利用超细旋转盘式砂磨机细化颗粒固相烧结法,合成锂离子电池正极材料Li Ni0.80Co0.15Al0.05O2。原料经过砂磨后,混合均匀,粒径达到纳米级。根据塔曼定理,混合均匀的微小粒径可以在相同的烧结温度下,提高烧结的强度。SEM、XRD分别表征NC...利用超细旋转盘式砂磨机细化颗粒固相烧结法,合成锂离子电池正极材料Li Ni0.80Co0.15Al0.05O2。原料经过砂磨后,混合均匀,粒径达到纳米级。根据塔曼定理,混合均匀的微小粒径可以在相同的烧结温度下,提高烧结的强度。SEM、XRD分别表征NCA材料的颗粒形貌和晶形结构。结果显示,通过细化颗粒烧结后的样品具有良好的形貌和层状结构。CV法测试样品的氧化还原性能,电池测试系统测试样品的电化学性能。测试结果显示,经过细化颗粒,在720℃合成的NCA材料具有良好的层状结构,018/110峰分裂明显。样品的电化学性能优良,0.2C下,首次放电容量达到182 m Ah?g?1,30次循环后容量保持率99.9%。1C下,首次放电容量153 m Ah?g?1,100次循环后容量保持率92.6%。展开更多
LiNi1-xCoxO2 cathode materials for lithium ion batteries were synthesized by the co-precipitation and solid-state reaction methods with LiOH·H2O, Ni(NO3)2·6H2O and Co(NO3)2·6H2O as raw materials. The ma...LiNi1-xCoxO2 cathode materials for lithium ion batteries were synthesized by the co-precipitation and solid-state reaction methods with LiOH·H2O, Ni(NO3)2·6H2O and Co(NO3)2·6H2O as raw materials. The materials were characterized by XRD, SEM and electrochemical tests. The results showed that synthesized cathode materials were with layered structure similar to α-NaFeO2 and uniform morphology and nearly normal grain size distribution and better electrochemical performance when x was 0.18. The first charge and discharge capacity of the cathode material was 224.3 mAh·g-1 and 194.2 mAh·g-1, respectively. 88.5% of the first discharge capacity remained at the 20th cycle.展开更多
采用改进的碳酸盐共沉淀与高温固相法相结合的方法制备出了高倍率性能的锂离子电池正极材料Li[Ni1/3Co1/3Mn1/3]O2,通过X射线衍射(XRD)、扫描电镜(SEM)、循环伏安扫描(CV)、电化学阻抗谱(EIS)和电化学性能测试等手段对材料进行表征.结...采用改进的碳酸盐共沉淀与高温固相法相结合的方法制备出了高倍率性能的锂离子电池正极材料Li[Ni1/3Co1/3Mn1/3]O2,通过X射线衍射(XRD)、扫描电镜(SEM)、循环伏安扫描(CV)、电化学阻抗谱(EIS)和电化学性能测试等手段对材料进行表征.结果表明,该方法制备的材料具有良好的α-Na Fe O2型层状结构(R3m(166)),一次粒径平均大小为157 nm,二次颗粒成球形.同传统碳酸盐制备得到的材料相比,该材料具备良好的倍率性能和循环性能,在2.7-4.3 V电压范围内,0.1C(1.0C=180 m A?g-1)倍率下,首次放电比容量为156.4m Ah?g-1,库仑效率为81.9%.在较高倍率下,即0.5C、5.0C和20C时,其放电比容量分别为136.9、111.3、81.3m Ah?g-1.在1C倍率下100次循环容量保持率为92.9%,高于传统共沉淀法得到的材料(87.0%).展开更多
文摘利用超细旋转盘式砂磨机细化颗粒固相烧结法,合成锂离子电池正极材料Li Ni0.80Co0.15Al0.05O2。原料经过砂磨后,混合均匀,粒径达到纳米级。根据塔曼定理,混合均匀的微小粒径可以在相同的烧结温度下,提高烧结的强度。SEM、XRD分别表征NCA材料的颗粒形貌和晶形结构。结果显示,通过细化颗粒烧结后的样品具有良好的形貌和层状结构。CV法测试样品的氧化还原性能,电池测试系统测试样品的电化学性能。测试结果显示,经过细化颗粒,在720℃合成的NCA材料具有良好的层状结构,018/110峰分裂明显。样品的电化学性能优良,0.2C下,首次放电容量达到182 m Ah?g?1,30次循环后容量保持率99.9%。1C下,首次放电容量153 m Ah?g?1,100次循环后容量保持率92.6%。
文摘LiNi1-xCoxO2 cathode materials for lithium ion batteries were synthesized by the co-precipitation and solid-state reaction methods with LiOH·H2O, Ni(NO3)2·6H2O and Co(NO3)2·6H2O as raw materials. The materials were characterized by XRD, SEM and electrochemical tests. The results showed that synthesized cathode materials were with layered structure similar to α-NaFeO2 and uniform morphology and nearly normal grain size distribution and better electrochemical performance when x was 0.18. The first charge and discharge capacity of the cathode material was 224.3 mAh·g-1 and 194.2 mAh·g-1, respectively. 88.5% of the first discharge capacity remained at the 20th cycle.
文摘采用改进的碳酸盐共沉淀与高温固相法相结合的方法制备出了高倍率性能的锂离子电池正极材料Li[Ni1/3Co1/3Mn1/3]O2,通过X射线衍射(XRD)、扫描电镜(SEM)、循环伏安扫描(CV)、电化学阻抗谱(EIS)和电化学性能测试等手段对材料进行表征.结果表明,该方法制备的材料具有良好的α-Na Fe O2型层状结构(R3m(166)),一次粒径平均大小为157 nm,二次颗粒成球形.同传统碳酸盐制备得到的材料相比,该材料具备良好的倍率性能和循环性能,在2.7-4.3 V电压范围内,0.1C(1.0C=180 m A?g-1)倍率下,首次放电比容量为156.4m Ah?g-1,库仑效率为81.9%.在较高倍率下,即0.5C、5.0C和20C时,其放电比容量分别为136.9、111.3、81.3m Ah?g-1.在1C倍率下100次循环容量保持率为92.9%,高于传统共沉淀法得到的材料(87.0%).