+ ,Eu 3+ ,Gd 3+ ,Tb 3+ and Dy 3+ )were synthesised by Blasse and Bril [2] at 750℃. The goal of the present work is to study the solid state reactions in the R 2O 3∶3Ga 2O 3∶4B 2O 3(R=La 3+ ,Y 3+ ,Ho 3+ ,Yb 3+ )systems.Such reactions can lead to RGa 3(BO 3) 4 formation. Reagent grade oxide powders were used as reactants and mixed together in desired rations in acetone.Then differential thermal analysis(DTA)was used to study the formations of borates and changes in structure of mixtures heated up to 1000℃.In addition pellets were prepared by using 15mPa pressure and sintered at different temperatures from 600℃ to 1100℃ for 20 hours in order to study the reactions by IR and X ray.展开更多
以氨基-1,2,4-三唑和2-偕二硝甲基-5-硝基四唑(HDNMNT)为原料,通过中和反应合成出两种新型含能离子盐——2-偕二硝甲基-5-硝基四唑3-氨基-1,2,4-三唑盐(3-ATDNMNT)和2-偕二硝甲基-5-硝基四唑4-氨基-1,2,4-三唑盐(4-ATDNMNT),收率分别为9...以氨基-1,2,4-三唑和2-偕二硝甲基-5-硝基四唑(HDNMNT)为原料,通过中和反应合成出两种新型含能离子盐——2-偕二硝甲基-5-硝基四唑3-氨基-1,2,4-三唑盐(3-ATDNMNT)和2-偕二硝甲基-5-硝基四唑4-氨基-1,2,4-三唑盐(4-ATDNMNT),收率分别为95.4%和96.7%;利用FT-IR、1 H NMR、13C NMR、15 N NMR及元素分析等方法对其结构进行表征;采用量子化学方法计算了3-ATDNMNT和4-ATDNMNT的爆轰性能;在标准状态下(膨胀比为70∶1),利用最小自由能原理,分别计算了两种离子盐在丁羟复合推进剂中的能量性能。结果表明,3-ATDNMNT的爆速和爆压分别为8.587km/s和33.58GPa,4-ATDNMNT的爆速和爆压分别为8.693km/s和34.31GPa。以3-ATDNMNT部分取代丁羟复合推进剂中的AP后,丁羟复合推进剂的理论比冲可达2 635.7N·s/kg。以4-ATDNMNT部分取代丁羟复合推进剂中的AP后,当HTPB、Al、AP及4-ATDNMNT各组分质量分数分别为10%、5%、15%及70%时,获得该丁羟复合推进剂的最高理论比冲为2 677.2N·s/kg。展开更多
基金Supported by the National Natural Science Foundation of China(21276209)the Natural Science Foundation of Shaanxi Province(2017JM2033)the Local Service Fund of Education Department of Shaanxi Province(18JF031)
文摘A series of oxides(La_(2-x)Ce_xCoO_(4±y)) with perovskite-like structure were prepared by the Pechini sol–gel method for dry reforming of methane reaction(DRM). The prepared catalysts were characterized by BET, XRD,TGA, H_2-TPR and SEM. Experimental results indicate that the addition of Ce can impact both sample morphology and catalytic performance significantly compared with La_2CoO_4 catalyst, and LaCeCoO_4 presented the highest catalytic ability among all the samples. The Ce addition tends to increase the specific surface area of La_(2-x)Ce_xCoO_(4±y)from 0.2 to 8.5 m^2·g^(-1), suggesting that LaCeCoO_4 catalyst contained more well-dispersed active sites and more space to reaction. Moreover, the catalytic performance and anti-coking ability were substantially improved after Ce addition during DRM, which may be attributed to the decrease of LaCoO_3 particle size and growth of oxygen storage capacity, respectively.
基金supported by the National Natural Science Foundation of China (No. 20976149)
文摘A solid ternary mixture consisting of NaF,silicon and one metal oxide such as La2O3,CeO2,Pr6O11,Nd2O3,and Y2O3 was prepared and usedas de-fluorinated reagent for CF4 decomposition.The results show that 90% conversion of CF4 can be reached initially over NaF-Si-La2O3,NaF-Si-CeO2,NaF-Si-Nd2O3,and NaF-Si-Y2O3 at 850 C.The fresh and used reagents were characterized using XRD and XPS techniques.It was found that the active components of NaF and metal oxides in NaF-Si-CeO2,NaF-Si-Pr6O11,NaF-Si-Nd2O3,and NaF-Si-Y2O3 weretransformed into inert phases of mixed metal fluorides and silicates,respectively,resulting in an ineffective utilization of these de-fluorinatedreagents,whereas no inert phases from NaF and La2O3 can be observed in the used NaF-Si-La2O3,indicating the NaF-Si-La2O3 reagent couldbe utilized more efficiently than the other reagents in CF4 decomposition.
文摘Single crystals of huntite type double borates possess excellent physical and chemical properties and are applied in laser optics.Substituted with various rare earths and Ga 3+ ,Cr 3+ or Sc 3+ ions the properties of these borates can be improved. [1] For the first time double borates RGa 3(BO 3) 4(R=Y 3+ ,Sm 3+ ,Eu 3+ ,Gd 3+ ,Tb 3+ and Dy 3+ )were synthesised by Blasse and Bril [2] at 750℃. The goal of the present work is to study the solid state reactions in the R 2O 3∶3Ga 2O 3∶4B 2O 3(R=La 3+ ,Y 3+ ,Ho 3+ ,Yb 3+ )systems.Such reactions can lead to RGa 3(BO 3) 4 formation. Reagent grade oxide powders were used as reactants and mixed together in desired rations in acetone.Then differential thermal analysis(DTA)was used to study the formations of borates and changes in structure of mixtures heated up to 1000℃.In addition pellets were prepared by using 15mPa pressure and sintered at different temperatures from 600℃ to 1100℃ for 20 hours in order to study the reactions by IR and X ray.
文摘以氨基-1,2,4-三唑和2-偕二硝甲基-5-硝基四唑(HDNMNT)为原料,通过中和反应合成出两种新型含能离子盐——2-偕二硝甲基-5-硝基四唑3-氨基-1,2,4-三唑盐(3-ATDNMNT)和2-偕二硝甲基-5-硝基四唑4-氨基-1,2,4-三唑盐(4-ATDNMNT),收率分别为95.4%和96.7%;利用FT-IR、1 H NMR、13C NMR、15 N NMR及元素分析等方法对其结构进行表征;采用量子化学方法计算了3-ATDNMNT和4-ATDNMNT的爆轰性能;在标准状态下(膨胀比为70∶1),利用最小自由能原理,分别计算了两种离子盐在丁羟复合推进剂中的能量性能。结果表明,3-ATDNMNT的爆速和爆压分别为8.587km/s和33.58GPa,4-ATDNMNT的爆速和爆压分别为8.693km/s和34.31GPa。以3-ATDNMNT部分取代丁羟复合推进剂中的AP后,丁羟复合推进剂的理论比冲可达2 635.7N·s/kg。以4-ATDNMNT部分取代丁羟复合推进剂中的AP后,当HTPB、Al、AP及4-ATDNMNT各组分质量分数分别为10%、5%、15%及70%时,获得该丁羟复合推进剂的最高理论比冲为2 677.2N·s/kg。