Preparation and Piezoelectric Properties of CuO-added(Ag_(0.75)Li_(0.1)Na_(0.1)K_(0.05_)NbO_3 Lead-free Ceramics

CuO-doped（Ag0.75Li0.1Na0.1K0.05）NbO3（ALNKN-xCuO, x = 0.2mol%） lead-free piezoelectric ceramics were prepared by the solid-state reaction method in air atmosphere. The effects of CuO addition on the phase structure, microstructure, and piezoelectric properties of the ceramics were investigated. The experimental results show that the ALNKN ceramics without doping CuO possess rhombohedral phase along with K2NbrO16- type phase and metallic silver phase. For all of the CuO-doped ALNKN ceramics, a pure perovskite structure with the orthorhombic phase was obtained by enclosing the samples in a corundum tube. A homogeneous microstructure with＇the grain size of about 1 ~tm was formed for the ceramics with 0.5mo1% CuO. The grain size increases with increasing amount of CuO. The temperature dependence of dielectric properties indicates that the ferroelectric phase of the ALNKN-xCuO ceramics becomes less stable with the addition of CuO. The ceramics with x = lm01% exhibit relatively good electrical properties along with a high Curie temperature. These results will provide a helpful guidance to preparing other AN-based ceramics by solid-state reaction method in air atmosphere.

Effect of Li content on the microstructure and properties of lead-free piezoelectric(K_(0.5)Na_(0.5))_(1-x)Li_xNbO_3 ceramics prepared by SPS

Lead-free piezoelectric （K0.5sNa0.5）1-xLixNbO3 （x = 0at%-20at%） ceramics were synthesized by spark plasma sintering （SPS） at low temperature and the effects of LiNbO3 addition on its crystal structure and properties were also studied. When the Li content was less than 6at%, a single proveskite phase with the similar structure of （K0.5Na0.5）NbO3 was formed; and a secondary phase with K3Li2Nb5O15 structure was observed in the 6at% 〈 x 〈 20at% compositional range. Furthermore, LiNbO3 existed as the third phase when the Li content was higher than 8at%. The grain sizes increased from 200-500 nm to 5-8 μm when the K3Li2Nb5O15 and LiNbO3 like phases were formed. With increasing Li content, the relative density of the ceramics first decreased from 97% to 93% and then kept constant. The piezoelectric coefficient d33, dielectric constant, and planner electromechanical coupling factor exhibited a decreasing tendency with increasing Li content because of the decrease in density and the formation of the secondary phase such as K3Li2Nb5O15 and LiNbO3. The formation of dense microstructure with a single phase is necessary in improving the properties of the （K0.5Na0.5）1-xLixNbO3 ceramics.

Piezoelectric and dielectric properties of Li_x(K_(0.46)Na_(0.54))_(1-x)Nb_(0.86)Ta_(0.1)Sb_(0.04)O_3 lead-free ceramics

Lead-free piezoelectric ceramics Lix(K0.46Na0.54)1-xNb0.86Ta0.1Sb0.04O3 (with x ranging from 0 to 0.1) were synthesized by conventional solid state sintering method. The effect of cationic substitution of Li for K and Na in the A sites of perovskite lattice on the structure, phase transition behavior and electrical properties were investigated. Morphotropic phase boundaries(MPB) between orthorhombic and tetragonal phase are found in the composition range of 0.06≤x≤0.08. Analogous to Pb(Zr,Ti)O3, the dielectric and piezoelectric properties are enhanced for the composition near the morphotropic phase boundary. The Li0.06(K0.46Na0.54)0.94- Nb0.86Ta0.1Sb0.04O3 ceramics show excellent electrical properties, that is, piezoelectric constant d33=215 pC/N, planar electromechanical coupling factor kp=41%, dielectric constant ε 3T3 /ε0=1 303, and dielectric loss tan δ=2.45%. The results indicate that Lix(K0.46Na0.54)1-x Nb0.86 Ta0.1Sb0.04O3 ceramic is a promising lead-free piezoelectric material.

