The asphalt pavement longitudinal crack is a common distress in cold regions,resulting from uneven deformation of the subgrade.Analysis of the correlation law between uneven deformation and crack distress is of positi...The asphalt pavement longitudinal crack is a common distress in cold regions,resulting from uneven deformation of the subgrade.Analysis of the correlation law between uneven deformation and crack distress is of positive significance for understanding the mechanism of crack initiation,and putting forward treatment measures.In view of the complexity of longitudinal crack inducement and road surface deformation,the grey relational method was used to analyze this relationship.Through long-term monitoring of the vertical deformation data of typical road sections,the vertical deformation law of the pavement surface and its deformation characteristics under the action of temperature field are analyzed.Parameters such as vertical relative deformation,vertical relative deformation rate and vertical differential deformation VDSr were constructed to describe vertical deformation characteristics.Typical distribution characteristics of longitudinal fractures and their length and distribution characteristics are also described.The grey correlation analysis theory was utilized to analyze the relationship between deformation characteristics of sections,cross sections and monitoring points and longitudinal crack characteristics(length and location).The analysis reveals a linear positive correlation or a high correlation between several indicators.This study can provide a deeper understanding of the occurrence and development mechanism of longitudinal cracks in asphalt pavement of cold areas,and give references for the research of road engineering structure,materials and distress prevention.展开更多
At present, embankment longitudinal cracks are a major problem in highways through permafrost regions, and seriously affect traffic safety and the normal operations of the highway. In the past, roadbed height in perma...At present, embankment longitudinal cracks are a major problem in highways through permafrost regions, and seriously affect traffic safety and the normal operations of the highway. In the past, roadbed height in permafrost regions was relatively low, and embankment cracks were rare and did not affect traffic safety. Thus, highway designers and researchers paid little attention to this problem, and they knew very little about distribution laws and mechanism of embankment longitudinal cracks. Due to this lack of knowledge, there is no uniform opinion on this problem, making it difficult to find measures that will mediate the impact of longi- tudinal crocks. Temperature is a major factor that affects and controls embankment stability in permafrost regions, especially in ice-rich and high-temperature regions, and solar radiation is the principal factor that determines surface temperatures. Under higher embankment, the difference of temperature will be larger between a sunny slope and a shady slope. Hence, the probability for longitudinal cracks generation is higher. In this paper, a survey and analysis of longitudinal cracks along the Qinghai-Tibet Highway were carried out. The longitudinal cracks are found to be related to the road strikes. Solar radiation is considered to play an important role in the generation of longitudinal cracks.展开更多
Based on a series of related investigations, a mechanism for the formation of longitudinal surface cracks on a continuous casting slab of high-carbon steel was investigated. High-temperature tensile tests performed on...Based on a series of related investigations, a mechanism for the formation of longitudinal surface cracks on a continuous casting slab of high-carbon steel was investigated. High-temperature tensile tests performed on slab samples,metallographic and scanning electron microscopy studies, as well as heat flux and shell thickness in continuous casting predicted on the basis of a mathematical model were conducted. The results showed that high- carbon steel exhibited a much lower liquidus temperature and a wider brittle temperature range immediately after solidification compared with those of low-carbon steel. Concentrations of elements K and Na, which are contained in the mold fluxes, were not observed in the cracks during this study. The calculated results showed that the heat flux and the shell thickness were uneven along the mold width and that the shell was thinner and close to the center line of the slab surface. The longitudinal cracks were observed in situ using confocal laser scanning microscopy, to first occur close to the solidification front,where the ductility was extremely low;in addition ,the shell growth was slower than in other regions, which led to a thinner shell and depressed shrinkage owing to a lack of lubrication by the mold fluxes below the meniscus. Furthermore, the pouring temperature of high-carbon steel is - 100 ~C lower than that of low-carbon steel,so the formation of a stable liquid flux near the meniscus within a short time at the beginning of casting is difficult. The amounts of liquid slag film and crystalline slag film were insufficient to provide adequate lubrication between the shell and the mold, which resulted in greater friction force that induced or aggravated cracks. Therefore, the homogeneity of mold fluxes and initial solidification in the mold should be improved to reduce the concentration of slab surface defects.展开更多
