The tensile properties of Sn-9Zn-xAg-ySb;{(x, y) = (0.2, 0.6), (0.2, 0.8), (0.6, 0.2), (0.8, 0.2)} lead-free solders were investigated. All the test samples were annealed at 150°C for 1 hour. The tests are carrie...The tensile properties of Sn-9Zn-xAg-ySb;{(x, y) = (0.2, 0.6), (0.2, 0.8), (0.6, 0.2), (0.8, 0.2)} lead-free solders were investigated. All the test samples were annealed at 150°C for 1 hour. The tests are carried out at room temperature at the strain rate of 4.17 × 10<sup>-3</sup> s<sup>-1</sup>, 20.85 × 10<sup>-3</sup> s<sup>-1</sup>, and 208.5 × 10<sup>-3</sup> s<sup>-1</sup>. It is seen that the tensile strength increases and the ductility decrease with increasing the strain rate over the investigated range. From the strain rate change test results, the strain sensitivity values are found in the range of 0.0831 to 0.1455 due to the addition of different alloying elements.展开更多
A survey of solder ball production processes especially focusing on disturbed molten metal jet breakup process was made. Then the formation of capillary wave on tin melt jet in the way of rapid solidification was stud...A survey of solder ball production processes especially focusing on disturbed molten metal jet breakup process was made. Then the formation of capillary wave on tin melt jet in the way of rapid solidification was studied. A semi-empirical formula, which can be written as λ=C_ vib(σ/ρ) 1/3f -2/3 to predict the relationship between wavelength of capillary wave and frequency of imposed vibration was obtained. Sn-4.0Ag-0.5Cu lead free solder ball was successfully produced with tight distribution and good sphericity. The excited jet breakup process is promising for cost effectively producing solder ball.展开更多
Soldering experiments with Sn-3.5Ag-0.5Cu lead-free solder on Au/Ni/Cu pad were carried out by means of diode-laser and IR reflow soldering methods respectively.The influence of different heating methods as well as ou...Soldering experiments with Sn-3.5Ag-0.5Cu lead-free solder on Au/Ni/Cu pad were carried out by means of diode-laser and IR reflow soldering methods respectively.The influence of different heating methods as well as output power of diode-laser on shear force of micro-joints was studied and the relationship between the shear force and microstructures of micro-joints was analyzed.The results indicate that the formation of intermetallic compound Ag3Sn is the key factor to affect the shear force and the fine eutectic network structures of micro-joints as well as the dispersion morphology of fine compound Ag3Sn,in which eutectic network band is responsible for the improvement of the shear force of micro-joints soldered with Sn-Ag-Cu lead-free solder.With the increases of output power of diode-laser,the shear force and the microstructures change obviously.The eutectic network structures of micro-joints soldered with diode-laser soldering method are more homogeneous and the grains of Ag3Sn compounds are finer in the range of near optimal output power than those soldered with IR reflow soldering method,so the shear force is also higher than that using IR reflow soldering method.When the output power value of diode-laser is about 41.0 W,the shear force exhibits the highest value that is 70% higher than that using IR reflow soldering method.展开更多
This article explores tile effects of phosphorus addition on the wettability between Sn-9Zn solder alloy and Cu substrates, the oxidation behavior and the corrosion behavior of Sn-9Zn solder alloy. Spreading test was ...This article explores tile effects of phosphorus addition on the wettability between Sn-9Zn solder alloy and Cu substrates, the oxidation behavior and the corrosion behavior of Sn-9Zn solder alloy. Spreading test was used to characterize the wettability of Sn-9Zn-xP solder alloys to Cu substrates. The oxidation and corrosion behaviors of Sn- 9Zn-xP solder alloys were determined by means of weight gaining, and secondary ion mass spectrometry was used to analyze the oxygen content. The role and mechanism of P in the solder alloys were also discussed. It is found that the addition of P can significantly improve the wettability of the solder alloys. Incorporating P into Sn-9Zn solder alloy obviously decreases the oxygen content and enhances the oxidation and corrosion resistance. Microstructure observations show that an appropriate amount of P can greatly refine coarse rod-like Zn-rich phases in Sn-gZn solder alloy.展开更多