Microstructure and electrical properties of Ti-modified (Na_(0.5)K_(0.5))(Ti_xNb_(1-x))O_3 lead-free piezoelectric ceramics

Ti-Modified (Na0.5K0.5)(TixNb1-x)O3 (NKNT) piezoelectric ceramics were fabricated by double-layer buried powder process at 1020°C for 2 h. The microstructures,and piezoelectric and dielectric properties of the lead-free NKNT ceramics were investigated. X-ray diffraction re-sults indicated that Ti4+ had diffused into the (Na0.5K0.5)NbO3 lattices to form a solid solution with a perovskite structure. The introducing of Ti into the (Na0.5K0.5)NbO3 solid solution effectively reduced the sintering temperature and...

Effects of Na/K ratio on the phase structure and electrical properties of Na_xK_(1-x)NbO_3 lead-free piezoelectric ceramics

Lead-free piezoelectric NaxK1-xNbO3（x = 0.3-0.8）（NKN） ceramics were fabricated by normal sintering at 1060°C for 2 h.Microstructures and electrical properties of the ceramics were investigated with a special emphasis on the influence of Na content.The grain size of the produced dense ceramic was decreased by increasing Na content.A discontinuous change in the space distance was found at the composition close to Na0.7K0.3NbO3 ceramic, which indicates the presence of a transitional composition between two different orthorhombic phases, which is similar to the behavior of morphotropic phase boundary（MPB） in NaxK1-xNbO3 ceramics.Such MPB-like behavior contributes to the enhanced piezoelectric coefficient d33 of 122 pC/N, planar-mode electromechanical coupling coefficient kP of 28.6%, and dielectric constant εr of 703, respectively for the Na0.7K0.3NbO3 ceramic.Cubic temperature TC and the transitional temperature TO-T from orthorhombic to tetragonal phase are observed at around 420°C and 200°C, respectively.

Microstructures and Electrical Properties of Bi_(0.5)-(Na_(1-x-y)K_xLi_y)_(0.5)TiO_3 Lead-free Piezoelectric Ceramics

The microstructures and electrical properties of Bi0.5（Na1-x-yKxLiy）0.5TiO3 lead-free piezoelectric ceramics were studied.These ceramics were prepared by conventional ceramic technique.XRD analysis reveals that the ceramics possess almost pure perovskite phase when y≤0.2.The SEM results show that,with more amounts of Li＋,the crystalline grain growing speed is accelerated,and the sintering temperature can effectively be decreased.The measurements of piezoelectric properties indicate that the ceramics with relatively low amount of Li＋ and high amount of K＋ have comparatively large piezoelectricity.The dielectric measurements show that the ceramics have properties like relaxor ferroelectrics and diffuse phase transition（DPT） at Td and Tc,respectively.The results of ferroelectric measurements reveal the system has relatively higher remanent polarization Pr（27.6 μC/cm2） and lower coercive field Ec（37.5 kV/cm）.

Effects of A-site non-stoichiometry on the structural and electrical properties of 0.96K_(0.5)Na_(0.5)NbO_3-0.04LiSbO_3 lead-free piezoelectric ceramics

Effects of A-site non-stoichiometry on the structural and electrical properties of 0.96K0.5＋xNa0.5＋xNbO3- 0.04LiSbO3 lead-free piezoelectric ceramics were examined for 0 ≤ x ≤0.02. The piezoelectric coefficients exhibited a maximum, d33 = 187 pC/N at x = 0.0075, coinciding with the maximum of the grain size and the apparent density at x = 0.0075. The apparent density and the piezoelectric coefficients decreased with increasing x at higher x which was likely due to the crystal geometrical distortion of 0.96K0.5＋xNa0.5＋xNbO3-0.04LiSbO3. In addition, super-large grains were found and this may be due to liquid phase sintering. Excess （K＋＋Na＋） attracted a sum of space charges to keep the charge neutral, resulting in charge leakage during the course of ceramic polarization, influencing the piezoelectric and ferroelectric properties. These findings are of importance for guiding the design of Ko.sNao.sNbO3-based lead-free ceramics with enhanced electrical properties.

