Layered cathode material LiCo1/3Ni1/3Mn1/3O2 was synthesized by Pechini process, and investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM) and galvanostatic charge/discharge cycling. The sampl...Layered cathode material LiCo1/3Ni1/3Mn1/3O2 was synthesized by Pechini process, and investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM) and galvanostatic charge/discharge cycling. The sample is well-crystallized and has a phase-pure a-NaFeO2 structure. The particle sizes are uniform, and distributed in the range of 20-200 nm. The initial discharge capacity of the Li/LiCo1/3Ni1/3Mn1/3O2 cell was about 149 mAh·g-1 when it was cycled at a voltage range of 4.5-2.3 V with a specific current of 0.25 mA. The result is better in comparison with solid-state solution method. The synthetic procedure was discussed. Three major reactions: chelation, esterification, and polymerization successively occurred.展开更多
采用改进的碳酸盐共沉淀与高温固相法相结合的方法制备出了高倍率性能的锂离子电池正极材料Li[Ni1/3Co1/3Mn1/3]O2,通过X射线衍射(XRD)、扫描电镜(SEM)、循环伏安扫描(CV)、电化学阻抗谱(EIS)和电化学性能测试等手段对材料进行表征.结...采用改进的碳酸盐共沉淀与高温固相法相结合的方法制备出了高倍率性能的锂离子电池正极材料Li[Ni1/3Co1/3Mn1/3]O2,通过X射线衍射(XRD)、扫描电镜(SEM)、循环伏安扫描(CV)、电化学阻抗谱(EIS)和电化学性能测试等手段对材料进行表征.结果表明,该方法制备的材料具有良好的α-Na Fe O2型层状结构(R3m(166)),一次粒径平均大小为157 nm,二次颗粒成球形.同传统碳酸盐制备得到的材料相比,该材料具备良好的倍率性能和循环性能,在2.7-4.3 V电压范围内,0.1C(1.0C=180 m A?g-1)倍率下,首次放电比容量为156.4m Ah?g-1,库仑效率为81.9%.在较高倍率下,即0.5C、5.0C和20C时,其放电比容量分别为136.9、111.3、81.3m Ah?g-1.在1C倍率下100次循环容量保持率为92.9%,高于传统共沉淀法得到的材料(87.0%).展开更多
文摘Layered cathode material LiCo1/3Ni1/3Mn1/3O2 was synthesized by Pechini process, and investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM) and galvanostatic charge/discharge cycling. The sample is well-crystallized and has a phase-pure a-NaFeO2 structure. The particle sizes are uniform, and distributed in the range of 20-200 nm. The initial discharge capacity of the Li/LiCo1/3Ni1/3Mn1/3O2 cell was about 149 mAh·g-1 when it was cycled at a voltage range of 4.5-2.3 V with a specific current of 0.25 mA. The result is better in comparison with solid-state solution method. The synthetic procedure was discussed. Three major reactions: chelation, esterification, and polymerization successively occurred.
文摘采用改进的碳酸盐共沉淀与高温固相法相结合的方法制备出了高倍率性能的锂离子电池正极材料Li[Ni1/3Co1/3Mn1/3]O2,通过X射线衍射(XRD)、扫描电镜(SEM)、循环伏安扫描(CV)、电化学阻抗谱(EIS)和电化学性能测试等手段对材料进行表征.结果表明,该方法制备的材料具有良好的α-Na Fe O2型层状结构(R3m(166)),一次粒径平均大小为157 nm,二次颗粒成球形.同传统碳酸盐制备得到的材料相比,该材料具备良好的倍率性能和循环性能,在2.7-4.3 V电压范围内,0.1C(1.0C=180 m A?g-1)倍率下,首次放电比容量为156.4m Ah?g-1,库仑效率为81.9%.在较高倍率下,即0.5C、5.0C和20C时,其放电比容量分别为136.9、111.3、81.3m Ah?g-1.在1C倍率下100次循环容量保持率为92.9%,高于传统共沉淀法得到的材料(87.0%).