Nonvolatile photorefractive properties in triply doped stoichiometric Mg:Fe:Mn:LiTaO_3 crystals

We have grown triply doped Mg:Fe:Mn:LiTaO3 crystals with near stoichiometry using the top seeded solution growth technique. The defect structure was investigated by infrared absorption spectra and Curie temperature. Using a blue laser as the source, excellent photorefractive properties were obtained. Nonvolatile holographic storage properties were investigated using the dual wavelength technique. We got a very high fixed diffraction efficiency and nonvolatile holographic storage sensitivity. The blue light has more than enough energy to excite holes of deep(Mn) and shallow(Fe) trap centers with the same phase, which enhance dramatically the blue photorefractive properties and the nonvolatile holographic storage. Mg2+ ion is no longer damage resistant at blue laser, but enhances photorefractive characteristics.

声表面波器件用Y36°切LiTaO_3晶片表面加工研究

采用双晶摆动曲线法测量了钽酸锂晶片的加工损伤层 ,其平均值在 2 6 .2～ 5 2 .8μm之间 ;根据工序要求 ,选取加工余量为 15 0 μm左右 ,采用天然石榴石研磨粉 ,适当的磨料浓度、添加悬浮剂、分散剂以避免产生缺陷 ,并采用化学机械抛光法 ,可获得较高加工质量的声表面波器件用Y36°切LiTaO3

LiTaO_3晶体在声表器件中的应用

随着移动通信市场的迅猛发展 ,对声表面波 (SAW )器件特别是射频低损耗滤波器的需求越来越大。而在制作这些SAW器件中 ,LiTaO3 晶体以其优良的温度稳定性和较高的耦合系数特性受到大多数声表器件制造商的青睐。LiTaO3 晶体最早是利用其瑞利波特性 ,切向为X切Y1 1 2°传 ,它适合制作要求稳定性好、带宽中等的滤波器。因此它大量用于彩电中频滤波器 ,其年用量上千万只。LiTaO3 在Y36°切或Y42°切 X传方向具有优良的漏表面波 (LSAW )特性 ,其耦合系数为4.7% ,温度系数为 - 32× 1 0 -6/℃。在常见的低损耗类型中 ,如镜象阻抗连接换能器或交错对插换能器 (IIC)构成的滤波器、双模谐振 (DMS)滤波器、阻抗元滤波器 (IEF)中 ,采用LiTaO3 均有成熟的设计和器件。富士通在 1 994年就已研制出中心频率 2 40 0MHz ,损耗 2dB的高频低损耗滤波器。我国个人移动通信是全球最大的市场之一 ,而其中的射频双工滤波器正是由Y36° X制作。据三洋公司预计全球RFSAW滤波器用量将从 1 997年的 2 .3亿只增长到 1 999年的 4.3亿只。因此 ,大力发展大尺寸高质量LiTaO3 晶体以满足GSM手机国产化用滤波器已成共识。

660nm激光抽运LiTaO_3∶Cr^(3+)晶体的激光运转

利用 6 6 0nm的巨脉冲激光抽运一种新的激光晶体LiTaO3∶Cr3+ ,获得了 1mJ的 90 1 6nm巨脉冲激光输出。经BBO晶体倍频获得了 45 0 8nm的蓝绿激光输出。