Utilization of nickel slag using selective reduction followed by magnetic separation 被引量:14
1
作者 潘建 郑国林 +1 位作者 朱德庆 周仙霖 《Transactions of Nonferrous Metals Society of China》 SCIE EI CAS CSCD 2013年第11期3421-3427,共7页
In order to utilize slag discarded by nickel plants, the selective recovery of nickel and copper versus iron was investigated by selective reduction, which was achieved by controlling the reduction parameters and magn... In order to utilize slag discarded by nickel plants, the selective recovery of nickel and copper versus iron was investigated by selective reduction, which was achieved by controlling the reduction parameters and magnetic separation process on bench scale. The results show that increasing the basicity (mass ratio of CaO to SIO2) of nickel slag facilitates the enrichment of nickel and copper The process parameters for selective reduction were optimized as follows: basicity of 0.15, reducing at 1200 ~C for 20 min, 5% coal on a dried slag mass base. The grinding-magnetic separation results of reduced briquettes show that concentrate containing 3.25%Ni, 1.20%Cu and 75.26%Fe is obtained and selective enrichment is achieved with a recovery of 82.20%, 80.00% for nickel and copper respectively, while the recovery of iron is only 42.17%. The S and P contents are not reduced obviously and further research may be needed to examine the behaviors of S and P in the process. 展开更多
关键词 nickel slag selective reduction magnetic separation
下载PDF
Enhancement of pentlandite surface magnetism and implications for its separation from serpentine via magnetic separation 被引量:3
2
作者 袁致涛 卢冀伟 +2 位作者 刘炯天 李丽匣 王双玉 《Transactions of Nonferrous Metals Society of China》 SCIE EI CAS CSCD 2017年第1期204-210,共7页
The magnetism of pentlandite surface was enhanced through the selective precipitation of micro-fine magnetite fractions on pentlandite surfaces. This was achieved through adjustment of slurry pH and addition of surfac... The magnetism of pentlandite surface was enhanced through the selective precipitation of micro-fine magnetite fractions on pentlandite surfaces. This was achieved through adjustment of slurry pH and addition of surfactants. The results showed that at pH 8.8 with the addition of 100 g/t sodium hexametaphosphate, 4.5 L/t oleic acid, and 4.5 L/t kerosene, significant amount of fine magnetite particles adhered to the pentlandite surface, while trace amount of coating was found on serpentine surfaces. Thus, the magnetism of pentlandite was enhanced and pentlandite was well separated from serpentine by magnetic separation under the magnetic field intensity of 200 kA/m. Scanning electron microscopy (SEM) and zeta potential measurement were performed to characterize changes of mineral surface properties. Calculations of the extended Derjaguin-Landau-Verwey-Ocerbeek (EDLVO) theory indicated that, in the presence of surfactants the total interaction energy between magnetite and pentlandite became stronger than that between magnetite and serpentine. This enabled the selective adhesion of magnetite particles to pentlandite surfaces, thereby enhancing its magnetism. 展开更多
关键词 PENTLANDITE SERPENTINE micro-fine magnetite magnetic separation selective magnetic coating
下载PDF
Behaviors of vanadium and chromium in coal-based direct reduction of high-chromium vanadium-bearing titanomagnetite concentrates followed by magnetic separation 被引量:4
3
作者 赵龙胜 王丽娜 +3 位作者 陈德胜 赵宏欣 刘亚辉 齐涛 《Transactions of Nonferrous Metals Society of China》 SCIE EI CAS CSCD 2015年第4期1325-1333,共9页
The reduction behaviors of FeO·V2O3 and FeO·Cr2O3 during coal-based direct reduction have a decisive impact on the efficient utilization of high-chromium vanadium-bearing titanomagnetite concentrates. The ef... The reduction behaviors of FeO·V2O3 and FeO·Cr2O3 during coal-based direct reduction have a decisive impact on the efficient utilization of high-chromium vanadium-bearing titanomagnetite concentrates. The effects of molar ratio of C to Fe n(C)/n(Fe) and temperature on the behaviors of vanadium and chromium during direct reduction and magnetic separation were investigated. The reduced samples were characterized by X-ray diffraction(XRD), scanning election microscopy(SEM) and energy dispersive spectrometry(EDS) techniques. Experimental results indicate that the recoveries of vanadium and chromium rapidly increase from 10.0% and 9.6% to 45.3% and 74.3%, respectively, as the n(C)/n(Fe) increases from 0.8 to 1.4. At n(C)/n(Fe) of 0.8, the recoveries of vanadium and chromium are always lower than 10.0% in the whole temperature range of 1100-1250 °C. However, at n(C)/n(Fe) of 1.2, the recoveries of vanadium and chromium considerably increase from 17.8% and 33.8% to 42.4% and 76.0%, respectively, as the temperature increases from 1100 °C to 1250 °C. At n(C)/n(Fe) lower than 0.8, most of the FeO·V2O3 and FeO·Cr2O3 are not reduced to carbides because of the lack of carbonaceous reductants, and the temperature has little effect on the reduction behaviors of FeO·V2O3 and FeO·Cr2O3, resulting in very low recoveries of vanadium and chromium during magnetic separation. However, at higher n(C)/n(Fe), the reduction rates of FeO·V2O3 and FeO·Cr2O3 increase significatly because of the excess amount of carbonaceous reductants. Moreover, higher temperatures largely induce the reduction of FeO·V2O3 and FeO·Cr2O3 to carbides. The newly formed carbides are then dissolved in the γ(FCC) phase, and recovered accompanied with the metallic iron during magnetic separation. 展开更多
