The crystallization behavior and kinetics of CaO-MgO-Al2O3 SiO2（CMAS） glass with the Fe2O3 content ranging from zero to 5%were investigated by differential scanning calorimetry（DSC）.The structure and phase analyse...The crystallization behavior and kinetics of CaO-MgO-Al2O3 SiO2（CMAS） glass with the Fe2O3 content ranging from zero to 5%were investigated by differential scanning calorimetry（DSC）.The structure and phase analyses were made by Fourier transform infrared spectroscopy（FT-IR） and X-ray diffraction（XRD）.The experiment results show that the endothermic peak temperature about 760℃ is associated with transition and the exothermic peak temperature about 1000℃ is associated with crystallization.The crystallization peak temperature decreases with increasing the Fe203 content.The crystallization mechanism is changed from two-dimensional crystallization to one-dimensional growth,and the intensity of diopside peaks becomes stronger gradually.There is a saltation for the crystallization temperature with the addition of 0.5%Fe2O3 due to the decomposition of Fe2O3.Si-O-Si,O-Si-O and T-O-T（T=Si,Fe,Al） linkages are observed in Fe2O3-CaO-MgO-Al2O3-SiO2 glass.展开更多
X-ray powder diffraction and Fourier transform infrared spectroscopy were applied for characterization of Li2O-Al2O3-SiO2 glass-ceramic powders doped with Eu2O3,Gd2O3 and Er2O3,respectively,in the conditions of differ...X-ray powder diffraction and Fourier transform infrared spectroscopy were applied for characterization of Li2O-Al2O3-SiO2 glass-ceramic powders doped with Eu2O3,Gd2O3 and Er2O3,respectively,in the conditions of different heat-treatment temperatures and with various amounts.The powders were derived from the polyacrylamide gel method.The results show that,the wet gels prepared by polyacrylamide perform a unique crystallization behavior in the process of drying,comparing with some customary preparation such as melt processing.The main crystal phase and crystallization sequence of Li2O-Al2O3-SiO2 micro-powders have no distinct with addition of Eu2O3,Gd2O3 or Er2O3,while the crystallization temperature of the β-spodumene decreased and the amount of the β-spodumene increased.展开更多
Li2O-Al2O3-SiO2 glass prepared from traditional melting and cooling process was investigated.The surface characteristic of LAS glass was studied by simulating tin bath with different temperature and time,and the effec...Li2O-Al2O3-SiO2 glass prepared from traditional melting and cooling process was investigated.The surface characteristic of LAS glass was studied by simulating tin bath with different temperature and time,and the effect of surface tension/viscosity ratio on flatting time was analyzed.The results demonstrated that LAS glass can polish effectively when polishing at 1 300 ℃ for 8 min,and the optimum flatting and polishing temperature was 1 250-1 300 ℃.展开更多
Through measuring the coefficient of linear expansion, the structure and properties of the Li2O-Al2O3-SiO2 low expansion glass ceramics containing B2O3 are studied by JR and XRD. It is shoutn that the IR method is eff...Through measuring the coefficient of linear expansion, the structure and properties of the Li2O-Al2O3-SiO2 low expansion glass ceramics containing B2O3 are studied by JR and XRD. It is shoutn that the IR method is efficient in the study of the glass-ceramics structure. There is a " Boron abnormality" in the system which has an important influence on the properties of the glass-ceramics.展开更多
基金Projects(51264023,51364020,U1202271)supported by the National Natural Science Foundation of ChinaProject(IRT1250)supported by the Program for Innovative Research Team in University of Ministry of Education of ChinaProject(2014HA003)supported by the Science and Technology Leading Talent of Yunnan Province,China
文摘The crystallization behavior and kinetics of CaO-MgO-Al2O3 SiO2（CMAS） glass with the Fe2O3 content ranging from zero to 5%were investigated by differential scanning calorimetry（DSC）.The structure and phase analyses were made by Fourier transform infrared spectroscopy（FT-IR） and X-ray diffraction（XRD）.The experiment results show that the endothermic peak temperature about 760℃ is associated with transition and the exothermic peak temperature about 1000℃ is associated with crystallization.The crystallization peak temperature decreases with increasing the Fe203 content.The crystallization mechanism is changed from two-dimensional crystallization to one-dimensional growth,and the intensity of diopside peaks becomes stronger gradually.There is a saltation for the crystallization temperature with the addition of 0.5%Fe2O3 due to the decomposition of Fe2O3.Si-O-Si,O-Si-O and T-O-T（T=Si,Fe,Al） linkages are observed in Fe2O3-CaO-MgO-Al2O3-SiO2 glass.
文摘X-ray powder diffraction and Fourier transform infrared spectroscopy were applied for characterization of Li2O-Al2O3-SiO2 glass-ceramic powders doped with Eu2O3,Gd2O3 and Er2O3,respectively,in the conditions of different heat-treatment temperatures and with various amounts.The powders were derived from the polyacrylamide gel method.The results show that,the wet gels prepared by polyacrylamide perform a unique crystallization behavior in the process of drying,comparing with some customary preparation such as melt processing.The main crystal phase and crystallization sequence of Li2O-Al2O3-SiO2 micro-powders have no distinct with addition of Eu2O3,Gd2O3 or Er2O3,while the crystallization temperature of the β-spodumene decreased and the amount of the β-spodumene increased.
基金Funded partly by the National Key Technology R&D Program in the 11th Five Year Plan of China(No. 2006BAJ02B00)Natural Science Foundation of Hubei Province (No.2008CDA037)
文摘Li2O-Al2O3-SiO2 glass prepared from traditional melting and cooling process was investigated.The surface characteristic of LAS glass was studied by simulating tin bath with different temperature and time,and the effect of surface tension/viscosity ratio on flatting time was analyzed.The results demonstrated that LAS glass can polish effectively when polishing at 1 300 ℃ for 8 min,and the optimum flatting and polishing temperature was 1 250-1 300 ℃.
文摘Through measuring the coefficient of linear expansion, the structure and properties of the Li2O-Al2O3-SiO2 low expansion glass ceramics containing B2O3 are studied by JR and XRD. It is shoutn that the IR method is efficient in the study of the glass-ceramics structure. There is a " Boron abnormality" in the system which has an important influence on the properties of the glass-ceramics.