Manufacture and Cytotoxicity of a Lead-free Piezoelectric Ceramic as a Bone Substitute—Consolidation of Porous Lithium Sodium Potassium Niobate by Cold Isostatic Pressing

Aim The piezoelectric properties and cytotoxicity of a porous lead-free piezoelectric ceramic for use as a direct bone substitute were investigated. Methodology Cold isostatic pressing （CIP） was applied to fabricate porous lithium sodium potassium niobate （Li0.06Na0.5K0.44） NbO3 specimens using a pore-forming method. The morphologies of the CIP-processed specimens were characterized and compared to those of specimens made by from conventional pressing procedures. The effects of the ceramic on the attachment and proliferation of osteoblasts isolated from the cranium of 1-day-old Sprague- Dawley rats were examined by a scanning electron microscopy （SEM） and metbylthiazol tetrazolium （MTT） assay. Results The results showed that CIP enhanced piezoelectricity and biological performance of the niobate specimen, and also promoted an extracellular matrix-like topography of it. In vitro studies showed that the CIP-enhanced material had positive effects on the attachment and proliferation of osteoblasts. Conclusion Niobate ceramic generated by CIP shows a promise for being a piezoelectric composite bone substitute.

Phase Structure, Microstructure and Electrical Properties of K_xNa_((1-x))NbO_3 Piezoelectric Ceramics with Different K/Na Ratio

The K_xNa_((1-x))NbO_3(x=0.45, 0.46, 0.47, 0.48, 0.49, 0.50) lead-free piezoelectric ceramics was fabricated by conventional solid-state sintering method. It was found that the ratio of alkaline metal would affect the microstructure, bulk density, and optimum sintering temperatures of ceramics. Meanwhile, the electrical properties were also influenced by modulating the K/Na ratio, exhibiting corresponding composition-dependent properties. The optimum electrical properties of K_xNa_((1-x))NbO_3 such as piezoelectric constant d_(33) = 115 pC/N, mechanical quality factor Q_m = 20, Curie temperature Tc = 365 ~oC, ε_(33)~T/ε_0= 588.1, dielectric loss tan δ = 0.024, bulk density(ρ) = 3.08 g/cm^3, remnant polarization(P_r) = 8.87 μC/cm^2 and coercive field(Ec) = 13.79 kV/cm were obtained at x = 0.46.

Modified phase transition and electrical properties of [Li_(0.05)(Na_(0.535)K_(0.48))_(0.95)]- (Nb_(0.94)Sb_(0.06))O_3 lead-free piezoelectric ceramic by sintering temperature

Li/Sb-doped (Na,K)NbO3 with a nominal composition of [Li0.05(Na0.535K0.48)0.95](Nb0.94Sb0.06)O3 ceramic was synthesized by normal sintering. The phase structure, microstructure, and electrical properties were investigated with a special emphasis on the influence of the sintering temperature. A polymorphic phase transition (PPT) from orthorhombic to tetragonal symmetry was observed when the sintering temperature was raised from 1040 to 1050 ℃, whereby the piezoelectric coefficient d33 and the electromechanical coupling coefficient kp reached the peak values of 245 pC·N-1 and 41.2%, respectively. The PPT induced by varying the sintering temperature is due to the different volatilization extents of alkali metals and appears to a lower sintering temperature with increasing Li content. The trace modifying of alkali metal content is more effective than doping B site element to enhance the d33 value.