Sn-Ag alloy system has been regarded as one of the most promising lead-free solder to substitute conventional Sn- Pb eutectic solder. But the formation of bulk Ag3Sn intermetallic compounds (IMCs) during reflow and ...Sn-Ag alloy system has been regarded as one of the most promising lead-free solder to substitute conventional Sn- Pb eutectic solder. But the formation of bulk Ag3Sn intermetallic compounds (IMCs) during reflow and post heat treatment significantly influences the performance of the solder joints. With an effort to clarify its microstructural evolution as a function of slow cooling rates, the fraction of bulk IMCs within the slowly solidified Sn-4.0 wt pct Ag solder was investigated by standard metallographic and compared with that detected by thermal analysis. It was found that the bulk IMCs fraction determined by thermal analysis corresponds quite well with the microstructure observation results. In accordance with the conventional solidification theory, the lower the applied cooling rate, the fewer the amount of bulk Ag3Sn IMCs formed in Sn-4.0 wt pct Ag alloy. In addition, Vickers hardness measurement results indicated that the relative coarse eutectic Ag3Sn IMCs distributing in the lamellar eutectic structure favored the improvement of the mechanical performance.展开更多
An orthogonal method was used to evaluate the effects of Ga, Al, Ag, and Ce multi-additions on the wetting characteristics of Sn-9Zn lead-free solders by wetting balance method. The results show that the optimal loadi...An orthogonal method was used to evaluate the effects of Ga, Al, Ag, and Ce multi-additions on the wetting characteristics of Sn-9Zn lead-free solders by wetting balance method. The results show that the optimal loading of Ga, Al, Ag, and Ce was 0.2 wt.%, 0.002 wt.%, 0.25 wt.%, and 0.15 wt.%, respectively. Intermetallic compounds (IMCs) formed at the interface between Sn-9Zn-0.2Ga-0.002Al-0.25Ag- 0.15Ce solder and Cu substrate were investigated by scanning electron microscope (SEM) and energy dispersive spectroscopy (EDS) analysis. The SEM images illustrate that the IMCs can be divided into two portions from the substrate side to the solder side: a planar CusZns layer and an additional continuous scallop-like AgZn3 layer. The EDS analysis also shows that Ga segregates in the solder abutting upon the interface. X-ray photoelectron spectroscopy (XPS) and Auger electron spectroscopy (AES) of the surface components of Sn-9Zn-0.2Ga-0.002Al- 0.25Ag-0.15Ce solder indicate that Al aggregates at the surface in the form of Al203 protective fdm, which prevents the further oxidation of the solder surface. On the other hand, Ce aggregates at the subsurface, which may reduce the surface tension of the solder and improve the wettability in consequence.展开更多
A lead-free Sn-3.5Ag solder was prepared by rapid solidification technology. The high solidification rate, obtained by rapid cooling, promotes nucleation, and suppresses the growth of Ag3Sn intermetallic compounds (I...A lead-free Sn-3.5Ag solder was prepared by rapid solidification technology. The high solidification rate, obtained by rapid cooling, promotes nucleation, and suppresses the growth of Ag3Sn intermetallic compounds (IMCs) in Ag-rich zone, yielding fine Ag3Sn nanoparticulates with spherical morphology in the matrix of the solder. The large amount of tough homogeneously-dispersed IMCs helps to improve the surface area per unit volume and obstructs the dislocation lines passing through the solder, which fits with the dispersion-strengthening theory. Hence, the rapidly-solidified Sn-3.5Ag solder exhibits a higher rnicrohardness when compared with a slowly-solidified Sn-3.5Ag solder.展开更多
The eutectic Sn-9Zn alloy was doped with Ag (0 wt.%-1 wt.%) to form Sn-9Zn-xAg lead-free solder alloys. The effect of the addition of Ag on the microstructure and solderability of this alloy was investigated and int...The eutectic Sn-9Zn alloy was doped with Ag (0 wt.%-1 wt.%) to form Sn-9Zn-xAg lead-free solder alloys. The effect of the addition of Ag on the microstructure and solderability of this alloy was investigated and intermetallic compounds (IMCs) formed at the solder/Cu interface were also examined in this study. The results show that, due to the addition of Ag, the microstructure of the solder changes. When the quantity of Ag is lower than 0.3 wt.%, the needle-like Zn-rich phase decreases gradually. However, when the quantity of Ag is 0.5 wt.%-1 wt.%, Ag-Zn intermetallic compounds appear in the solder. In particular, adding 0.3 wt.% Ag improves the wetting behavior due to the better oxidation resistance of the Sn-9Zn solder. The addition of an excessive amount of Ag will deteriorate the wetting property because the gluti- nosity and fluidity of Sn-9Zn-(0.5, 1)Ag solder decrease. The results also indicate that the addition of Ag to the Sn-Zn solder leads to the precipitation of ε-AgZn3 from the liquid solder on preformed interracial intermetallics (CusZn8). The peripheral AgZn3, nodular on the Cu5Zn8 IMCs layer, is likely to be generated by a peritectic reaction L + γ-Ag5Zns→AgZn3 and the following crystallization of AgZn3.展开更多
