Eu^(2+) and Mn^(2+) co-activated CaAlSiN_(3) red phosphors were produced using the solid-state reaction tech⁃nique in a N2 environment.Excitation spectra,emission spectra,and diffuse reflection spectra were used to st...Eu^(2+) and Mn^(2+) co-activated CaAlSiN_(3) red phosphors were produced using the solid-state reaction tech⁃nique in a N2 environment.Excitation spectra,emission spectra,and diffuse reflection spectra were used to study the luminescence characteristics,energy gap,and thermal stability in detail.CaAlSiN_(3)∶Eu^(2+) exhibits an extended emission band when stimulated with 450 nm blue light,which is caused by the 4f65d to 4f7 transition of Eu^(2+).Similar⁃ly,CaAlSiN_(3)∶Mn^(2+) displays a wide emission band centered at 628 nm,which results from Mn^(2+)’s transition from 4T1(4G) to 6A1(6S).When the ions of Mn^(2+)were combined into CaAlSiN_(3)∶Eu^(2+),the photoluminescence intensity of Eu^(2+ )was greatly boosted because there was energy transfer and co-emission between Mn^(2+) and Eu^(2+).Beyond that,CaAlSiN_(3)∶Eu^(2+),Mn^(2+) emerges with splendid thermostability and high quantum efficiency,the quenching temperature surpasses 300℃,and the internal quantum efficiency is determined to be around 84.9%.The white LED was pack⁃aged with a combination of CaAlSiN_(3)∶Eu^(2+),Mn^(2+),LuAG∶Ce3+ and a blue chip.At a warm white-light corresponding color temperature(3009 K) with CIE coordinates(0.4223,0.3748),the color rendering index Ra has reached 93.2.CaAlSiN_(3)∶Eu^(2+),Mn^(2+) would have great application potential as a red-emitting phosphor for white LEDs.展开更多
采用溶胶-凝胶法制备出Y_(2-2 x)MgTiO_(6)∶2 x Eu^(3+)(YMT∶2 x Eu^(3+),0≤x≤0.11)新型红色荧光粉。通过X射线衍射仪(XRD)检测样品的纯度,结果显示YMT∶Eu^(3+)样品属于单斜晶系,空间群为P21/n,无其他杂相。扫描电子显微镜(SEM)照...采用溶胶-凝胶法制备出Y_(2-2 x)MgTiO_(6)∶2 x Eu^(3+)(YMT∶2 x Eu^(3+),0≤x≤0.11)新型红色荧光粉。通过X射线衍射仪(XRD)检测样品的纯度,结果显示YMT∶Eu^(3+)样品属于单斜晶系,空间群为P21/n,无其他杂相。扫描电子显微镜(SEM)照片显示荧光粉为2μm的不规则颗粒。当激发波长为264 nm时,发射光谱出现四个尖锐的发射峰,分别位于591(^(5)D_(0)→^(7)F_(1))、619(^(5)D_(0)→^(7)F_(2))、657(^(5)D_(0)→^(7)F_(3))和693 nm(^(5)D_(0)→^(7)F_(4))。Eu^(3+)离子之间能量传递为电偶极子-电偶极子(d-d)相互作用。YMT∶0.14Eu^(3+)荧光粉的CIE色度坐标为(0.645,0.332),与红光标准色坐标(0.67,0.33)非常接近。变温PL光谱及热激活能计算结果显示荧光粉具有一定的热稳定性,因此YMT∶Eu^(3+)是一种具有潜在应用价值的LED红色荧光粉。展开更多
Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub&...Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.展开更多
文摘Eu^(2+) and Mn^(2+) co-activated CaAlSiN_(3) red phosphors were produced using the solid-state reaction tech⁃nique in a N2 environment.Excitation spectra,emission spectra,and diffuse reflection spectra were used to study the luminescence characteristics,energy gap,and thermal stability in detail.CaAlSiN_(3)∶Eu^(2+) exhibits an extended emission band when stimulated with 450 nm blue light,which is caused by the 4f65d to 4f7 transition of Eu^(2+).Similar⁃ly,CaAlSiN_(3)∶Mn^(2+) displays a wide emission band centered at 628 nm,which