The fact that the amount of the mold flux components differs at differentlocations on the cracking surface indicates that the longitudinal surface cracks are initiallyformed in the mold and are enlarged in the seconda...The fact that the amount of the mold flux components differs at differentlocations on the cracking surface indicates that the longitudinal surface cracks are initiallyformed in the mold and are enlarged in the secondary cooling zone. Based on the hot ductilitymeasurement of two typical container used steels, it is known that the steels are in severeembrittlement state in the temperature range of 825-775 deg C. By means of increasing Cr/Ni platingthickness on the upper part of the mold, reducing mold heat flux, adopting new secondary coolingpattern, etc., the occurrence of the surface longitudinal cracks on the steel CC (continuouscasting) slabs has been significantly reduced.展开更多
Hypo-peritectic steels are widely used in various industrial fields because of their high strength,high toughness,high processability,high weldability,and low material cost.However,surface defects are liable to occur ...Hypo-peritectic steels are widely used in various industrial fields because of their high strength,high toughness,high processability,high weldability,and low material cost.However,surface defects are liable to occur during continuous casting,which includes depression,longitudinal cracks,deep oscillation marks,and severe level fluctuation with slag entrapment.The high-efficiency production of hypo-peritectic steels by continuous casting is still a great challenge due to the limited understanding of the mechanism of peritectic solidification.This work reviews the definition and classification of hypo-peritectic steels and introduces the formation tendency of common surface defects related to peritectic solidification.New achievements in the mechanism of peritectic reaction and transformation have been listed.Finally,countermeasures to avoiding surface defects of hypo-peritectic steels duiring continuous casting are summarized.Enlightening certain points in the continuous casting of hypo-peritectic steels and the development of new techniques to overcome the present problems will be a great aid to researchers.展开更多
The No. 3 slab caster,which mainly provides slabs to the 5000 mm plate mill at Baosteel, was put into production in December,2004. The size of the biggest slab produced by this caster is 2300 mm in width and 300 mm in...The No. 3 slab caster,which mainly provides slabs to the 5000 mm plate mill at Baosteel, was put into production in December,2004. The size of the biggest slab produced by this caster is 2300 mm in width and 300 mm in thickness. The designed output of the caster is 2.3 Mt/a. Slab surface longitudinal crack defects,which were related to the heat flux of the mold, frequently occurred in the early stage of the startup of the caster. As mild cooling powder is beneficial to the uniformity of the shell of initial slabs ,the concentration of stress is reduced, and the longitudinal cracking on the surface is avoided. This study evaluates the performance of several kinds of powder, and the results show that mold powder of high basicity, high crystallization proportion and low heat flux is to the benefit of the reduction of the longitudinal cracks on the surface and the defects of slabs.展开更多
Chamfered mould has gradually become a new technology equipment to eliminate transverse corner crack.However,longitudinal corner crack ratio of chamfered slab was very high.Solidification microstructure was detected i...Chamfered mould has gradually become a new technology equipment to eliminate transverse corner crack.However,longitudinal corner crack ratio of chamfered slab was very high.Solidification microstructure was detected in the area where the longitudinal corner crack occurred.Effect of narrow face shape and taper distribution of mould copper plate on longitudinal corner crack was studied by industrial tests.Water velocity distribution in the narrow copper plate was studied by numerical simulation.On the premise of preventing cooling water from nuclear boiling,improvement measures of mould cooling process and water seam structure were put forward through heat transfer calculation.The results showed that local taper of the meniscus region of mould should be increased to prevent generation of longitudinal corner crack.Chamfering slope length of narrow copper plate should be controlled within 55 mm,and chamfering angle should be controlled at about 30°.Average water velocity should be more than 7.0 m/s.The flat and chamfering regions of narrow copper plate working face should be designed as double taper and funnel structure,respectively.The water seam in the chamfering region should preferentially choose the combined cooling structure with two holes and one slot.In order to prevent the extension of longitudinal corner crack,chamfered narrow face foot roller should be used.展开更多