Effect of different contents of La and Ga on the wettability and the mierostrueture of interface of Sn-8.9Zn- 2.7Bi trinary alloys was studied. The results show that different contents of La and Ga have significant ef...Effect of different contents of La and Ga on the wettability and the mierostrueture of interface of Sn-8.9Zn- 2.7Bi trinary alloys was studied. The results show that different contents of La and Ga have significant effect on the wettability of Sn-Zn-Bi based lead-free solder under the condition of both atmosphere and nitrogen. By adding suitable amount of Ga, Cu and La to Sn-Zn-Bi solder, a new lead-free solder Sn-8.9Zn-2.7Bi- 1.0Ga-0.5Cu-0.2La with better wettability was prepared, which has a wetting angle of 25.1° to Cu.展开更多
The microstructure and melting behavior of Sn-9Zn-2Cu (SZC) lead-free solder with 3 wt pct Bi and various amount of Ni additions were studied. The wetting properties and the interracial reaction of Sn-Zn-Cu with Cu ...The microstructure and melting behavior of Sn-9Zn-2Cu (SZC) lead-free solder with 3 wt pct Bi and various amount of Ni additions were studied. The wetting properties and the interracial reaction of Sn-Zn-Cu with Cu substrate were also examined. The results indicated that the addition of 3 wt pct Bi could decrease the melting point of the solder and Ni would refine the microstructure and the rod-shape Cu5Zn8 phase changed into square-shape (Cu, Ni)5Zn8 phase. The addition of Bi, Ni greatly improved the wettability of SZC solder. In addition, the interracial phase of the solders/Cu joint was typical planar Cu5Zn8 in SZC-3Bi-INi alloy.展开更多
In the present work, the effect of Ni doping on the microstructures and properties of Zn-20 Sn high temperature lead-free solder has been investigated. Interestingly,Ni was present as the form of Ni-Zn compounds in th...In the present work, the effect of Ni doping on the microstructures and properties of Zn-20 Sn high temperature lead-free solder has been investigated. Interestingly,Ni was present as the form of Ni-Zn compounds in the microstructure of Zn-20 Sn-xNi alloy.When the Ni-doping amount was 0.2~0.4 wt.%, the presence of δ phase was found, and when the doping amoun was 0.8 wt.%, the presence of γ phase was observed. With the increase of Ni content, the liquidus temperature increased but the solidus temperature did not change obviously. In addition, the microhardness and electrical resistivities of Zn-20 Sn-xNi solder increased gradually. And the spreading area and shear strength increased firstly but decreased afterwards. When the content of Ni was 0.4 wt.%, the spreading area and shear strength of solder reached to be maximum. After the addition of 0.4 wt.% Ni, the microstructure of the interfacial intermetallic compound(IMC) layer of the interface didn't change, but the total thickness of the IMC layer reduced. The δ-phase was embedded in the grain boundary of ε-Cu Zn5, which hindered the diffusion of atoms. The thickness of IMC layer at the interface reduced, which led to the improvement of the shear strength of the interface.展开更多
Solder balls, which are used in advanced electronics packages such as BGA (Ball Grid Array) and CSP (Chip Scale Package) to substitute the leads and realize the electrical and mechanical connections between substrate ...Solder balls, which are used in advanced electronics packages such as BGA (Ball Grid Array) and CSP (Chip Scale Package) to substitute the leads and realize the electrical and mechanical connections between substrate and chip,have severe specifications in diameter tolerance, roundness and surface quality, and therefore challenge the traditional technologies for fabrication of metallic particles and powders. The present work made a survey of perturbed molten metal jet break-up process, observed the formation and growth of capillary wave of tin-lead melt jet by way of rapid solidification, and on the basis of the above research, successfully obtained tin-lead eutectic and Sn-4.0Ag-0.5Cu lead free solder balls with tight distribution and good sphericity of particles through optimization of processing parameters, forming a solid base for cost effectively producing solder balls.展开更多
The Sn-9Zn lead-free solder alloy was prepared by conventional casting technique then cold-rolled into long sheets of 1 mm thickness and 3 mm width. It was annealed at 80, 120 and 160°C for 60 min to investigate ...The Sn-9Zn lead-free solder alloy was prepared by conventional casting technique then cold-rolled into long sheets of 1 mm thickness and 3 mm width. It was annealed at 80, 120 and 160°C for 60 min to investigate the effect of isochronal heat treatment on structure and mechanical properties of the cold rolled Sn-9Zn alloy. The results showed that, the crystallite size and lattice strain have opposite behavior with increasing annealing temperature due to recovery and recrystalization processes associated with the heat treatment process. Vickers micro-hardness number increases continuously from 155 to 180 MPa with increasing annealing temperature. Ultimate tensile strength (UTS) was also calculated. It was found that, it is equal to 61.4 MPa for the non annealed sample and slightly decreases to 60.5 and 58.2 MPa for samples annealed at 80 and 120°C, respectively. While, increases to 65.4 MPa for the sample annealed at 160°C. Also, ductility increases with increasing annealing temperature in opposite manor with the UTS. The new method for Micro-creep behavior as well as the creep rate calculated by this method has been characterized at room temperature.展开更多
