The purpose of the study is to decrease content of CaF2 in dephosphorization slag. The dephosphorization effects of CaF2 replaced by B2O3 were investigated. The dephosphorization experiments were carried out at 1 450 ...The purpose of the study is to decrease content of CaF2 in dephosphorization slag. The dephosphorization effects of CaF2 replaced by B2O3 were investigated. The dephosphorization experiments were carried out at 1 450 ℃ in air atmosphere. The results show that the melting points and dephosphorization ratios change little when CaF2 was replaced by B2O3. The dephosphorization ratios are all greater than 80% and melting points can meet the requirement of hot metal pretreatment. Because of the change of alkalinity caused by B2 03, the oxidation of slag increases with increasing of B2 Oa contents. It is beneficial to pre-dephosphorization. As a result, for decreasing its pollution, CaF2 can be replaced by B2Oa to dispose fluoride-free pre-dephosphorization slag.展开更多
There are some problems in steelmaking with hot metal containing low silicon content such as difficulty in slag formation, less slag for dephosphorization and slag adhesion on oxygen lance and hood. To overcome these ...There are some problems in steelmaking with hot metal containing low silicon content such as difficulty in slag formation, less slag for dephosphorization and slag adhesion on oxygen lance and hood. To overcome these problems, experiments wcrc conducted and some improvements were obtained, such as adding appropriate flux, increasing the lance position slightly during steelmaking and using effective multi-outlet nozzle. Moreover, to keep normal heating rate, the ore and scrap charge should be reduced due to less chemical heat input in steelmaking.展开更多
基金Item Sponsored by National Natural Science Foundation of China and Baosteel(50674001)
文摘The purpose of the study is to decrease content of CaF2 in dephosphorization slag. The dephosphorization effects of CaF2 replaced by B2O3 were investigated. The dephosphorization experiments were carried out at 1 450 ℃ in air atmosphere. The results show that the melting points and dephosphorization ratios change little when CaF2 was replaced by B2O3. The dephosphorization ratios are all greater than 80% and melting points can meet the requirement of hot metal pretreatment. Because of the change of alkalinity caused by B2 03, the oxidation of slag increases with increasing of B2 Oa contents. It is beneficial to pre-dephosphorization. As a result, for decreasing its pollution, CaF2 can be replaced by B2Oa to dispose fluoride-free pre-dephosphorization slag.
文摘There are some problems in steelmaking with hot metal containing low silicon content such as difficulty in slag formation, less slag for dephosphorization and slag adhesion on oxygen lance and hood. To overcome these problems, experiments wcrc conducted and some improvements were obtained, such as adding appropriate flux, increasing the lance position slightly during steelmaking and using effective multi-outlet nozzle. Moreover, to keep normal heating rate, the ore and scrap charge should be reduced due to less chemical heat input in steelmaking.