The effect of fast cooling rate on the microstructure and mechanical properties of low-carbon high-strength steel annealed in the intercritical region was investigated using a Gleeble 1500 thermomechanical simulator a...The effect of fast cooling rate on the microstructure and mechanical properties of low-carbon high-strength steel annealed in the intercritical region was investigated using a Gleeble 1500 thermomechanical simulator and a continuous annealing thermomeehanical simulator. The results showed that the microstructure consisted of ferrite and bainite as the main phases with a small amount of retained austenite and martensite islands at cooling rate of 5 and 50 ℃/s, respectively. Fast cooling after continuous annealing affected all constituents of the microstructure. The mechanical properties were improved considerably. Ultimate tensile strength （U-TS） increased and total elongation （TEL） decreased with increasing cooling rate in all specimens. The specimen 1 at a cooling rate of 5 ℃/s exhibited the maximum TEL and UTSxTEL （20% and 27 200 MPa%, respectively） because of the competition between weakening by presence of the retained austenite plus the carbon indigence by carbide precipitation, and strengthening by martensitic islands and precipitation. The maximum UTS and YS （1 450 and 951 MPa, respectively） were obtained for specimen 2 at a cooling rate of 50 ℃/s. This is attributed to the effect of dispersion strengthening of finer martensite islands and the effect of precipitation strengthening of carbide precipitates.展开更多
Cu, as an austenitic stable element, is added to steel in order to suppress the adverse effects of high content of C and Mn on welding. Based on C partitioning, Cu and Mn partitioning can further improve the stability...Cu, as an austenitic stable element, is added to steel in order to suppress the adverse effects of high content of C and Mn on welding. Based on C partitioning, Cu and Mn partitioning can further improve the stability of retained austenite in the intercritical annealing process. A sample of low carbon steel containing Cu was treated by the intercritical annealing, then quenching process（I＆Q）. Subsequently, another sample was treated by the intercritical annealing, subsequent austenitizing, then quenching and partitioning process（I＆Q＆P）. The effects of element partitioning behavior in intercritical region on the microstructure and mechanical properties of the steel were studied. The results showed that after the I＆Q process ferrite and martensite could be obtained, with C, Cu and Mn enriched in the martensite. When intercritically heated at 800 ℃, Cu and Mn were partitioned from ferrite to austenite, which was enhanced gradually as the heating time was increased. This partitioning effect was the most obvious when the sample was heated at 800 ℃ for 40 min. At the early stage of α→γ transformation, the formation of γ was controlled by the partitioning of carbon, while at the later stage, it was mainly affected by the partitioning of Cu and Mn. After the I＆Q＆P process, the partitioning effect of Cu and Mn element could be retained. C was assembled in retained austenite during the quenching and partitioning process. The strength and elongation of I＆Q＆P steel was increased by 5 305 MPa% compared with that subjected to Q＆P process. The volume fraction of retained autensite was increased from 8.5% to 11.2%. Hence, the content of retained austenite could be improved significantly by Mn and Cu partitioning, which increased the elongation of steel.展开更多
Low carbon bainitic steel derives the high strength mainly from high density of dislocations rather than carbon and alloy element content, so it tends to evolve into equilibrium microstructure with low density of disl...Low carbon bainitic steel derives the high strength mainly from high density of dislocations rather than carbon and alloy element content, so it tends to evolve into equilibrium microstructure with low density of dislocations under thermal disturbance. In the present investigation, granular bainite and lath-like bainitic ferrite were produced respectively in Mo-free low-carbon steels by changing cooling rate;. It has been found that granular bainite possesses a lower strength at room temperature than bainitic ferrite, but it exhibits a slower decrease of strength with temperature increasing. Dislocation density in both granular bainite and bainitic ferrite decreases via recovery and recrystallization at high temperature. However, when reheating of bainite is carded out at temperature below 600 ℃, a long time will be needed for incubation of recrystallization, during which the hardness of bainite maintains stable. The property makes bainite, especially granular bainite, become a potential microstructure for matrix of high strength fire-resistant steel.展开更多
The 1,000 MPa ultra-high strength hot-rolled plate steel with low-carbon bainitic microstructure was developed in the laboratory for coal mine refuge chamber. The static recrystallization behavior, microstructure evol...The 1,000 MPa ultra-high strength hot-rolled plate steel with low-carbon bainitic microstructure was developed in the laboratory for coal mine refuge chamber. The static recrystallization behavior, microstructure evolution, and mechanical properties of this hot-rolled plate steel were investigated by the hot compression, continuous cooling trans- formation, and tensile deformation test. The results show that the developed steel has excellent mechanical properties at both room and elevated temperature, and its microstructure mainly consists of lath bainite, granular bainite, and ferrite after thermal-mechanical control process （TMCP）. The ultra-high strength plate steel is obtained by the TMCP process in hot rolling, strengthened by bainitic transformation, microstructure refinement, and precipitation of alloying elements such as Nb, Ti, Mo, and Cu. The experimental steel has relatively low welding crack sensitivity index and high atmospheric corrosion resistance index. Therefore, the developed steel has a good balance of strength and ductility both at room and elevated temperature, weldability and corrosion resistance, and it can suffice for the basic demands for materials in the manufacture of coal mine refuge chamber.展开更多
基金Sponsored by National Natural Science Foundation of China(No.51004037)Shenyang City Application Basic Research Project(No.F13-316-1-15)
文摘The effect of fast cooling rate on the microstructure and mechanical properties of low-carbon high-strength steel annealed in the intercritical region was investigated using a Gleeble 1500 thermomechanical simulator and a continuous annealing thermomeehanical simulator. The results showed that the microstructure consisted of ferrite and bainite as the main phases with a small amount of retained austenite and martensite islands at cooling rate of 5 and 50 ℃/s, respectively. Fast cooling after continuous annealing affected all constituents of the microstructure. The mechanical properties were improved considerably. Ultimate tensile strength （U-TS） increased and total elongation （TEL） decreased with increasing cooling rate in all specimens. The specimen 1 at a cooling rate of 5 ℃/s exhibited the maximum TEL and UTSxTEL （20% and 27 200 MPa%, respectively） because of the competition between weakening by presence of the retained austenite plus the carbon indigence by carbide precipitation, and strengthening by martensitic islands and precipitation. The maximum UTS and YS （1 450 and 951 MPa, respectively） were obtained for specimen 2 at a cooling rate of 50 ℃/s. This is attributed to the effect of dispersion strengthening of finer martensite islands and the effect of precipitation strengthening of carbide precipitates.