In this paper,the phenomena of Mg_(2)Sn-induced Sn whisker growth were explored on the surfaces of Mg/Sn/Mg ultrasonic-assisted soldering joints after aging treatment.The in-situ observation and thermal analysis confi...In this paper,the phenomena of Mg_(2)Sn-induced Sn whisker growth were explored on the surfaces of Mg/Sn/Mg ultrasonic-assisted soldering joints after aging treatment.The in-situ observation and thermal analysis confirmed that the formation and the corrosion of Mg_(2)Sn nanoparticles were the dominant reason of Sn whisker growth.The Mg_(2)Sn accumulation at the grain boundaries would pin the dislocation slip and affect the continuity of whisker growth,and the boundary angle would thus play a decisive role in the growth shape of Sn whiskers due to the pining effect of Mg_(2)Sn.This study might be conducive to elucidating the growth behavior of Sn whiskers and provide the exploration strategy to further improve the bonding strength of Mg/Sn/Mg ultrasonic-assisted soldering joints.展开更多
The formation and growth behavior of intermetallic compound(IMC) layers after introducing an electroless Ni-W-P metallization into the Sn-3.0Ag-0.5Cu(SAC305) solder joint during soldering and aging were investigated. ...The formation and growth behavior of intermetallic compound(IMC) layers after introducing an electroless Ni-W-P metallization into the Sn-3.0Ag-0.5Cu(SAC305) solder joint during soldering and aging were investigated. The soldering was performed at 250 ℃ for 10 min, followed by air cooling and aging treatment at 150 ℃ up to 15 days. The results show that the scallop-like Cu_6Sn_5 IMC layer and planar-like Cu_3Sn formed between solder and Cu substrate during soldering and aging. The Ni_3P and(Ni,Cu)_3Sn_4 compounds were formed between electroless Ni-W-P layer and solder, and Cu substrate was not damaged and kept a smooth interface. When the isothermal aging treatment was applied, the total thickness of IMCs which formed at the SAC305/Cu and SAC305/Ni-W-P/Cu interface increased with increasing aging time. Kirkendall voids emerged at the Cu_3Sn and the Ni_3P layers, but the voids emerged at the Ni_3P layer in the form of crack. The amount of Kirkendall voids increased and the crack elongated with increasing aging time. The Cu_6Sn_5 and(Ni,Cu)_3Sn_4grains grew by merging adjacent grains. In the process of growth, the growing interfacial compounds filled the free space, and new columnar dendrite grain of(Ni,Cu)_3Sn_4 constantly generated during aging treatment. After 15 days aging, the Ni-W-P barrier layer was still remained, which indicated that the Ni-W-P layer can be a good barrier layer between the solder alloys and Cu substrate.展开更多
Emf technique was employed to determine indium activities in the liquid Ag-In-Pd alloys using galvanic cells with yttria-stabilised-zirconia as solid electrolyte according to the scheme: kanthal/rhenium, Ag-In-Pd, In...Emf technique was employed to determine indium activities in the liquid Ag-In-Pd alloys using galvanic cells with yttria-stabilised-zirconia as solid electrolyte according to the scheme: kanthal/rhenium, Ag-In-Pd, In2O3 | YSZ | Ni, NiO, Pt. Composition and temperature measurement ranges were limited, because of very steep liquidus surface; 35 compositions for Xpd up to 0.3 were investigated and at temperatures from near-liquidus up to 1700 K. High temperature experiments required special moly furnace to be constructed with unique automatic gas supply system for fumace winding protective atmosphere. Emf readings were taken and recorded by automatic data acquisition system. Linear dependence of emf on temperature was observed for all compositions investigated, and results were approximated by straight line equa- tions. Then In activities were calculated using well-known relations and taking into account correction for thermoelectric power between kanthal and platinum. Results are to be used along with other existing data to perform assessment of the ternary system under accord.展开更多