In order to solve the problem of the high surface longitudinal crack ratio of heavy peritectic steel slabs produced by the No. 3 continuous caster at Baosteel,the physical properties of the original mold flux and the ...In order to solve the problem of the high surface longitudinal crack ratio of heavy peritectic steel slabs produced by the No. 3 continuous caster at Baosteel,the physical properties of the original mold flux and the optimized mold flux were compared in a comprehensive way by using analytical measures, such as a slag film heat-flow simulator, a thermowire molten flux crystallization tester and an X-ray diffractometer in the laboratory. The results reveal that one of the major reasons for the cracks is the poor heat transfer ability of the original mold flux. However, the optimized mold flux with a high basicity features a high crystallizing rate,low crystallization temperature and low heat-flow density. Therefore, the optimized mold flux is more suitable for casting peritectic steel by the heavy slab continuous caster. The test results show that the slabs produced by using the optimized mold flux had no surface longitudinal crack in four test casts, while the surface longitudinal crack ratio of the slabs produced by using the original mold flux was 5%. The optimized mold flux can effectively prevent slab surface longitudinal cracks from occurring.展开更多
The surface longitudinal cracking of peritectic steel Q345 D slab was studied by means of metallographic microscopy and scanning electron microscopy. The results show that the surface longitudinal cracking is caused b...The surface longitudinal cracking of peritectic steel Q345 D slab was studied by means of metallographic microscopy and scanning electron microscopy. The results show that the surface longitudinal cracking is caused by the shell repeatedly tearing and healing under the action of stress, which is due to disruption of the steel matrix continuity with inclusion aggregation on the shell surface. The relative precautions of reducing the cracking are raised according to the practical situation.展开更多
Scattering of an incident grazing longitudinal ultrasonic wave pulse by a traction - free ribbon - type crack in solid is theoretically analyzed. An exact series solution of the scattered field is obtained by iteratio...Scattering of an incident grazing longitudinal ultrasonic wave pulse by a traction - free ribbon - type crack in solid is theoretically analyzed. An exact series solution of the scattered field is obtained by iteration. Each term of the series corresponds roughly to one of the rescattering processes by the respective crack tips. The first two terms, which combine to form the second order approximate solution, are discussed in detail. This 2nd - order solution includes scattered cylindrical longitudinal waves, cylindrical shear waves , head waves and surface waves on the crack surfaces, and it gives good description of the early - time wave field.展开更多
By using the dynamic photoelastic method and our technique of fabricating an internal crack in solid , the scattered waves of incident grazing longitudinal ultrasonic wave pulse by a ribbon-type crack are ob-served an...By using the dynamic photoelastic method and our technique of fabricating an internal crack in solid , the scattered waves of incident grazing longitudinal ultrasonic wave pulse by a ribbon-type crack are ob-served and analyzed . In particular, the distribution of the intensity of the scattered head wave is measured quantitatively . The experimental results fairly agree with the theoretical ones given in ref. [ 1 ] .展开更多
The correlation between the longitudinal crack occurrence and integrated heat transfer of the mold with data mining methods was investigated.Firstly,three kinds of support vector machine models based on principal comp...The correlation between the longitudinal crack occurrence and integrated heat transfer of the mold with data mining methods was investigated.Firstly,three kinds of support vector machine models based on principal component analysis with different input features were established to explore the effect of integrated heat transfer on the accuracy of the prediction model for the longitudinal crack.The results show that the accuracy was improved while features including mean and standard deviation of integrated heat transfer were added.Then,the difference in integrated heat transfer between defect and normal samples under the same process parameters was quantitatively compared.Compared with normal samples,the temperature difference of cooling water for defect samples decreased by 0.65%,and the temperature difference fluctuation increased by 31.1%.Finally,the literature data were used to provide support for the quantitative correlation according to defect formation mechanism.A new criterion for the prediction of longitudinal crack and a discovering method for correlation between product quality and process parameters in the manufacturing industry have been provided.展开更多
