A series of Mn-based catalysts, MnOx, MnOx-CeO, Pd-Mn-Ce, MnOx/AC were prepared. And their performances for NO low-temperature SCR were investigated in this study. The NO conversion is about 90% at 100 ℃ on MnOx-CeOa...A series of Mn-based catalysts, MnOx, MnOx-CeO, Pd-Mn-Ce, MnOx/AC were prepared. And their performances for NO low-temperature SCR were investigated in this study. The NO conversion is about 90% at 100 ℃ on MnOx-CeOand almost all NO can be converted at 120 ℃. Similar results are also observed in the tests on MnOx-CeO/AC. The excellent low-temperature catalytic activity of modified Mn-based catalysts, which may be mainly due to the oxygen storage function of CeO, can improve the oxygen flow on the catalysts surface. Then the oxidation of NO to NO2 is accelerated, which is the key step of NO SCR.展开更多
A series of catalysts of Mn/USY and Mn-Fe/USY prepared by impregnation were studied for low-temperature selective catalytic reduction （SCR） of NO with NH3 in the presence of excess of oxygen. It was found that the a...A series of catalysts of Mn/USY and Mn-Fe/USY prepared by impregnation were studied for low-temperature selective catalytic reduction （SCR） of NO with NH3 in the presence of excess of oxygen. It was found that the addition of Fe enhanced the catalytic performance at low-temperature. Mn-Fe/USY catalyst yielded nearly 100% NO conversion in a range of temperature from 423 to 573 K at a space velocity of 36 000 cm3g^-1·h^-1. Coexistence of manganese and iron oxides enhanced the dispersion of the supported oxides, no visible phase of the oxides can be observed on catalyst. The addition of Fe enhanced the number and strength of the Bronsted and Lewis acid sites on the surface of the catalyst, which might promote the absorption of NH3 to form active intermediate and enhance the catalytic performance at low-temperature.展开更多
基金the Key Project of the National Natural Science Foundation of China (20437010)the Natural Science Foundation of Yunnan Province (2007E184M)the Science Foundation of the Education Department of Yunnan Province(07C11400)
文摘A series of Mn-based catalysts, MnOx, MnOx-CeO, Pd-Mn-Ce, MnOx/AC were prepared. And their performances for NO low-temperature SCR were investigated in this study. The NO conversion is about 90% at 100 ℃ on MnOx-CeOand almost all NO can be converted at 120 ℃. Similar results are also observed in the tests on MnOx-CeO/AC. The excellent low-temperature catalytic activity of modified Mn-based catalysts, which may be mainly due to the oxygen storage function of CeO, can improve the oxygen flow on the catalysts surface. Then the oxidation of NO to NO2 is accelerated, which is the key step of NO SCR.
基金This work was financially supported by the National Natural Science Foundation of China （No. 20437010） the Chinese Postdoctoral Science Foundation （No. 2005037058）.
文摘A series of catalysts of Mn/USY and Mn-Fe/USY prepared by impregnation were studied for low-temperature selective catalytic reduction （SCR） of NO with NH3 in the presence of excess of oxygen. It was found that the addition of Fe enhanced the catalytic performance at low-temperature. Mn-Fe/USY catalyst yielded nearly 100% NO conversion in a range of temperature from 423 to 573 K at a space velocity of 36 000 cm3g^-1·h^-1. Coexistence of manganese and iron oxides enhanced the dispersion of the supported oxides, no visible phase of the oxides can be observed on catalyst. The addition of Fe enhanced the number and strength of the Bronsted and Lewis acid sites on the surface of the catalyst, which might promote the absorption of NH3 to form active intermediate and enhance the catalytic performance at low-temperature.