A new kind of vanadium bronze with rich lithium (Li_5V_5O_(15))was prepared from Li_2CO_3 and V_2O_5 at 680℃ for 24 hrs. The charge and discharge curves of bronze electrode were determined in organic electrolyte. One...A new kind of vanadium bronze with rich lithium (Li_5V_5O_(15))was prepared from Li_2CO_3 and V_2O_5 at 680℃ for 24 hrs. The charge and discharge curves of bronze electrode were determined in organic electrolyte. One mole of this material could be incorporated up to 4 mole lithium at 0.2mA/cm^2 and 1.0V cut-off voltage, corresponding capacity about 340Ah/kg. Compared with the cell of Li/Li_(1+x)V_3O_5 the cell of Li/new bronze had higher capacity, smoother discberge curve, but lower plateau voltage (about 1.8V). The cycling behaviour of this material was good. The electrode insertion reaction was controlled by the lithium diffusion process in the bronze. This new bronze could be used for low voltage rechargeable lithium battery.展开更多
基金This project is supported by The National Natural Science Foundation of China
文摘A new kind of vanadium bronze with rich lithium (Li_5V_5O_(15))was prepared from Li_2CO_3 and V_2O_5 at 680℃ for 24 hrs. The charge and discharge curves of bronze electrode were determined in organic electrolyte. One mole of this material could be incorporated up to 4 mole lithium at 0.2mA/cm^2 and 1.0V cut-off voltage, corresponding capacity about 340Ah/kg. Compared with the cell of Li/Li_(1+x)V_3O_5 the cell of Li/new bronze had higher capacity, smoother discberge curve, but lower plateau voltage (about 1.8V). The cycling behaviour of this material was good. The electrode insertion reaction was controlled by the lithium diffusion process in the bronze. This new bronze could be used for low voltage rechargeable lithium battery.