This paper discusses cracking in airport pavements as studied in Construction Cycle 6 of testing carried out at the National Airport Pavement Testing Facility by the Federal Aviation Administration. Pavements of three...This paper discusses cracking in airport pavements as studied in Construction Cycle 6 of testing carried out at the National Airport Pavement Testing Facility by the Federal Aviation Administration. Pavements of three different flexural strengths as well as two different subgrades, a soft bituminous layer and a more rigid layer known as econocrete, were tested. In addition to this, cracking near two types of isolated transition joints, a reinforced edge joint and a thickened edge joint, was considered. The pavement sections were tested using a moving load simulating that of an aircraft. It has been determined that the degree of cracking was reduced as the flexural strength of the pavement was increased and that fewer cracks formed over the econocrete base than over the bituminous base. In addition, the thickened edge transition joint was more effective in preventing cracking at the edges compared to the reinforced edge joint.展开更多
基金funded by Key Scientific Research Project of Heilongjiang Provincial Department of Transportation(Grant number MH20200828)National Natural Science Foundation of China joint fund for regional innovation and development(Grant number U20A20315)。
文摘The asphalt pavement longitudinal crack is a common distress in cold regions,resulting from uneven deformation of the subgrade.Analysis of the correlation law between uneven deformation and crack distress is of positive significance for understanding the mechanism of crack initiation,and putting forward treatment measures.In view of the complexity of longitudinal crack inducement and road surface deformation,the grey relational method was used to analyze this relationship.Through long-term monitoring of the vertical deformation data of typical road sections,the vertical deformation law of the pavement surface and its deformation characteristics under the action of temperature field are analyzed.Parameters such as vertical relative deformation,vertical relative deformation rate and vertical differential deformation VDSr were constructed to describe vertical deformation characteristics.Typical distribution characteristics of longitudinal fractures and their length and distribution characteristics are also described.The grey correlation analysis theory was utilized to analyze the relationship between deformation characteristics of sections,cross sections and monitoring points and longitudinal crack characteristics(length and location).The analysis reveals a linear positive correlation or a high correlation between several indicators.This study can provide a deeper understanding of the occurrence and development mechanism of longitudinal cracks in asphalt pavement of cold areas,and give references for the research of road engineering structure,materials and distress prevention.
基金funded by the Transportation Construction Projects from the Ministry of Transport of the People's Republic of China (Contract No.:2002 318 795 02)
文摘At present, embankment longitudinal cracks are a major problem in highways through permafrost regions, and seriously affect traffic safety and the normal operations of the highway. In the past, roadbed height in permafrost regions was relatively low, and embankment cracks were rare and did not affect traffic safety. Thus, highway designers and researchers paid little attention to this problem, and they knew very little about distribution laws and mechanism of embankment longitudinal cracks. Due to this lack of knowledge, there is no uniform opinion on this problem, making it difficult to find measures that will mediate the impact of longi- tudinal crocks. Temperature is a major factor that affects and controls embankment stability in permafrost regions, especially in ice-rich and high-temperature regions, and solar radiation is the principal factor that determines surface temperatures. Under higher embankment, the difference of temperature will be larger between a sunny slope and a shady slope. Hence, the probability for longitudinal cracks generation is higher. In this paper, a survey and analysis of longitudinal cracks along the Qinghai-Tibet Highway were carried out. The longitudinal cracks are found to be related to the road strikes. Solar radiation is considered to play an important role in the generation of longitudinal cracks.
