NiAl-La2O3 compostite coating was prepared by Ni-La2O3 electrodeposited and pack aluminized at 1173 K on Ni-base superalloy K38. The result of oxidation in air at 1273 K for 20 h shows that the oxidation rate of NiAl-...NiAl-La2O3 compostite coating was prepared by Ni-La2O3 electrodeposited and pack aluminized at 1173 K on Ni-base superalloy K38. The result of oxidation in air at 1273 K for 20 h shows that the oxidation rate of NiAl-La2O3 coating is remarkably lower than that of NiAl-La2O3 free coating. The oxide film surface morphology of NiAl-La2O3 composite coating was obviously modified after oxidation. HREM study of the fine structure of aluminum oxide on the composite coating shows that La2O3 particles with diameter of 10 ̄40 nm were incorporated into u-Al2O3 layer. It is believed that La2O3 dispersive particles improve NiAl coating oxidation resistance by a way to influence aluminum layer microstructure and to modify cationic transfer behavior of the layer growth.展开更多
文摘NiAl-La2O3 compostite coating was prepared by Ni-La2O3 electrodeposited and pack aluminized at 1173 K on Ni-base superalloy K38. The result of oxidation in air at 1273 K for 20 h shows that the oxidation rate of NiAl-La2O3 coating is remarkably lower than that of NiAl-La2O3 free coating. The oxide film surface morphology of NiAl-La2O3 composite coating was obviously modified after oxidation. HREM study of the fine structure of aluminum oxide on the composite coating shows that La2O3 particles with diameter of 10 ̄40 nm were incorporated into u-Al2O3 layer. It is believed that La2O3 dispersive particles improve NiAl coating oxidation resistance by a way to influence aluminum layer microstructure and to modify cationic transfer behavior of the layer growth.