Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part i...Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part icles were characterized by powder X ray diffraction(XRD),thermal analysis(TGA DSC), infrared spectroscopy(FT IR),transmission electron microscopy(SEM) and scanning electron microscopy(TEM). The size distribution in whisker like and nanocrystalline materials arein the range of 10～50μm and 10～20nm respectively. The whisker MOS is metastable phase in MgSO4 NaOH H2O system at 140℃,whereas nanometer MOS is stable phase.展开更多
[ Objective] The aim was to study pretreatment of ultrasound enhancing dilute H2SO4 on cellulase activity of corn straw liquid fermentation and explore the pretretment＇ s optimal conditions. [ Method ] By using ortho...[ Objective] The aim was to study pretreatment of ultrasound enhancing dilute H2SO4 on cellulase activity of corn straw liquid fermentation and explore the pretretment＇ s optimal conditions. [ Method ] By using orthogonal test, the pretretment of ultrasound enhancing dilute H2SO4 on corn straw was studied, then straw was fermented as the sole carbon source. Finally, the cellulase activity in extracellular fermentation broth was determined. [Result] The results showed that cellulase activity in extracellular broth was greatest under the conditions of acid bath time 3 h, acid concentration 3.5%, ultrasonic power 150 W, and ultrasonic time 5 h. They were FPA 15.82 U/ml, Cx 39.9 U/ml, 13-Giu 55.94 U/ml respectively. [ Conclusion] Under the above conditions, extracellular cellulase production has a high stability.展开更多
Lithium-ion batteries(LIBs)featuring a Ni-rich cathode exhibit increased specific capacity,but the establishment of a stable interphase through the implementation of a functional electrolyte strategy remains challengi...Lithium-ion batteries(LIBs)featuring a Ni-rich cathode exhibit increased specific capacity,but the establishment of a stable interphase through the implementation of a functional electrolyte strategy remains challenging.Especially when the battery is operated under high temperature,the trace water present in the electrolyte will accelerate the hydrolysis of the electrolyte and the resulting HF will further erode the interphase.In order to enhance the long-term cycling performance of graphite/LiNi_(0.8)Co_(0.1)Mn_(0.1)O_(2)(NCM811)LIBs,herein,Tolylene-2,4-diisocyanate(TDI)additive containing lone-pair electrons is employed to formulate a novel bifunctional electrolyte aimed at eliminating H_(2)O/HF generated at elevated temperature.After 1000 cycles at 25℃,the battery incorporating the TDI-containing electrolyte exhibits an impressive capacity retention of 94%at 1 C.In contrast,the battery utilizing the blank electrolyte has a lower capacity retention of only 78%.Furthermore,after undergoing 550 cycles at 1 C under45℃,the inclusion of TDI results in a notable enhancement of capacity,increasing it from 68%to 80%.This indicates TDI has a favorable influence on the cycling performance of LIBs,especially at elevated temperatures.The analysis of the film formation mechanism suggests that the lone pair of electrons of the isocyanate group in TDI play a crucial role in inhibiting the generation of H_(2)O and HF,which leads to the formation of a thin and dense interphase.The existence of this interphase is thought to substantially enhance the cycling performance of the LIBs.This work not only improves the performance of graphite/NCM811 batteries at room temperature and high temperature by eliminating H_(2)O/HF but also presents a novel strategy for advancing functional electrolyte development.展开更多
文摘Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part icles were characterized by powder X ray diffraction(XRD),thermal analysis(TGA DSC), infrared spectroscopy(FT IR),transmission electron microscopy(SEM) and scanning electron microscopy(TEM). The size distribution in whisker like and nanocrystalline materials arein the range of 10～50μm and 10～20nm respectively. The whisker MOS is metastable phase in MgSO4 NaOH H2O system at 140℃,whereas nanometer MOS is stable phase.
基金Supported by the National Key Technology R&D Program during the11~(th)five-year Plan(2007BAD34B03)the Important Project of Ministryof Education(107127)Scientific Research Foundation ofHefei University of Technology(113-036404)~~
文摘[ Objective] The aim was to study pretreatment of ultrasound enhancing dilute H2SO4 on cellulase activity of corn straw liquid fermentation and explore the pretretment＇ s optimal conditions. [ Method ] By using orthogonal test, the pretretment of ultrasound enhancing dilute H2SO4 on corn straw was studied, then straw was fermented as the sole carbon source. Finally, the cellulase activity in extracellular fermentation broth was determined. [Result] The results showed that cellulase activity in extracellular broth was greatest under the conditions of acid bath time 3 h, acid concentration 3.5%, ultrasonic power 150 W, and ultrasonic time 5 h. They were FPA 15.82 U/ml, Cx 39.9 U/ml, 13-Giu 55.94 U/ml respectively. [ Conclusion] Under the above conditions, extracellular cellulase production has a high stability.
基金financially supported by the Scientific and Technological Plan Projects of Guangzhou City(202103040001),P.R.Chinathe Project of Science and Technology Department of Henan Province(222102240074)the Key Research Programs of Higher Education Institutions of Henan Province(24B150009)。
文摘Lithium-ion batteries(LIBs)featuring a Ni-rich cathode exhibit increased specific capacity,but the establishment of a stable interphase through the implementation of a functional electrolyte strategy remains challenging.Especially when the battery is operated under high temperature,the trace water present in the electrolyte will accelerate the hydrolysis of the electrolyte and the resulting HF will further erode the interphase.In order to enhance the long-term cycling performance of graphite/LiNi_(0.8)Co_(0.1)Mn_(0.1)O_(2)(NCM811)LIBs,herein,Tolylene-2,4-diisocyanate(TDI)additive containing lone-pair electrons is employed to formulate a novel bifunctional electrolyte aimed at eliminating H_(2)O/HF generated at elevated temperature.After 1000 cycles at 25℃,the battery incorporating the TDI-containing electrolyte exhibits an impressive capacity retention of 94%at 1 C.In contrast,the battery utilizing the blank electrolyte has a lower capacity retention of only 78%.Furthermore,after undergoing 550 cycles at 1 C under45℃,the inclusion of TDI results in a notable enhancement of capacity,increasing it from 68%to 80%.This indicates TDI has a favorable influence on the cycling performance of LIBs,especially at elevated temperatures.The analysis of the film formation mechanism suggests that the lone pair of electrons of the isocyanate group in TDI play a crucial role in inhibiting the generation of H_(2)O and HF,which leads to the formation of a thin and dense interphase.The existence of this interphase is thought to substantially enhance the cycling performance of the LIBs.This work not only improves the performance of graphite/NCM811 batteries at room temperature and high temperature by eliminating H_(2)O/HF but also presents a novel strategy for advancing functional electrolyte development.
基金Supported by the Natural Science Foundation of Hunan Province(0 0 JJY2 0 1 1 0 ) and Scientific Re-search Fund of Hunan Provincial Education Department(0 1 C0 2 2