关键词 high-chromium vanadium-bearing titanomagnetite concentrates coal-based direct reduction magnetic separation reduction behavior VANADIUM CHROMIUM
下载PDF
Recovery of iron from waste ferrous sulphate by co-precipitation and magnetic separation 被引量:6
4
作者 余旺 彭映林 郑雅杰 《Transactions of Nonferrous Metals Society of China》 SCIE EI CAS CSCD 2017年第1期211-219,共9页
Magnetite concentrate was recovered from ferrous sulphate by co-precipitation and magnetic separation. In co-precipitation process, the effects of reaction conditions on iron recovery were studied, and the optimal rea... Magnetite concentrate was recovered from ferrous sulphate by co-precipitation and magnetic separation. In co-precipitation process, the effects of reaction conditions on iron recovery were studied, and the optimal reaction parameters are proposed as follows: n(CaO)/n(Fe2+) 1.4:1, reaction temperature 80 ℃, ferrous ion concentration 0.4 mol/L, and the final mole ratio of Fe3+ to FJ+ in the reaction solution 1.9-2.1. In magnetic separation process, the effects of milling time and magnetic induction intensity on iron recovery were investigated. Wet milling played an important part in breaking the encapsulated magnetic phases. The results showed that the mixed product was wet-milled for 20 min before magnetic separation, the grade and recovery rate of iron in magnetite concentrate were increased from 51.41% and 84.15% to 62.05% and 85.35%, respectively. 展开更多
关键词 ferrous sulphate titanium dioxide magnetite concentrate CO-PRECIPITATION wet milling magnetic separation
下载PDF
Study on Optimizing High-Gradient Magnetic Separation—Part 1: Improvement of Magnetic Particle Retention Based on CFD Simulations
5
作者 Yonas S. Shaikh Christian Seibert Percy Kampeis 《World Journal of Condensed Matter Physics》 CAS 2016年第2期123-136,共14页
The introduction of functionalized magnetizable particles for the purification of enzymes or for the multi-use of pre-immobilized biocatalysts offers a great potential for time and cost savings in biotechnological pro... The introduction of functionalized magnetizable particles for the purification of enzymes or for the multi-use of pre-immobilized biocatalysts offers a great potential for time and cost savings in biotechnological process design. The selective separation of the magnetizable particles is performed for example by a high-gradient magnetic separator. In this study FEM and CFD simulations of the magnetic field and the fluid flow field within a filter chamber of a magnetic separator were carried out, to find an optimal separator design. The motion of virtual magnetizable particles was calculated with a one-way coupled Lagrangian approach in order to test many geometric and parametric variations in reduced time. It was found that a flow homogenisator smoothed the fluid flow, so that the linear velocity became nearly equal over the cross section in the direction of flow. Furthermore the retention of magnetizable particles increases with a high total edge length within the filter matrix. 展开更多
关键词 Computational Fluid Dynamics Finite Element Method magnetic Particles High-Gradient magnetic Separator magnetic filtration BIOCATALYSIS Enzyme Purification
下载PDF
Study on Optimizing High-Gradient Magnetic Separation—Part 2: Experimental Evaluation of the Performance of a New Designed Magnetic Filter
6
作者 Yonas S. Shaikh Christian Seibert Percy Kampeis 《World Journal of Condensed Matter Physics》 CAS 2016年第2期137-151,共15页
The introduction of functionalized magnetizable particles and high-gradient magnetic separation represents a time and money saving alternative to conventional purification and separation unit operations in the biotech... The introduction of functionalized magnetizable particles and high-gradient magnetic separation represents a time and money saving alternative to conventional purification and separation unit operations in the biotechnical sector. This technique has some advantages especially for the recycling of immobilized enzymes. A new magnetic filter with sight glasses was constructed and produced to study the performance of high-gradient magnetic separation at varied parameters. By optical analysis the buildup of a clogging was identified as the major parameter which affected the separation performance. For the cleaning procedure, a two-phase flow of water with highly dispersed air bubbles was tested which led to a nearly complete cleaning of the filter chamber. 展开更多
关键词 magnetic Particles magnetic filtration High-Gradient magnetic separation ENZYME BIOCATALYSIS
下载PDF