results from Mn^(2+)’s transition from 4T1(4G) to 6A1(6S).When the ions of Mn^(2+)were combined into CaAlSiN_(3)∶Eu^(2+),the photoluminescence intensity of Eu^(2+ )was greatly boosted because there was energy transfer and co-emission between Mn^(2+) and Eu^(2+).Beyond that,CaAlSiN_(3)∶Eu^(2+),Mn^(2+) emerges with splendid thermostability and high quantum efficiency,the quenching temperature surpasses 300℃,and the internal quantum efficiency is determined to be around 84.9%.The white LED was pack⁃aged with a combination of CaAlSiN_(3)∶Eu^(2+),Mn^(2+),LuAG∶Ce3+ and a blue chip.At a warm white-light corresponding color temperature(3009 K) with CIE coordinates(0.4223,0.3748),the color rendering index Ra has reached 93.2.CaAlSiN_(3)∶Eu^(2+),Mn^(2+) would have great application potential as a red-emitting phosphor for white LEDs.
文摘采用溶胶-凝胶法制备出Y_(2-2 x)MgTiO_(6)∶2 x Eu^(3+)(YMT∶2 x Eu^(3+),0≤x≤0.11)新型红色荧光粉。通过X射线衍射仪(XRD)检测样品的纯度,结果显示YMT∶Eu^(3+)样品属于单斜晶系,空间群为P21/n,无其他杂相。扫描电子显微镜(SEM)照片显示荧光粉为2μm的不规则颗粒。当激发波长为264 nm时,发射光谱出现四个尖锐的发射峰,分别位于591(^(5)D_(0)→^(7)F_(1))、619(^(5)D_(0)→^(7)F_(2))、657(^(5)D_(0)→^(7)F_(3))和693 nm(^(5)D_(0)→^(7)F_(4))。Eu^(3+)离子之间能量传递为电偶极子-电偶极子(d-d)相互作用。YMT∶0.14Eu^(3+)荧光粉的CIE色度坐标为(0.645,0.332),与红光标准色坐标(0.67,0.33)非常接近。变温PL光谱及热激活能计算结果显示荧光粉具有一定的热稳定性,因此YMT∶Eu^(3+)是一种具有潜在应用价值的LED红色荧光粉。
文摘Silane coupling agent KH560 was used to modify the surface of nano-α-Al<sub>2</sub>O<sub>3</sub> in ethanol-aqueous solution with different proportions. The particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> was determined by nano-particle size analyzer, and the effects of nano-α-Al<sub>2</sub>O<sub>3</sub> content, ethanol-aqueous solution ratio and KH560 dosage on the dispersion and particle size of nano-α-Al<sub>2</sub>O<sub>3</sub> were investigated. The material structure before and after modification was determined by Fourier transform infrared spectroscopy (FTIR). Aqueous polyurethane resin and inorganic components are combined with modified nano-α-Al<sub>2</sub>O<sub>3</sub> dispersion to form chromium-free passivation solution. The solution is coated on the galvanized sheet, the adhesion and surface hardness are tested, the bonding strength of the coating and the surface hardness of the substrate are discussed. The corrosion resistance and surface morphology of the matrix were investigated by electrochemical test, neutral salt spray test and scanning electron microscope test. The chromium-free passivation film formed after the modification of nano-α-Al<sub>2</sub>O<sub>3</sub> increases the surface hardness of galvanized sheet by about 85%. The corrosion resistance of the film is better than that of a single polyurethane film. The results show that the surface hardness and corrosion resistance of polyurethane resin composite passivation film are significantly improved by the introduction of nano-α-Al<sub>2</sub>O<sub>3</sub>.