The influence of microstructural characteristics on Lu¨ders strain and mechanical properties was explored by means of altering thermo-mechanical circumstances in an intercritical annealing(IA)medium-Mn Fe-11Mn-0....The influence of microstructural characteristics on Lu¨ders strain and mechanical properties was explored by means of altering thermo-mechanical circumstances in an intercritical annealing(IA)medium-Mn Fe-11Mn-0.09C-0.25Si(wt.%)steel.By IA of cold-rolled samples with severe plastic deformation,exclusively equiaxed dual phases were obtained because of active recovery and recrystallization.The equiaxed austenite(gamma E)with a larger size and inadequate chemical concentration was more readily transformed into martensite,and subsequent transformation-induced plasticity(TRIP)effect was triggered actively at relatively higher IA temperature,lessening localized deformation.In addition,grown-in dislocations were prone to multiply and migrate around a broad mean free path for coarser equiaxed ferrite(alpha E)due to weakening dynamic recovery;therefore,it was the ensuing increased mobility of dislocations instead of reserving plentiful initial dislocation density that facilitated the propagation velocity of Luders bands and the accumulation of work hardening.In contrast,the bimodal-grained microstructure with lath-like and equiaxed austenite(gamma L+gamma E)satisfactorily contributed to a smaller yield point elongation(YPE)without compromise of comprehensive mechanical properties on the grounds that austenitic gradient stability gave rise to discontinuous but sustainable TRIP effect and incremental work hardening.Hence,Luders strain is closely related to the absence of work hardening in the region which yields locally.It follows that the decreased stability of retained austenite,favorable mobility of dislocations and the bimodal-grained structure all prominently make up for the insufficiency of work hardening,thereof resulting in a limited YPE.展开更多
The Luders deformation behavior in a medium Mn transformation induced plasticity (TRIP) steel is investigated at different temperatures ranging from 25 to 300 ℃. It demonstrates that the Ltiders band appears at all...The Luders deformation behavior in a medium Mn transformation induced plasticity (TRIP) steel is investigated at different temperatures ranging from 25 to 300 ℃. It demonstrates that the Ltiders band appears at all testing temperatures but with varied Luders strains which do not change monoton ically with temperature. The martensitic transformation is simultaneously observed within the Ltiders band in varying degrees depending on the testing temperature. It is well verified that the martensitic transformation is not responsible for the formation of Luders band, and a reasonable explanation is given for the non-monotonic variation of Luders strain with increasing temperature.展开更多
基金the support of the National Key Research and Development Program of Thirteenth Five-Year Plan Period(Grant No.2017YFB0304400)the National Natural Science Foundation of China(Grant No.51574028).
文摘The influence of microstructural characteristics on Lu¨ders strain and mechanical properties was explored by means of altering thermo-mechanical circumstances in an intercritical annealing(IA)medium-Mn Fe-11Mn-0.09C-0.25Si(wt.%)steel.By IA of cold-rolled samples with severe plastic deformation,exclusively equiaxed dual phases were obtained because of active recovery and recrystallization.The equiaxed austenite(gamma E)with a larger size and inadequate chemical concentration was more readily transformed into martensite,and subsequent transformation-induced plasticity(TRIP)effect was triggered actively at relatively higher IA temperature,lessening localized deformation.In addition,grown-in dislocations were prone to multiply and migrate around a broad mean free path for coarser equiaxed ferrite(alpha E)due to weakening dynamic recovery;therefore,it was the ensuing increased mobility of dislocations instead of reserving plentiful initial dislocation density that facilitated the propagation velocity of Luders bands and the accumulation of work hardening.In contrast,the bimodal-grained microstructure with lath-like and equiaxed austenite(gamma L+gamma E)satisfactorily contributed to a smaller yield point elongation(YPE)without compromise of comprehensive mechanical properties on the grounds that austenitic gradient stability gave rise to discontinuous but sustainable TRIP effect and incremental work hardening.Hence,Luders strain is closely related to the absence of work hardening in the region which yields locally.It follows that the decreased stability of retained austenite,favorable mobility of dislocations and the bimodal-grained structure all prominently make up for the insufficiency of work hardening,thereof resulting in a limited YPE.
基金support from the Steel Joint Funds of the National Natural Science Foundation of China(Grant No.U1560204)Research Grants Council of Hong Kong(Grant Nos.HKU719712E,HKU712713E)Small Project Funding of HKU(Grant No.201409176053)
文摘The Luders deformation behavior in a medium Mn transformation induced plasticity (TRIP) steel is investigated at different temperatures ranging from 25 to 300 ℃. It demonstrates that the Ltiders band appears at all testing temperatures but with varied Luders strains which do not change monoton ically with temperature. The martensitic transformation is simultaneously observed within the Ltiders band in varying degrees depending on the testing temperature. It is well verified that the martensitic transformation is not responsible for the formation of Luders band, and a reasonable explanation is given for the non-monotonic variation of Luders strain with increasing temperature.