基金Funded by National Natural Science Foundation of China(Nos.51574107,51304186)Natural Science Foundation of Hebei Province(Nos.E2016209048,E2017209048)Tangshan High Performance Metal and Composite Materials Science and Technical Innovation Team(No.15130202C)
文摘Cu, as an austenitic stable element, is added to steel in order to suppress the adverse effects of high content of C and Mn on welding. Based on C partitioning, Cu and Mn partitioning can further improve the stability of retained austenite in the intercritical annealing process. A sample of low carbon steel containing Cu was treated by the intercritical annealing, then quenching process（I＆Q）. Subsequently, another sample was treated by the intercritical annealing, subsequent austenitizing, then quenching and partitioning process（I＆Q＆P）. The effects of element partitioning behavior in intercritical region on the microstructure and mechanical properties of the steel were studied. The results showed that after the I＆Q process ferrite and martensite could be obtained, with C, Cu and Mn enriched in the martensite. When intercritically heated at 800 ℃, Cu and Mn were partitioned from ferrite to austenite, which was enhanced gradually as the heating time was increased. This partitioning effect was the most obvious when the sample was heated at 800 ℃ for 40 min. At the early stage of α→γ transformation, the formation of γ was controlled by the partitioning of carbon, while at the later stage, it was mainly affected by the partitioning of Cu and Mn. After the I＆Q＆P process, the partitioning effect of Cu and Mn element could be retained. C was assembled in retained austenite during the quenching and partitioning process. The strength and elongation of I＆Q＆P steel was increased by 5 305 MPa% compared with that subjected to Q＆P process. The volume fraction of retained autensite was increased from 8.5% to 11.2%. Hence, the content of retained austenite could be improved significantly by Mn and Cu partitioning, which increased the elongation of steel.
文摘Low carbon bainitic steel derives the high strength mainly from high density of dislocations rather than carbon and alloy element content, so it tends to evolve into equilibrium microstructure with low density of dislocations under thermal disturbance. In the present investigation, granular bainite and lath-like bainitic ferrite were produced respectively in Mo-free low-carbon steels by changing cooling rate;. It has been found that granular bainite possesses a lower strength at room temperature than bainitic ferrite, but it exhibits a slower decrease of strength with temperature increasing. Dislocation density in both granular bainite and bainitic ferrite decreases via recovery and recrystallization at high temperature. However, when reheating of bainite is carded out at temperature below 600 ℃, a long time will be needed for incubation of recrystallization, during which the hardness of bainite maintains stable. The property makes bainite, especially granular bainite, become a potential microstructure for matrix of high strength fire-resistant steel.
基金supported by the National Natural Science Foundation of China (Nos. 51174057 and 51274062)the National High Technology Research and Development Program of China (No. 2012AA03A503)Research Fund for the Doctoral Program of Higher Education of China (No. 20130042110040)
文摘The 1,000 MPa ultra-high strength hot-rolled plate steel with low-carbon bainitic microstructure was developed in the laboratory for coal mine refuge chamber. The static recrystallization behavior, microstructure evolution, and mechanical properties of this hot-rolled plate steel were investigated by the hot compression, continuous cooling trans- formation, and tensile deformation test. The results show that the developed steel has excellent mechanical properties at both room and elevated temperature, and its microstructure mainly consists of lath bainite, granular bainite, and ferrite after thermal-mechanical control process （TMCP）. The ultra-high strength plate steel is obtained by the TMCP process in hot rolling, strengthened by bainitic transformation, microstructure refinement, and precipitation of alloying elements such as Nb, Ti, Mo, and Cu. The experimental steel has relatively low welding crack sensitivity index and high atmospheric corrosion resistance index. Therefore, the developed steel has a good balance of strength and ductility both at room and elevated temperature, weldability and corrosion resistance, and it can suffice for the basic demands for materials in the manufacture of coal mine refuge chamber.