The wetting property of (Sn-9Zn)-2Cu (wt pct) on Ni substrate and the evolution of interracial microstructure in (Sn-9Zn)-2Cu/Ni joints during soldering as well as isothermal aging were studied. The wetting abil...The wetting property of (Sn-9Zn)-2Cu (wt pct) on Ni substrate and the evolution of interracial microstructure in (Sn-9Zn)-2Cu/Ni joints during soldering as well as isothermal aging were studied. The wetting ability of eutectic Sn-gZn solder on Ni substrate was markedly improved by adding 2 wt pct Cu into this solder alloy. Plate-like Cu5Zn8 intermetallic compounds (IMCs) were detected in (Sn-9Zn)-2Cu solder matrix. A continuous NisZn21 IMC layer was formed at (Sn-9Zn)-2Cu/Ni interface after soldering. This IMC layer kept its type and integrality even after aging at 170℃ for up to 1000 h. At the early aging stage (before 500 h), the IMC layer grew fast and its thickness followed a linear relationship with the square root of aging time. Thereafter, however, the thickness increased very slowly with longer aging time. When the joints were aged for 1000 h, a new IMC phase, (Cu,Ni)5Zn8, was found in the matrix near the interface. The formation of (Cu,Ni)5Zns phase can be attributed to the diffusion of Ni atoms into the solder matrix from the substrate.展开更多
文摘The tensile properties of Sn-9Zn-xAg-ySb;{(x, y) = (0.2, 0.6), (0.2, 0.8), (0.6, 0.2), (0.8, 0.2)} lead-free solders were investigated. All the test samples were annealed at 150°C for 1 hour. The tests are carried out at room temperature at the strain rate of 4.17 × 10<sup>-3</sup> s<sup>-1</sup>, 20.85 × 10<sup>-3</sup> s<sup>-1</sup>, and 208.5 × 10<sup>-3</sup> s<sup>-1</sup>. It is seen that the tensile strength increases and the ductility decrease with increasing the strain rate over the investigated range. From the strain rate change test results, the strain sensitivity values are found in the range of 0.0831 to 0.1455 due to the addition of different alloying elements.
文摘A survey of solder ball production processes especially focusing on disturbed molten metal jet breakup process was made. Then the formation of capillary wave on tin melt jet in the way of rapid solidification was studied. A semi-empirical formula, which can be written as λ=C_ vib(σ/ρ) 1/3f -2/3 to predict the relationship between wavelength of capillary wave and frequency of imposed vibration was obtained. Sn-4.0Ag-0.5Cu lead free solder ball was successfully produced with tight distribution and good sphericity. The excited jet breakup process is promising for cost effectively producing solder ball.
文摘Soldering experiments with Sn-3.5Ag-0.5Cu lead-free solder on Au/Ni/Cu pad were carried out by means of diode-laser and IR reflow soldering methods respectively.The influence of different heating methods as well as output power of diode-laser on shear force of micro-joints was studied and the relationship between the shear force and microstructures of micro-joints was analyzed.The results indicate that the formation of intermetallic compound Ag3Sn is the key factor to affect the shear force and the fine eutectic network structures of micro-joints as well as the dispersion morphology of fine compound Ag3Sn,in which eutectic network band is responsible for the improvement of the shear force of micro-joints soldered with Sn-Ag-Cu lead-free solder.With the increases of output power of diode-laser,the shear force and the microstructures change obviously.The eutectic network structures of micro-joints soldered with diode-laser soldering method are more homogeneous and the grains of Ag3Sn compounds are finer in the range of near optimal output power than those soldered with IR reflow soldering method,so the shear force is also higher than that using IR reflow soldering method.When the output power value of diode-laser is about 41.0 W,the shear force exhibits the highest value that is 70% higher than that using IR reflow soldering method.
基金supported by the National Natural Science Foundation of China(No.50904035)
文摘This article explores tile effects of phosphorus addition on the wettability between Sn-9Zn solder alloy and Cu substrates, the oxidation behavior and the corrosion behavior of Sn-9Zn solder alloy. Spreading test was used to characterize the wettability of Sn-9Zn-xP solder alloys to Cu substrates. The oxidation and corrosion behaviors of Sn- 9Zn-xP solder alloys were determined by means of weight gaining, and secondary ion mass spectrometry was used to analyze the oxygen content. The role and mechanism of P in the solder alloys were also discussed. It is found that the addition of P can significantly improve the wettability of the solder alloys. Incorporating P into Sn-9Zn solder alloy obviously decreases the oxygen content and enhances the oxidation and corrosion resistance. Microstructure observations show that an appropriate amount of P can greatly refine coarse rod-like Zn-rich phases in Sn-gZn solder alloy.
基金the National Natural Science Foundation of China(No.50401033)the Foundation for the Author of National Excellent Doctoral Dissertation of China(No.200335)+1 种基金the Natural Science Foundation of Tianjin City(No.033608811)Scientific Reseaxch Foundation for the Returned 0verseas Chinese Scholaxs,State Education Ministry,for grant and financial support.