Effects of Excess Barium on the Structure and Electrical Properties of(Ba,Ca)TiO_3 Piezoelectric Ceramics with High Mechanical Quality Factors

Manganese-doped Ba（0.925）Ca（0.075）TiO3 lead-free piezoelectric ceramics（abbreviated as BCT）with high mechanical quality factor were synthesized by conventional solid-state reaction method.The effects of excess Ba on the crystal structure,microstructure,and electrical properties of the ceramics were systematically investigated.X-ray diffraction and Raman spectra revealed that Ca^2＋ions were pushed from Ba sites to Ti sites of BCT when 1.5 mol%extra Ba^2＋ions were added after sintering.The grain size of the ceramics was decreased by adding extra Ba^2＋ions.The mechanical quality factor and resistivity of the ceramics decreased dramatically when the excess Ba was more than 1.5 mol%.High piezoelectric coefficients（d（33）=150-190 pC/N）and high mechanical quality factors（Qm=1 000-1 200）were obtained in the ceramics when the excess of Ba was between 0.5 mol%and 1 mol%.These results indicated that the properties of BCT ceramics could be tailored by adjusting the content of Ba.

Effect of poling condition on piezoelectric properties of (K_(0.5)Na_(0.5))NbO_3 ceramics

The lead-free piezoelectric ceramics (K0.5Na0.5)NbO3 (abbreviated as KNN) with the relative density of 97.6% were synthesized by press-less sintering owing to the careful control of processing conditions. The phase structure of KNN ceramics was analyzed. The results show that the pure perovskite phase with orthorhombic symmetry is in all ceramics specimens. The effect of poling conditions on the piezoelectric properties of KNN ceramics was investigated. The results show that the piezoelectric constant d33 and electromechanical coupling factor kp increase with poling field, poling temperature and poling time increasing, then decrease because of electric broken. Take into account of poling conditions and piezoelectric properties of pure KNN ceramics, the optimum poling conditions for pure KNN ceramics are poling field of 4 kV/mm, poling temperature of 140℃and poling time of 20-25 min.

Influence of Composition on Properties of BNT-BT Lead-Free Piezoceramics

Lead-free piezoelectric ceramics of (Bi1/2Na1/2)TiO3-BaTiO3(BNT-BT) were prepared by the conventional piezoelectric ceramic preparation technique (free air atmosphere sintering). The influence of BaTiO3 additive amount and La2O3 additive amount on the properties of BNT-BT lead-free piezoceramics were investigated. The results show that the dielectric constant(ε) and piezoelectric strain constant(d33) of materials start increasing and then decreasing while BaTiO3 additive amount increasing, the e and d33 of materials have maximum value (ε= 1650, d33 = 120 PC·N -1 ) while x (BaTiO3) =0.06 mol. Theεand d33 of materials start increasing and then decreasing while La2O3 additive amount increasing, the e and d33 of materials have maximum value (ε= 1684, d33 = 153 PC·N-1) while w(La2O3) =0.3% . The influence of La2O3 additive amount on the microstructure of BNT-BT piezoelectric ceramics was analysed by SEM( scanning electron microscope). The influence mechanism of La2O3 additive amount on the properties of BNT-BT piezoelectric ceramics was discussed. The BNT-BT ceramics with optimum comprehensive properties were obtained.

Preparation and properties of (K_(0.5)Na_(0.5))NbO_3-LiNbO_3 ceramics

The lead-free piezoelectric ceramics (1-x)(K0.5Na0.5)NbO3-xLiNbO3(abbreviated as KNLN) were synthesized by a traditional solid state reaction. The effects of Li+ on the sintering characteristic, the phase structure and piezoelectric properties of KNLN ceramics were investigated. The sintering temperature of KNN-based ceramics is decreased by doping Li+ and the range of the sintering temperature is narrow. The KNLN ceramics exhibit an enhanced piezoelectric properties with the piezoelectric constant d33 value of 180-200 pC/N, The electromechanical coupling coefficients kp is 35%-40%. The results show that (1-x)(K0.5Na0.5)-NbO3-xLiNbO3 (x=0.05, 0.06) is a promising high-temperature lead free piezoelectric ceramic.

