Most motor oils are made from mineral oils derived from petroleum, the reserves of which are limited and exhaustible. The aim of this study is to produce and characterize motor oil formulations based on mixtures of ru...Most motor oils are made from mineral oils derived from petroleum, the reserves of which are limited and exhaustible. The aim of this study is to produce and characterize motor oil formulations based on mixtures of rubber latex cup bottom oil (RLCBO) and used frying oil (UFO). The results show that these formulations have a density between 0.91 and 0.92. These densities evolve linearly with the proportion of cup bottom oil and temperature. Similarly, the kinematic viscosity of the blends follows an exponential relationship with temperature. By plotting the logarithm of these kinematic viscosities against the inverse of the temperature, we were able to determine the activation energy of the various blends and deduce that the formulations behave Newtonian.展开更多
Natural rubber latex （NRL） and methyl methacrylate （MMA） grafted rubber latex were blended in different ratios and irradiated at various absorbed doses by gamma rays from Co-60 source at room temperature. The tens...Natural rubber latex （NRL） and methyl methacrylate （MMA） grafted rubber latex were blended in different ratios and irradiated at various absorbed doses by gamma rays from Co-60 source at room temperature. The tensile properties, swelling ratio and permanent set were measured. The maximum tensile strength and modulus at 500% elongation were obtained at an absorbed dose of 8 kGy. Modulus increases from 6.99 MPa to 9.87 MPa for an increase in proportion of MMA grafted rubber from 40% to 60% in the blend at similar absorbed dose. Elongation at break and swelling ratio decrease with increasing absorbed dose as well as the MMA grafted rubber content in the blends. The decreasing trend of permanent set is high up to 5 kGy absorbed dose, and beyond that dose, it becomes almost flat.展开更多
文摘Most motor oils are made from mineral oils derived from petroleum, the reserves of which are limited and exhaustible. The aim of this study is to produce and characterize motor oil formulations based on mixtures of rubber latex cup bottom oil (RLCBO) and used frying oil (UFO). The results show that these formulations have a density between 0.91 and 0.92. These densities evolve linearly with the proportion of cup bottom oil and temperature. Similarly, the kinematic viscosity of the blends follows an exponential relationship with temperature. By plotting the logarithm of these kinematic viscosities against the inverse of the temperature, we were able to determine the activation energy of the various blends and deduce that the formulations behave Newtonian.
文摘Natural rubber latex （NRL） and methyl methacrylate （MMA） grafted rubber latex were blended in different ratios and irradiated at various absorbed doses by gamma rays from Co-60 source at room temperature. The tensile properties, swelling ratio and permanent set were measured. The maximum tensile strength and modulus at 500% elongation were obtained at an absorbed dose of 8 kGy. Modulus increases from 6.99 MPa to 9.87 MPa for an increase in proportion of MMA grafted rubber from 40% to 60% in the blend at similar absorbed dose. Elongation at break and swelling ratio decrease with increasing absorbed dose as well as the MMA grafted rubber content in the blends. The decreasing trend of permanent set is high up to 5 kGy absorbed dose, and beyond that dose, it becomes almost flat.