Carbon was coated on the surface of LiMnSiOto improve the electrochemical performance as cathode materials, which were synthesized by the solution method followed by heat treatment at 700 ℃ and the solid-state method...Carbon was coated on the surface of LiMnSiOto improve the electrochemical performance as cathode materials, which were synthesized by the solution method followed by heat treatment at 700 ℃ and the solid-state method followed by heat treatment at 950 ℃. It is shown that the cycling performance is greatly enhanced by carbon coating, compared with the pristine LiMnSiOcathode obtained by the solution method. The initial discharge capacity of LiMnSiO/C nanocomposite is 280.9 m Ah/g at 0.05 C with the carbon content of 33.3 wt%. The reasons for the improved electrochemical performance are smaller grain size and higher electronic conductivity due to the carbon coating. The LiMnSiO/C cathode material obtained by the solid-state method exhibits poor cycling performance, the initial discharge capacity is less than 25 m Ah/g.展开更多
以五氧化二钒干凝胶、碳酸锰、磷酸二氢铵、碳酸锂、乙炔黑为原料,采用固相法在相对较低的温度条件下合成了x Li Mn PO4·y Li3V2(PO4)3锂离子电池复合正极材料。采用X射线衍射(XRD)、扫描电镜(SEM)对其晶体结构和表面形貌进行表征...以五氧化二钒干凝胶、碳酸锰、磷酸二氢铵、碳酸锂、乙炔黑为原料,采用固相法在相对较低的温度条件下合成了x Li Mn PO4·y Li3V2(PO4)3锂离子电池复合正极材料。采用X射线衍射(XRD)、扫描电镜(SEM)对其晶体结构和表面形貌进行表征。结果表明,750℃下烧结15 h合成的3Li Mn PO4·Li3V2(PO4)3为结晶良好的两相结构,颗粒粒径较小且分布比较均匀,其在室温、0.2 C倍率下首次充放电容量分别为144.8 m Ah/g和139.8 m Ah/g,循环50次后容量为130.5 m Ah/g。展开更多
通过溶胶-凝胶法制备了Li_2FeSiO_4@C/CNTs(LFS@C/CNTs)纳米复合材料,其中三嵌段共聚物P123用作结构导向剂和碳源,碳纳米管作为导电线提高材料的导电性。LFS@C/CNTs不仅具有海绵状纳米孔,能够与电解液充分接触改善锂离子的传输路径,同...通过溶胶-凝胶法制备了Li_2FeSiO_4@C/CNTs(LFS@C/CNTs)纳米复合材料,其中三嵌段共聚物P123用作结构导向剂和碳源,碳纳米管作为导电线提高材料的导电性。LFS@C/CNTs不仅具有海绵状纳米孔,能够与电解液充分接触改善锂离子的传输路径,同时由非晶碳和碳纳米管构成的三维桥联导电网络利于电子的快速传递,提高了材料大电流充放电能力和循环稳定性。复合后的LFS@C/CNTs的高倍率性能相比LFS@C明显提高,当CNTs的掺量为4%,电压窗口为1.5~4.5 V,0.1C电流密度下放电比容量为182 m Ah·g^(-1)。在10C经70次循环后该材料的放电比容量能保持在117 m Ah·g^(-1),是LFS@C放电比容量(55 m Ah·g^(-1))的两倍。展开更多
基金Funded by the National Natural Science Foundation of China(No.51372136)Shenzhen Basic Research Project(No.CYJ20130402145002372)
文摘Carbon was coated on the surface of LiMnSiOto improve the electrochemical performance as cathode materials, which were synthesized by the solution method followed by heat treatment at 700 ℃ and the solid-state method followed by heat treatment at 950 ℃. It is shown that the cycling performance is greatly enhanced by carbon coating, compared with the pristine LiMnSiOcathode obtained by the solution method. The initial discharge capacity of LiMnSiO/C nanocomposite is 280.9 m Ah/g at 0.05 C with the carbon content of 33.3 wt%. The reasons for the improved electrochemical performance are smaller grain size and higher electronic conductivity due to the carbon coating. The LiMnSiO/C cathode material obtained by the solid-state method exhibits poor cycling performance, the initial discharge capacity is less than 25 m Ah/g.
文摘以五氧化二钒干凝胶、碳酸锰、磷酸二氢铵、碳酸锂、乙炔黑为原料,采用固相法在相对较低的温度条件下合成了x Li Mn PO4·y Li3V2(PO4)3锂离子电池复合正极材料。采用X射线衍射(XRD)、扫描电镜(SEM)对其晶体结构和表面形貌进行表征。结果表明,750℃下烧结15 h合成的3Li Mn PO4·Li3V2(PO4)3为结晶良好的两相结构,颗粒粒径较小且分布比较均匀,其在室温、0.2 C倍率下首次充放电容量分别为144.8 m Ah/g和139.8 m Ah/g,循环50次后容量为130.5 m Ah/g。
文摘通过溶胶-凝胶法制备了Li_2FeSiO_4@C/CNTs(LFS@C/CNTs)纳米复合材料,其中三嵌段共聚物P123用作结构导向剂和碳源,碳纳米管作为导电线提高材料的导电性。LFS@C/CNTs不仅具有海绵状纳米孔,能够与电解液充分接触改善锂离子的传输路径,同时由非晶碳和碳纳米管构成的三维桥联导电网络利于电子的快速传递,提高了材料大电流充放电能力和循环稳定性。复合后的LFS@C/CNTs的高倍率性能相比LFS@C明显提高,当CNTs的掺量为4%,电压窗口为1.5~4.5 V,0.1C电流密度下放电比容量为182 m Ah·g^(-1)。在10C经70次循环后该材料的放电比容量能保持在117 m Ah·g^(-1),是LFS@C放电比容量(55 m Ah·g^(-1))的两倍。