Influence of CeO_2 doping amount on property of BCTZ lead-free piezoelectric ceramics sintered at low temperature

Ba0.85Ca0.15Ti0.9Zr0.1O3 （BCTZ） lead-free piezoelectric ceramics co-doped with CeO2 （x=0.1 wt.%, 0.2 wt.%, 0.3 wt.%, 0.4 wt.%, 0.5 wt.%） and Li2CO3 （0.6 wt.%） were prepared by conventional solid-state reaction method. Influence of CeO2 doping amount on the piezoelectric properties, dielectric properties, phase composition and microstructure of prepared BCTZ lead-free piezoelectric ceramics doped with Li2CO3 were investigated by X-ray diffraction （XRD） and scanning electron microscopy （SEM） and other analytical methods. The results showed that the sintered temperature of BCTZ lead-free piezoelectric ceramics doped with CeO2 decreased greatly when Li2CO3 doping amount was 0.6 wt.%;a pure perovskite structure of BCTZ lead-free piezoelectric ceramics co-doped with Li2CO3 and CeO2 and sintered at 1050 ℃ could also be obtained. The piezoelectric constant （d33）, the relative permit-tivity （εr） and the planar electromechanical coupling factor （kp） of BCTZ ceramics doped with Li2CO3 increased firstly and then de-creased, the dielectric loss （tanδ） decreased firstly and then increased and decreased at last when CeO2 doping amount increased. The influence of CeO2 doping on the properties of BCTZ lead-free piezoelectric ceramics doped with Li2CO3 were caused by“soft effect”and “hard effect”piezoelectric additive and causing lattice distortion. When CeO2 doping amount （x） was 0.2 wt.%, the BCTZ ceramics doped with Li2CO3 （0.6 wt.%） and sintered at 1050 ℃ possessed the best piezoelectric property and dielectric property with d33 of 436 pC/N, kp of 48.3%,εr of 3650, tanδof 1.5%.

Synthesis and Electrical Properties of Li-modified Bi_(0.5)Na_(0.5)TiO_3-BaTiO_3 Lead-free Piezoelectric Ceramics

Lead-free piezoelectric ceramics （1-y）Bi0.5（Na1-xLix）0.5TiO3-yBaTiO3 with x=0-0.125 and y=0.02-0.12 were fabricated by a solid-state reaction process, and their dielectric, piezoelectric and ferroelectric properties were investigated. The results show that the addition of Li^＋ significantly improves the sintering performance and piezoelectric properties of the ceramics. X-ray diffraction （XRD） patterns indicate that the ceramics possess pure perovskite structure. At room temperature, the ceramics provide high piezoelectric charge constant d33 （up to 210 pC/N）, high planar electromechanical coupling factor kp （34.5%）, large remanent polarization Pr （up to 40 μC/cm^2）, and low coercive field Ec （3.0 kV/mm）, which indicates that （1-y）Bi0.5（Na1-xLix）0.5TiO3-yBaTi03 is a good lead-free piezoelectric ceramic.

Multi-phase structure and electrical properties of Bi_(0.5)Li_(0.5)ZrO_3 doping K_(0.48)Na_(0.56)NbO_3 lead-free piezoelectric ceramics

(1–x)K_(0.48)Na_(0.56)NbO_3–xBi_(0.5)Li_(0.5)ZrO_3(KNN–x BLZ, x = 0–0.06) lead-free piezoelectric ceramics were prepared by the conventional solid-state sintering method, and their phase structures and electric properties as well as T_C were systematically investigated. The orthorhombic–tetragonal(O–T) two phases were detected in all(1–x)K_(0.48)Na_(0.56)NbO_3–xBi_(0.5)Li_(0.5)ZrO_3 ceramics at 0.01 ≤ x ≤ 0.05. Due to the appropriate ratio between O phase and T phase(CO/C T= 45/55), high piezoelectric properties of d 33= 239 pC/N, k_p= 34%, and P_r = 25.23 μC/cm^2 were obtained at x = 0.04. Moreover, a high T_C = 348 ℃ was also achieved in KNN–x BLZ ceramic at x = 0.04. These results indicate that (1–x)K_(0.48)Na_(0.56)NbO_3–xBi_(0.5)Li_(0.5)ZrO_3 system is a promising candidate for high-temperature piezoelectric devices.

