Magnesium(Mg)alloy stents are expected to be the next generation of stents because of good biocompatibility and biodegradability.Compared with cold drawing,dieless drawing with local heating is an effective method for...Magnesium(Mg)alloy stents are expected to be the next generation of stents because of good biocompatibility and biodegradability.Compared with cold drawing,dieless drawing with local heating is an effective method for manufacturing the Mg alloy microtubes since a large reduction in area can be achieved in a single pass.However,the microstructure and properties of dieless drawn tubes have not been clarified,leading to the problems in practical application of dieless drawn tubes.In this study,the microstructure and performance of dieless drawn tubes are clarified.The results show that temperature and speed in the dieless drawing process are two factors in determining the grain size of dieless drawn tubes since decreasing the temperature or increasing the speed promotes the generation of fine-grained microstructure.Twins are also generated during the dieless drawing process,which 1)disintegrates grains leading to refinement and 2)causes Hall-Petch law effect on dieless drawn tubes.Tensile tests show that grain size is the main factor in determining the mechanical properties of dieless drawn tubes,namely,0.2%proof stress 135-180MPa,ultimate tensile strength(UTS)200-250MPa,and elongation 8-12%.In 0.9 wt%NaCl solution,localized corrosion is the key factor in initiating the corrosion of dieless drawn tubes,but refined grains and fewer twins can alleviate local corrosion.These results imply that dieless drawn tubes are promising in the clinical application of Mg alloy stents for cardiovascular disease.展开更多
In tube hydroforming with axial feeding,under the effect of coupled internal pressure and axial stress,wrinkles often occur and affect the forming results.Wrinkling behavior of an AZ31B magnesium alloy tube was experi...In tube hydroforming with axial feeding,under the effect of coupled internal pressure and axial stress,wrinkles often occur and affect the forming results.Wrinkling behavior of an AZ31B magnesium alloy tube was experimentally investigated with different loading paths at different temperatures.Features of wrinkles,including shape,radius and width,were acquired from the experiments,as well as the thickness distribution.Numerical simulations were carried out to reveal the stress state during warm hydroforming,and then the strain history of material at the top and bottom of the wrinkles were analyzed according to the stress tracks and yielding ellipse.Finally,effects of loading paths on expansion ratio limit of warm hydroforming were analyzed.It is verified that at a certain temperature,expansion ratio limit can be increased obviously by applying a proper loading path and realizing enough axial feeding.展开更多
基金JSTP KAKENHI Grant Number 19H02476JKA and its promotion funds from KEIRIN RACE.Peihua Du thanks China Scholarship Council for the award of fellowship and funding(No.201707040058).
文摘Magnesium(Mg)alloy stents are expected to be the next generation of stents because of good biocompatibility and biodegradability.Compared with cold drawing,dieless drawing with local heating is an effective method for manufacturing the Mg alloy microtubes since a large reduction in area can be achieved in a single pass.However,the microstructure and properties of dieless drawn tubes have not been clarified,leading to the problems in practical application of dieless drawn tubes.In this study,the microstructure and performance of dieless drawn tubes are clarified.The results show that temperature and speed in the dieless drawing process are two factors in determining the grain size of dieless drawn tubes since decreasing the temperature or increasing the speed promotes the generation of fine-grained microstructure.Twins are also generated during the dieless drawing process,which 1)disintegrates grains leading to refinement and 2)causes Hall-Petch law effect on dieless drawn tubes.Tensile tests show that grain size is the main factor in determining the mechanical properties of dieless drawn tubes,namely,0.2%proof stress 135-180MPa,ultimate tensile strength(UTS)200-250MPa,and elongation 8-12%.In 0.9 wt%NaCl solution,localized corrosion is the key factor in initiating the corrosion of dieless drawn tubes,but refined grains and fewer twins can alleviate local corrosion.These results imply that dieless drawn tubes are promising in the clinical application of Mg alloy stents for cardiovascular disease.
基金Project(NCET-07-0237)supported by the Program for New Century Excellent Talents in University,China
文摘In tube hydroforming with axial feeding,under the effect of coupled internal pressure and axial stress,wrinkles often occur and affect the forming results.Wrinkling behavior of an AZ31B magnesium alloy tube was experimentally investigated with different loading paths at different temperatures.Features of wrinkles,including shape,radius and width,were acquired from the experiments,as well as the thickness distribution.Numerical simulations were carried out to reveal the stress state during warm hydroforming,and then the strain history of material at the top and bottom of the wrinkles were analyzed according to the stress tracks and yielding ellipse.Finally,effects of loading paths on expansion ratio limit of warm hydroforming were analyzed.It is verified that at a certain temperature,expansion ratio limit can be increased obviously by applying a proper loading path and realizing enough axial feeding.