文摘Based on a series of related investigations, a mechanism for the formation of longitudinal surface cracks on a continuous casting slab of high-carbon steel was investigated. High-temperature tensile tests performed on slab samples,metallographic and scanning electron microscopy studies, as well as heat flux and shell thickness in continuous casting predicted on the basis of a mathematical model were conducted. The results showed that high- carbon steel exhibited a much lower liquidus temperature and a wider brittle temperature range immediately after solidification compared with those of low-carbon steel. Concentrations of elements K and Na, which are contained in the mold fluxes, were not observed in the cracks during this study. The calculated results showed that the heat flux and the shell thickness were uneven along the mold width and that the shell was thinner and close to the center line of the slab surface. The longitudinal cracks were observed in situ using confocal laser scanning microscopy, to first occur close to the solidification front,where the ductility was extremely low;in addition ,the shell growth was slower than in other regions, which led to a thinner shell and depressed shrinkage owing to a lack of lubrication by the mold fluxes below the meniscus. Furthermore, the pouring temperature of high-carbon steel is - 100 ~C lower than that of low-carbon steel,so the formation of a stable liquid flux near the meniscus within a short time at the beginning of casting is difficult. The amounts of liquid slag film and crystalline slag film were insufficient to provide adequate lubrication between the shell and the mold, which resulted in greater friction force that induced or aggravated cracks. Therefore, the homogeneity of mold fluxes and initial solidification in the mold should be improved to reduce the concentration of slab surface defects.
文摘The fact that the amount of the mold flux components differs at differentlocations on the cracking surface indicates that the longitudinal surface cracks are initiallyformed in the mold and are enlarged in the secondary cooling zone. Based on the hot ductilitymeasurement of two typical container used steels, it is known that the steels are in severeembrittlement state in the temperature range of 825-775 deg C. By means of increasing Cr/Ni platingthickness on the upper part of the mold, reducing mold heat flux, adopting new secondary coolingpattern, etc., the occurrence of the surface longitudinal cracks on the steel CC (continuouscasting) slabs has been significantly reduced.
基金financially supported by the Fundamental Research Funds for the Central Universities(No.FRF-TP-19-017A3)the National Natural Science Foundation of China(No.51874026)。
文摘Hypo-peritectic steels are widely used in various industrial fields because of their high strength,high toughness,high processability,high weldability,and low material cost.However,surface defects are liable to occur during continuous casting,which includes depression,longitudinal cracks,deep oscillation marks,and severe level fluctuation with slag entrapment.The high-efficiency production of hypo-peritectic steels by continuous casting is still a great challenge due to the limited understanding of the mechanism of peritectic solidification.This work reviews the definition and classification of hypo-peritectic steels and introduces the formation tendency of common surface defects related to peritectic solidification.New achievements in the mechanism of peritectic reaction and transformation have been listed.Finally,countermeasures to avoiding surface defects of hypo-peritectic steels duiring continuous casting are summarized.Enlightening certain points in the continuous casting of hypo-peritectic steels and the development of new techniques to overcome the present problems will be a great aid to researchers.
文摘The No. 3 slab caster,which mainly provides slabs to the 5000 mm plate mill at Baosteel, was put into production in December,2004. The size of the biggest slab produced by this caster is 2300 mm in width and 300 mm in thickness. The designed output of the caster is 2.3 Mt/a. Slab surface longitudinal crack defects,which were related to the heat flux of the mold, frequently occurred in the early stage of the startup of the caster. As mild cooling powder is beneficial to the uniformity of the shell of initial slabs ,the concentration of stress is reduced, and the longitudinal cracking on the surface is avoided. This study evaluates the performance of several kinds of powder, and the results show that mold powder of high basicity, high crystallization proportion and low heat flux is to the benefit of the reduction of the longitudinal cracks on the surface and the defects of slabs.
文摘Chamfered mould has gradually become a new technology equipment to eliminate transverse corner crack.However,longitudinal corner crack ratio of chamfered slab was very high.Solidification microstructure was detected in the area where the longitudinal corner crack occurred.Effect of narrow face shape and taper distribution of mould copper plate on longitudinal corner crack was studied by industrial tests.Water velocity distribution in the narrow copper plate was studied by numerical simulation.On the premise of preventing cooling water from nuclear boiling,improvement measures of mould cooling process and water seam structure were put forward through heat transfer calculation.The results showed that local taper of the meniscus region of mould should be increased to prevent generation of longitudinal corner crack.Chamfering slope length of narrow copper plate should be controlled within 55 mm,and chamfering angle should be controlled at about 30°.Average water velocity should be more than 7.0 m/s.The flat and chamfering regions of narrow copper plate working face should be designed as double taper and funnel structure,respectively.The water seam in the chamfering region should preferentially choose the combined cooling structure with two holes and one slot.In order to prevent the extension of longitudinal corner crack,chamfered narrow face foot roller should be used.