Na/K RATIOS DEPENDENCE OF PIEZOELECTRIC AND FERROELECTRIC PROPERTIES IN(K_(1-x)Na_(x))TNbO_(3)LEAD-FREE CERAMICS

In order to clarify the Na/K ratios dependence of piezoelectric properties,(K_(1-x)Na_(x))TNbO_(3)cer-amics were prepared by conventional solid-state sintering at a=0.4-0.6 with a smaller com-positional interval(0.02 mol).The results demonstrate that the Na/K ratios have obvious effecton piezoelectric and ferroelectric properties of(K_(1-x)Na_(x))NbO_(3)ceramics.Piezoelectric and fer-roelectric properties show the maximum(d_(33)147 pc/N,k_(p)=0.40,and P_(r)=24μC/cm^(2))at=0.54,which is not consistent with conventional viewpoint.The reasons should be attributedto the existence of a phase boundary at a=0.54 mol,which is similar to the morphotropic phaseboundary in Pb(Zr,Ti)O_(3)ceramics.

BiCoO3-doped （Ko.47sN ao.47sLio.os）（N bo.8Tao.2）03 lead-free piezoelectric ceramics

（1-x）（K0.47sNa0.475Li0.os）（Nb0.sTa0.2）O3-xBiCoO3 （KNLNT-BC） lead-free piezoelectric ceramics were prepared by the conventional solid-state sintering method. Effects of the BC content on the phase structure, microstructure and electrical properties of KNLNT-BC ceramics were investigated. XRD patterns reveal that all the ceramic samples are in the pure perovskite-type structure, and the phase structure changes from the tetragonal to pseudo-cubic phase with the increase of the BC content. After the substitution of BC, the grain size is significantly reduced and relaxer behaviors are induced. By adding a small amount of BC to KNLNT ceramics, piezoelectric properties are improved, while further addition of BC makes the piezoelectric properties deteriorate markedly. The optimized electrical properties atx= 0.005 are as follows： d33 = 194 pC/N, kp = 0.44.

Pr_(2)FeCrO_(6)掺杂对(Bi_(0.5)Na_(0.5))TiO_(3)–BaTiO_(3)无铅压电陶瓷结构和性能的影响

采用了传统陶瓷制备工艺制备了(1-x)[0.935(Bi_(0.5)Na_(0.5))TiO_(3)-0.065BaTiO_(3)]-x Pr_(2)FeCrO_(6)(简写为BNT-BT-x PFC)无铅压电陶瓷,并研究了PFC掺杂对该体系陶瓷相结构与电性能的影响。PFC的引入将BNT-BT陶瓷所具有的三方/四方共存结构转变为赝立方相结构。伴随着相结构的转变,BNT-BT陶瓷的铁电有序性被破坏,电致应变性能获得显著提升。材料在PFC掺杂量为0.6 mol%时获得最佳的电致应变性能:单向电致应变值达0.41%(60 kV/cm),约合压电应变常数d 33*(S_(max)/E_(max))为683 pm/V。同时,该组分陶瓷还具有良好的电致伸缩性能,其室温下的电致伸缩系数Q 33为0.023 m4/C2(60 kV/cm)。同时,Q 33在室温至120℃温度区间无明显下降,呈现出优异的温度稳定性,表明该体系陶瓷在驱动器领域具有良好的应用前景。