文摘Sn-Ag alloy system has been regarded as one of the most promising lead-free solder to substitute conventional Sn- Pb eutectic solder. But the formation of bulk Ag3Sn intermetallic compounds (IMCs) during reflow and post heat treatment significantly influences the performance of the solder joints. With an effort to clarify its microstructural evolution as a function of slow cooling rates, the fraction of bulk IMCs within the slowly solidified Sn-4.0 wt pct Ag solder was investigated by standard metallographic and compared with that detected by thermal analysis. It was found that the bulk IMCs fraction determined by thermal analysis corresponds quite well with the microstructure observation results. In accordance with the conventional solidification theory, the lower the applied cooling rate, the fewer the amount of bulk Ag3Sn IMCs formed in Sn-4.0 wt pct Ag alloy. In addition, Vickers hardness measurement results indicated that the relative coarse eutectic Ag3Sn IMCs distributing in the lamellar eutectic structure favored the improvement of the mechanical performance.
文摘An orthogonal method was used to evaluate the effects of Ga, Al, Ag, and Ce multi-additions on the wetting characteristics of Sn-9Zn lead-free solders by wetting balance method. The results show that the optimal loading of Ga, Al, Ag, and Ce was 0.2 wt.%, 0.002 wt.%, 0.25 wt.%, and 0.15 wt.%, respectively. Intermetallic compounds (IMCs) formed at the interface between Sn-9Zn-0.2Ga-0.002Al-0.25Ag- 0.15Ce solder and Cu substrate were investigated by scanning electron microscope (SEM) and energy dispersive spectroscopy (EDS) analysis. The SEM images illustrate that the IMCs can be divided into two portions from the substrate side to the solder side: a planar CusZns layer and an additional continuous scallop-like AgZn3 layer. The EDS analysis also shows that Ga segregates in the solder abutting upon the interface. X-ray photoelectron spectroscopy (XPS) and Auger electron spectroscopy (AES) of the surface components of Sn-9Zn-0.2Ga-0.002Al- 0.25Ag-0.15Ce solder indicate that Al aggregates at the surface in the form of Al203 protective fdm, which prevents the further oxidation of the solder surface. On the other hand, Ce aggregates at the subsurface, which may reduce the surface tension of the solder and improve the wettability in consequence.
基金This work was financially supported by the National Natural Science Foundation of China (No. 50401003), the Natural Science Foundation of Tianjin City (No. 033608811) and Fok Ying Tong Education Foundation (No. 104015).
文摘A lead-free Sn-3.5Ag solder was prepared by rapid solidification technology. The high solidification rate, obtained by rapid cooling, promotes nucleation, and suppresses the growth of Ag3Sn intermetallic compounds (IMCs) in Ag-rich zone, yielding fine Ag3Sn nanoparticulates with spherical morphology in the matrix of the solder. The large amount of tough homogeneously-dispersed IMCs helps to improve the surface area per unit volume and obstructs the dislocation lines passing through the solder, which fits with the dispersion-strengthening theory. Hence, the rapidly-solidified Sn-3.5Ag solder exhibits a higher rnicrohardness when compared with a slowly-solidified Sn-3.5Ag solder.
基金supported by the Jiangsu Six-kind Skilled Personnel Project,China (No.06-E-020)
文摘The eutectic Sn-9Zn alloy was doped with Ag (0 wt.%-1 wt.%) to form Sn-9Zn-xAg lead-free solder alloys. The effect of the addition of Ag on the microstructure and solderability of this alloy was investigated and intermetallic compounds (IMCs) formed at the solder/Cu interface were also examined in this study. The results show that, due to the addition of Ag, the microstructure of the solder changes. When the quantity of Ag is lower than 0.3 wt.%, the needle-like Zn-rich phase decreases gradually. However, when the quantity of Ag is 0.5 wt.%-1 wt.%, Ag-Zn intermetallic compounds appear in the solder. In particular, adding 0.3 wt.% Ag improves the wetting behavior due to the better oxidation resistance of the Sn-9Zn solder. The addition of an excessive amount of Ag will deteriorate the wetting property because the gluti- nosity and fluidity of Sn-9Zn-(0.5, 1)Ag solder decrease. The results also indicate that the addition of Ag to the Sn-Zn solder leads to the precipitation of ε-AgZn3 from the liquid solder on preformed interracial intermetallics (CusZn8). The peripheral AgZn3, nodular on the Cu5Zn8 IMCs layer, is likely to be generated by a peritectic reaction L + γ-Ag5Zns→AgZn3 and the following crystallization of AgZn3.