文摘In order to solve the problem of the high surface longitudinal crack ratio of heavy peritectic steel slabs produced by the No. 3 continuous caster at Baosteel,the physical properties of the original mold flux and the optimized mold flux were compared in a comprehensive way by using analytical measures, such as a slag film heat-flow simulator, a thermowire molten flux crystallization tester and an X-ray diffractometer in the laboratory. The results reveal that one of the major reasons for the cracks is the poor heat transfer ability of the original mold flux. However, the optimized mold flux with a high basicity features a high crystallizing rate,low crystallization temperature and low heat-flow density. Therefore, the optimized mold flux is more suitable for casting peritectic steel by the heavy slab continuous caster. The test results show that the slabs produced by using the optimized mold flux had no surface longitudinal crack in four test casts, while the surface longitudinal crack ratio of the slabs produced by using the original mold flux was 5%. The optimized mold flux can effectively prevent slab surface longitudinal cracks from occurring.
文摘The surface longitudinal cracking of peritectic steel Q345 D slab was studied by means of metallographic microscopy and scanning electron microscopy. The results show that the surface longitudinal cracking is caused by the shell repeatedly tearing and healing under the action of stress, which is due to disruption of the steel matrix continuity with inclusion aggregation on the shell surface. The relative precautions of reducing the cracking are raised according to the practical situation.
文摘Scattering of an incident grazing longitudinal ultrasonic wave pulse by a traction - free ribbon - type crack in solid is theoretically analyzed. An exact series solution of the scattered field is obtained by iteration. Each term of the series corresponds roughly to one of the rescattering processes by the respective crack tips. The first two terms, which combine to form the second order approximate solution, are discussed in detail. This 2nd - order solution includes scattered cylindrical longitudinal waves, cylindrical shear waves , head waves and surface waves on the crack surfaces, and it gives good description of the early - time wave field.
文摘By using the dynamic photoelastic method and our technique of fabricating an internal crack in solid , the scattered waves of incident grazing longitudinal ultrasonic wave pulse by a ribbon-type crack are ob-served and analyzed . In particular, the distribution of the intensity of the scattered head wave is measured quantitatively . The experimental results fairly agree with the theoretical ones given in ref. [ 1 ] .
基金the support from National Natural Science Foundation of China(52274318).
文摘The correlation between the longitudinal crack occurrence and integrated heat transfer of the mold with data mining methods was investigated.Firstly,three kinds of support vector machine models based on principal component analysis with different input features were established to explore the effect of integrated heat transfer on the accuracy of the prediction model for the longitudinal crack.The results show that the accuracy was improved while features including mean and standard deviation of integrated heat transfer were added.Then,the difference in integrated heat transfer between defect and normal samples under the same process parameters was quantitatively compared.Compared with normal samples,the temperature difference of cooling water for defect samples decreased by 0.65%,and the temperature difference fluctuation increased by 31.1%.Finally,the literature data were used to provide support for the quantitative correlation according to defect formation mechanism.A new criterion for the prediction of longitudinal crack and a discovering method for correlation between product quality and process parameters in the manufacturing industry have been provided.
基金the Federal Aviation Administration (FAA) as this work is funded under FAA research grant #10-G-012project has been sponsored by the FAA
文摘This paper discusses cracking in airport pavements as studied in Construction Cycle 6 of testing carried out at the National Airport Pavement Testing Facility by the Federal Aviation Administration. Pavements of three different flexural strengths as well as two different subgrades, a soft bituminous layer and a more rigid layer known as econocrete, were tested. In addition to this, cracking near two types of isolated transition joints, a reinforced edge joint and a thickened edge joint, was considered. The pavement sections were tested using a moving load simulating that of an aircraft. It has been determined that the degree of cracking was reduced as the flexural strength of the pavement was increased and that fewer cracks formed over the econocrete base than over the bituminous base. In addition, the thickened edge transition joint was more effective in preventing cracking at the edges compared to the reinforced edge joint.