Based on aluminum sulfate,a fluorine-free and alkali-free liquid accelerator(FF-AF-A)was prepared in this study.The setting time and compressive strength of three cement types with different FF-AF-A dosages were fully...Based on aluminum sulfate,a fluorine-free and alkali-free liquid accelerator(FF-AF-A)was prepared in this study.The setting time and compressive strength of three cement types with different FF-AF-A dosages were fully investigated.The compatibility of the FF-AF-A with the superplasticizers were also investigated,and the early hydration behavior and morphology of the hydration products of reference cement paste with the FF-AF-A were explored by hydration heat,X-ray diffractometry(XRD),and scanning electron microscopy(SEM).Test results indicated that adding the FF-AF-A at 8 wt%of the cement weight resulted in 2 min 35 s initial setting time and 6 min 30 s final setting time.The 1-day compressive strength of the cement mortar with 8 wt%of FF-AF-A reached 13.5 MPa,which represents an increase of 35%as compared to the strength of cement mortar without the FF-AF-A,and the 28-day compressive strength ratio was 119%.In addition,the FF-AF-A also showed good compatibility with different superplasticizer dosages.The results show that,when the FF-AF-A was added to the cement paste,it promoted the formation of ettringite crystals due to the aluminum ions(Al^(3+))and sulfate ions(SO_(4)^(2-))reacted with gypsum in the cement,as well as promoted the hydration of tricalcium aluminate(C_(3)A)and tricalcium silicate(C3S)leading to the overall structure becomes more compact.As a consequence,the hydration heat rate of the cement sharply increased,the cement paste setting time is shortened,and the compressive strength of cement mortar is improved.展开更多
A linear acceleration sensor,which is inspired by the human balance organ,is designed and prepared. It uses a liquid mass-block and a symmetrical-electrodes metal-core polyvinylidene fluoride fiber(SMPF)as the sensor ...A linear acceleration sensor,which is inspired by the human balance organ,is designed and prepared. It uses a liquid mass-block and a symmetrical-electrodes metal-core polyvinylidene fluoride fiber(SMPF)as the sensor element. The output signal of the sensor has an exponential relationship with the excitation amplitude of the impacting vibration. It is capable of detecting the amplitude and the correct frequency for sinusoidal excitations using an exponential correlation. The experiments indicate that both the output signal of the sensor and the resonance frequency increase substantially with increasing diameter of the metal core. The first-order resonance frequencies of the sensors with 40,60,and 80 μm diameter metal wires are below 10 Hz,which is near the range of human body motion frequencies.展开更多
A colliding microjet liquid sheet target system was developed and tested for pairs of round nozzles of 10,11 and 18μm in diameter.The sheet's position stability was found to be better than a few micrometers.Upon ...A colliding microjet liquid sheet target system was developed and tested for pairs of round nozzles of 10,11 and 18μm in diameter.The sheet's position stability was found to be better than a few micrometers.Upon interaction with 50 mJ laser pulses,the 18μm jet has a resonance amplitude of 16μm at a repetition rate of 33 Hz,while towards 100 Hz it converges to 10μm for all nozzles.A white-light interferometric system was developed to measure the liquid sheet thickness in the target chamber both in air and in vacuum,with a measurement range of 182 nm±1μm and an accuracy of±3%.The overall shape and 3D shape of the sheet follow the Hasson±Peck model in air.In vacuum versus air,the sheet gradually loses 10%of its thickness,so the thinnest sheet achieved was below 200 nm at a vacuum level of 10±4mbar,and remained stable for several hours of operation.展开更多
基金grateful funding provided by National Key Research and Development Program of China(Project 2019YFC1906202)Guangxi Key Research and Development Plan(Guike AB19259008)Major Science and Technology Special Project of Guangxi Province(Guike AA18242007-3).
文摘Based on aluminum sulfate,a fluorine-free and alkali-free liquid accelerator(FF-AF-A)was prepared in this study.The setting time and compressive strength of three cement types with different FF-AF-A dosages were fully investigated.The compatibility of the FF-AF-A with the superplasticizers were also investigated,and the early hydration behavior and morphology of the hydration products of reference cement paste with the FF-AF-A were explored by hydration heat,X-ray diffractometry(XRD),and scanning electron microscopy(SEM).Test results indicated that adding the FF-AF-A at 8 wt%of the cement weight resulted in 2 min 35 s initial setting time and 6 min 30 s final setting time.The 1-day compressive strength of the cement mortar with 8 wt%of FF-AF-A reached 13.5 MPa,which represents an increase of 35%as compared to the strength of cement mortar without the FF-AF-A,and the 28-day compressive strength ratio was 119%.In addition,the FF-AF-A also showed good compatibility with different superplasticizer dosages.The results show that,when the FF-AF-A was added to the cement paste,it promoted the formation of ettringite crystals due to the aluminum ions(Al^(3+))and sulfate ions(SO_(4)^(2-))reacted with gypsum in the cement,as well as promoted the hydration of tricalcium aluminate(C_(3)A)and tricalcium silicate(C3S)leading to the overall structure becomes more compact.As a consequence,the hydration heat rate of the cement sharply increased,the cement paste setting time is shortened,and the compressive strength of cement mortar is improved.
基金supported by the National Natural Science Foundation of China(Nos. 51775483 and 51275447)the Research Innovation Program for College Graduates of Jiangsu Province(No.SJLX_0589)
文摘A linear acceleration sensor,which is inspired by the human balance organ,is designed and prepared. It uses a liquid mass-block and a symmetrical-electrodes metal-core polyvinylidene fluoride fiber(SMPF)as the sensor element. The output signal of the sensor has an exponential relationship with the excitation amplitude of the impacting vibration. It is capable of detecting the amplitude and the correct frequency for sinusoidal excitations using an exponential correlation. The experiments indicate that both the output signal of the sensor and the resonance frequency increase substantially with increasing diameter of the metal core. The first-order resonance frequencies of the sensors with 40,60,and 80 μm diameter metal wires are below 10 Hz,which is near the range of human body motion frequencies.
基金The project has been supported by the National Research,Development,and Innovation Office through the National Laboratory program(contract Nos.NKFIH-877-2/2020,NKFIH-476-4/2021 and NKFIH-476-16/2021)The ELIALPS project(GINOP-2.3.6-15-2015-00001)is supported by the European Union and co-financed by the European Regional Development Fund。
文摘A colliding microjet liquid sheet target system was developed and tested for pairs of round nozzles of 10,11 and 18μm in diameter.The sheet's position stability was found to be better than a few micrometers.Upon interaction with 50 mJ laser pulses,the 18μm jet has a resonance amplitude of 16μm at a repetition rate of 33 Hz,while towards 100 Hz it converges to 10μm for all nozzles.A white-light interferometric system was developed to measure the liquid sheet thickness in the target chamber both in air and in vacuum,with a measurement range of 182 nm±1μm and an accuracy of±3%.The overall shape and 3D shape of the sheet follow the Hasson±Peck model in air.In vacuum versus air,the sheet gradually loses 10%of its thickness,so the thinnest sheet achieved was below 200 nm at a vacuum level of 10±4mbar,and remained stable for several hours of operation.