文摘Effect of different contents of La and Ga on the wettability and the mierostrueture of interface of Sn-8.9Zn- 2.7Bi trinary alloys was studied. The results show that different contents of La and Ga have significant effect on the wettability of Sn-Zn-Bi based lead-free solder under the condition of both atmosphere and nitrogen. By adding suitable amount of Ga, Cu and La to Sn-Zn-Bi solder, a new lead-free solder Sn-8.9Zn-2.7Bi- 1.0Ga-0.5Cu-0.2La with better wettability was prepared, which has a wetting angle of 25.1° to Cu.
文摘The microstructure and melting behavior of Sn-9Zn-2Cu (SZC) lead-free solder with 3 wt pct Bi and various amount of Ni additions were studied. The wetting properties and the interracial reaction of Sn-Zn-Cu with Cu substrate were also examined. The results indicated that the addition of 3 wt pct Bi could decrease the melting point of the solder and Ni would refine the microstructure and the rod-shape Cu5Zn8 phase changed into square-shape (Cu, Ni)5Zn8 phase. The addition of Bi, Ni greatly improved the wettability of SZC solder. In addition, the interracial phase of the solders/Cu joint was typical planar Cu5Zn8 in SZC-3Bi-INi alloy.
基金supported by the scientific and technological project in Fujian Province(2015H0008)
文摘In the present work, the effect of Ni doping on the microstructures and properties of Zn-20 Sn high temperature lead-free solder has been investigated. Interestingly,Ni was present as the form of Ni-Zn compounds in the microstructure of Zn-20 Sn-xNi alloy.When the Ni-doping amount was 0.2~0.4 wt.%, the presence of δ phase was found, and when the doping amoun was 0.8 wt.%, the presence of γ phase was observed. With the increase of Ni content, the liquidus temperature increased but the solidus temperature did not change obviously. In addition, the microhardness and electrical resistivities of Zn-20 Sn-xNi solder increased gradually. And the spreading area and shear strength increased firstly but decreased afterwards. When the content of Ni was 0.4 wt.%, the spreading area and shear strength of solder reached to be maximum. After the addition of 0.4 wt.% Ni, the microstructure of the interfacial intermetallic compound(IMC) layer of the interface didn't change, but the total thickness of the IMC layer reduced. The δ-phase was embedded in the grain boundary of ε-Cu Zn5, which hindered the diffusion of atoms. The thickness of IMC layer at the interface reduced, which led to the improvement of the shear strength of the interface.
文摘Solder balls, which are used in advanced electronics packages such as BGA (Ball Grid Array) and CSP (Chip Scale Package) to substitute the leads and realize the electrical and mechanical connections between substrate and chip,have severe specifications in diameter tolerance, roundness and surface quality, and therefore challenge the traditional technologies for fabrication of metallic particles and powders. The present work made a survey of perturbed molten metal jet break-up process, observed the formation and growth of capillary wave of tin-lead melt jet by way of rapid solidification, and on the basis of the above research, successfully obtained tin-lead eutectic and Sn-4.0Ag-0.5Cu lead free solder balls with tight distribution and good sphericity of particles through optimization of processing parameters, forming a solid base for cost effectively producing solder balls.
基金This work was financially supported by the National Natural Science Foundation of China (No. 50401003), Fok Ying Tong Education Foundation (No. 104015), and the Natural Science Foundation of Tianjin City (No. 033608811).
文摘The Sn-9Zn lead-free solder alloy was prepared by conventional casting technique then cold-rolled into long sheets of 1 mm thickness and 3 mm width. It was annealed at 80, 120 and 160°C for 60 min to investigate the effect of isochronal heat treatment on structure and mechanical properties of the cold rolled Sn-9Zn alloy. The results showed that, the crystallite size and lattice strain have opposite behavior with increasing annealing temperature due to recovery and recrystalization processes associated with the heat treatment process. Vickers micro-hardness number increases continuously from 155 to 180 MPa with increasing annealing temperature. Ultimate tensile strength (UTS) was also calculated. It was found that, it is equal to 61.4 MPa for the non annealed sample and slightly decreases to 60.5 and 58.2 MPa for samples annealed at 80 and 120°C, respectively. While, increases to 65.4 MPa for the sample annealed at 160°C. Also, ductility increases with increasing annealing temperature in opposite manor with the UTS. The new method for Micro-creep behavior as well as the creep rate calculated by this method has been characterized at room temperature.
基金supported by Science and Technology Planning Project of Shenzhen (Grant No. JCYJ201908 09161213154)Xiamen Youth Innovation Fund Project (Grant No. 3502Z20206026)Academy-level Project of Xiamen City University (Grant No.KYKJ2019-4)。
文摘In this paper,the phenomena of Mg_(2)Sn-induced Sn whisker growth were explored on the surfaces of Mg/Sn/Mg ultrasonic-assisted soldering joints after aging treatment.The in-situ observation and thermal analysis confirmed that the formation and the corrosion of Mg_(2)Sn nanoparticles were the dominant reason of Sn whisker growth.The Mg_(2)Sn accumulation at the grain boundaries would pin the dislocation slip and affect the continuity of whisker growth,and the boundary angle would thus play a decisive role in the growth shape of Sn whiskers due to the pining effect of Mg_(2)Sn.This study might be conducive to elucidating the growth behavior of Sn whiskers and provide the exploration strategy to further improve the bonding strength of Mg/Sn/Mg ultrasonic-assisted soldering joints.
