The 10Ni5CrMoV steel examined was a 16 mm thick plate. Specimens measuring 12 mm×12 mm×120 mm were thermally cycled using DM-100A weld simulator with various parameters. The main results are summarized as fo...The 10Ni5CrMoV steel examined was a 16 mm thick plate. Specimens measuring 12 mm×12 mm×120 mm were thermally cycled using DM-100A weld simulator with various parameters. The main results are summarized as follaws. In the coarse-grained austenitized region（ Tm = 1 300℃ ＋ 1300℃ ） ,the microstructure is in good toughness. At the condition of Tm = 1 300℃ ＋ 850℃ and t8/5=43 s, the toughness decreases heavily because M-A constituent and twin martensite appear at the prior aastenite grain boundaries. When Tm= 1300℃ ＋ 850℃ or 1300℃ ＋ 730℃ and t8/5 = 85 s, local brittle zone is formed because of relatively coarse granular bainite.展开更多
In this paper, toughness properties and microstructurc of low-alloyed multipass welds with yield strength above 700MPa have 6een studied using the weld thermal simulation and throughout thickness CTOD fracture mechani...In this paper, toughness properties and microstructurc of low-alloyed multipass welds with yield strength above 700MPa have 6een studied using the weld thermal simulation and throughout thickness CTOD fracture mechanics tests. Impact testing of thermal simulated specimens showed that the primary weld metal and the fine gmmed weld metal had good toughness, while the coarse grained weld metal had the lowest toughness value as the local brittle zone (LBZ) in multipass weld metals. Cleavage fracture in CTOD testing of thick multipass weld metals was initiated from martensite-austenite (MA) phases in the LBZ. MA phases were distributed at the prior austenite grain boundaries and around ferrite grains. As the size of the local brittle zone along the fatigue crack front increases, CTOD frncture toughness of multipass weld metals decreases. The weakest link theory was used to evaluate effect of the local brittle zone on fracture toughness of thick multipass weld metals. The estimated curves agree well with the eaperimental data.展开更多
By using thermo-simulation,Auger analysis and Charpy Ⅴ impact test and with the observation of the microstructures in which cleavage crack was initiated,the morphology and toughness of the local brittle zone of C-Mn ...By using thermo-simulation,Auger analysis and Charpy Ⅴ impact test and with the observation of the microstructures in which cleavage crack was initiated,the morphology and toughness of the local brittle zone of C-Mn and Cr-Ni-Mo multipass weld metals have been investigated.The results indicated that the local brittle zone in C-Mn weld metals with low and high Mn％ and Cr- Ni-Mo weld metals is different.With statistical analysis,it has been revealed that the more the local brittle zone and the lower their toughness,the lower the toughness of the entire weld metals.The alloy elements have a noticeable influ- ence on the toughness of the local brittle zone,thereby changing the toughness of weld metals.展开更多
文摘The 10Ni5CrMoV steel examined was a 16 mm thick plate. Specimens measuring 12 mm×12 mm×120 mm were thermally cycled using DM-100A weld simulator with various parameters. The main results are summarized as follaws. In the coarse-grained austenitized region（ Tm = 1 300℃ ＋ 1300℃ ） ,the microstructure is in good toughness. At the condition of Tm = 1 300℃ ＋ 850℃ and t8/5=43 s, the toughness decreases heavily because M-A constituent and twin martensite appear at the prior aastenite grain boundaries. When Tm= 1300℃ ＋ 850℃ or 1300℃ ＋ 730℃ and t8/5 = 85 s, local brittle zone is formed because of relatively coarse granular bainite.
文摘In this paper, toughness properties and microstructurc of low-alloyed multipass welds with yield strength above 700MPa have 6een studied using the weld thermal simulation and throughout thickness CTOD fracture mechanics tests. Impact testing of thermal simulated specimens showed that the primary weld metal and the fine gmmed weld metal had good toughness, while the coarse grained weld metal had the lowest toughness value as the local brittle zone (LBZ) in multipass weld metals. Cleavage fracture in CTOD testing of thick multipass weld metals was initiated from martensite-austenite (MA) phases in the LBZ. MA phases were distributed at the prior austenite grain boundaries and around ferrite grains. As the size of the local brittle zone along the fatigue crack front increases, CTOD frncture toughness of multipass weld metals decreases. The weakest link theory was used to evaluate effect of the local brittle zone on fracture toughness of thick multipass weld metals. The estimated curves agree well with the eaperimental data.
文摘By using thermo-simulation,Auger analysis and Charpy Ⅴ impact test and with the observation of the microstructures in which cleavage crack was initiated,the morphology and toughness of the local brittle zone of C-Mn and Cr-Ni-Mo multipass weld metals have been investigated.The results indicated that the local brittle zone in C-Mn weld metals with low and high Mn％ and Cr- Ni-Mo weld metals is different.With statistical analysis,it has been revealed that the more the local brittle zone and the lower their toughness,the lower the toughness of the entire weld metals.The alloy elements have a noticeable influ- ence on the toughness of the local brittle zone,thereby changing the toughness of weld metals.