基金Funded by National Natural Science Foundation of China(Nos.51465039,51665038)Natural Science Foundation of Jiangxi Province(Nos.20151BAB206041,20161BAB206122)the State Key Laboratory of Solidification Processing in NWPU(No.SKLSP201508)
文摘The formation and growth behavior of intermetallic compound(IMC) layers after introducing an electroless Ni-W-P metallization into the Sn-3.0Ag-0.5Cu(SAC305) solder joint during soldering and aging were investigated. The soldering was performed at 250 ℃ for 10 min, followed by air cooling and aging treatment at 150 ℃ up to 15 days. The results show that the scallop-like Cu_6Sn_5 IMC layer and planar-like Cu_3Sn formed between solder and Cu substrate during soldering and aging. The Ni_3P and(Ni,Cu)_3Sn_4 compounds were formed between electroless Ni-W-P layer and solder, and Cu substrate was not damaged and kept a smooth interface. When the isothermal aging treatment was applied, the total thickness of IMCs which formed at the SAC305/Cu and SAC305/Ni-W-P/Cu interface increased with increasing aging time. Kirkendall voids emerged at the Cu_3Sn and the Ni_3P layers, but the voids emerged at the Ni_3P layer in the form of crack. The amount of Kirkendall voids increased and the crack elongated with increasing aging time. The Cu_6Sn_5 and(Ni,Cu)_3Sn_4grains grew by merging adjacent grains. In the process of growth, the growing interfacial compounds filled the free space, and new columnar dendrite grain of(Ni,Cu)_3Sn_4 constantly generated during aging treatment. After 15 days aging, the Ni-W-P barrier layer was still remained, which indicated that the Ni-W-P layer can be a good barrier layer between the solder alloys and Cu substrate.
基金This work contributes to Group Project No. 4, within the frame of European Project COST "Action 531: Lead-free sol-ders". Financial support from Polish State Committee for Scientific Research under grant No. 62/E - 88/SPB/COST/ T08//DZ 459/2003-2006 is gratefully acknowledged.
文摘Emf technique was employed to determine indium activities in the liquid Ag-In-Pd alloys using galvanic cells with yttria-stabilised-zirconia as solid electrolyte according to the scheme: kanthal/rhenium, Ag-In-Pd, In2O3 | YSZ | Ni, NiO, Pt. Composition and temperature measurement ranges were limited, because of very steep liquidus surface; 35 compositions for Xpd up to 0.3 were investigated and at temperatures from near-liquidus up to 1700 K. High temperature experiments required special moly furnace to be constructed with unique automatic gas supply system for fumace winding protective atmosphere. Emf readings were taken and recorded by automatic data acquisition system. Linear dependence of emf on temperature was observed for all compositions investigated, and results were approximated by straight line equa- tions. Then In activities were calculated using well-known relations and taking into account correction for thermoelectric power between kanthal and platinum. Results are to be used along with other existing data to perform assessment of the ternary system under accord.
基金supported by the National Key Project of ScientificTechnical Supporting Programs during the 11th Five-year Plan (No. 2006BAE03B02-2)NSFC Key Program (No. U0734006)
文摘The wetting property of (Sn-9Zn)-2Cu (wt pct) on Ni substrate and the evolution of interracial microstructure in (Sn-9Zn)-2Cu/Ni joints during soldering as well as isothermal aging were studied. The wetting ability of eutectic Sn-gZn solder on Ni substrate was markedly improved by adding 2 wt pct Cu into this solder alloy. Plate-like Cu5Zn8 intermetallic compounds (IMCs) were detected in (Sn-9Zn)-2Cu solder matrix. A continuous NisZn21 IMC layer was formed at (Sn-9Zn)-2Cu/Ni interface after soldering. This IMC layer kept its type and integrality even after aging at 170℃ for up to 1000 h. At the early aging stage (before 500 h), the IMC layer grew fast and its thickness followed a linear relationship with the square root of aging time. Thereafter, however, the thickness increased very slowly with longer aging time. When the joints were aged for 1000 h, a new IMC phase, (Cu,Ni)5Zn8, was found in the matrix near the interface. The formation of (Cu,Ni)5Zns phase can be attributed to the diffusion of Ni atoms into the solder matrix from the substrate.