Recovery of iron from high phosphorus oolitic iron ore using coal-based reduction followed by magnetic separation 被引量:44
7
作者 Yong-sheng Sun Yue-xin Han +2 位作者 Peng Gao Ze-hong Wang Duo-zhen Ren 《International Journal of Minerals,Metallurgy and Materials》 SCIE EI CAS CSCD 2013年第5期411-419,共9页
Oolitic iron ore is one of the most important iron resources. This paper reports the recovery of iron from high phosphorus oolitic iron ore using coal-based reduction and magnetic separation. The influences of reducti... Oolitic iron ore is one of the most important iron resources. This paper reports the recovery of iron from high phosphorus oolitic iron ore using coal-based reduction and magnetic separation. The influences of reduction temperature, reduction time, C/O mole ratio, and CaO content on the metallization degree and iron recovery were investigated in detail. Experimental results show that reduced products with the metallization degree of 95.82% could be produced under the optimal conditions (i.e., reduction temperature, 1250℃; reduction time, 50 min; C/O mole ratio, 2.0; and CaO content, 10wt%). The magnetic concentrate containing 89.63wt% Fe with the iron recovery of 96.21% was obtained. According to the mineralogical and morphologic analysis, the iron minerals had been reduced and iron was mainly enriched into the metallic iron phase embedded in the slag matrix in the form of spherical particles. Apatite was also reduced to phosphorus, which partially migrated into the metallic iron phase. 展开更多
关键词 oolitic iron ore iron ore reduction magnetic separation PHOSPHORUS
下载PDF
Metalizing reduction and magnetic separation of vanadium titano-magnetite based on hot briquetting 被引量:10
8
作者 Shuang-yin Chen Man-sheng Chu 《International Journal of Minerals,Metallurgy and Materials》 SCIE EI CAS CSCD 2014年第3期225-233,共9页
To achieve high efficiency utilization of Panzhihua vanadium titano-magnetite, a new process of metalizing reduction and magnetic separation based on hot briquetting is proposed, and factors that affect the cold stren... To achieve high efficiency utilization of Panzhihua vanadium titano-magnetite, a new process of metalizing reduction and magnetic separation based on hot briquetting is proposed, and factors that affect the cold strength of the hot-briquetting products and the efficiency of reduction and magnetic separation are successively investigated through laboratory experiments. The relevant mechanisms are elucidated on the basis of microstructural observations. Experimental results show that the optimal process parameters for hot briquetting include a hot briquetting temperature of 475°C, a carbon ratio of 1.2, ore and coal particle sizes of less than 74 μm. Additionally, with respect to metalizing reduction and magnetic separation, the rational parameters include a magnetic field intensity of 50 mT, a reduction temperature of 1350°C, a reduction time of 60 min, and a carbon ratio of 1.2. Under these above conditions, the crushing strength of the hot-briquetting agglomerates is 1480 N, and the recovery ratios of iron, vanadium, and titanium are as high as 91.19%, 61.82%, and 85.31%, respectively. The new process of metalizing reduction and magnetic separation based on hot briquetting demonstrates the evident technological advantages of high efficiency separation of iron from other valuable elements in the vanadium titano-magnetite. 展开更多
关键词 MAGNETITE hot briquetting ore reduction magnetic separation
下载PDF
Efficient enrichment of nickel and iron in laterite nickel ore by deep reduction and magnetic separation 被引量:19
9
作者 Shuai YUAN Wen-tao ZHOU +1 位作者 Yan-jun LI Yue-xin HAN 《Transactions of Nonferrous Metals Society of China》 SCIE EI CAS CSCD 2020年第3期812-822,共11页
The process of deep reduction and magnetic separation was proposed to enrich nickel and iron from laterite nickel ores.Results show that nickel-iron concentrates with nickel grade of 6.96%,nickel recovery of 94.06%,ir... The process of deep reduction and magnetic separation was proposed to enrich nickel and iron from laterite nickel ores.Results show that nickel-iron concentrates with nickel grade of 6.96%,nickel recovery of 94.06%,iron grade of 34.74%,and iron recovery of 80.44% could be obtained after magnetic separation under the conditions of reduction temperature of 1275℃,reduction time of 50 min,slag basicity of 1.0,carbon-containing coefficient of 2.5,and magnetic field strength of 72 kA/m.Reduction temperature and time affected the possibility of deep reduction and reaction progress.Slag basicity affected the composition of slag in burden and the spilling and enriching rate of nickel-iron from a matrix to form nickel-iron particles.Nickel-iron particles were generated,aggregated,and grew gradually in the reduction process.Nickel-iron particles can be effectively separated from gangue minerals by magnetic separation. 展开更多
关键词 laterite nickel ore deep reduction magnetic separation nickel-iron concentrate reduction mechanism
下载PDF
Effect of desliming on the magnetic separation of low-grade ferruginous manganese ore 被引量:7
10
作者 Sunil Kumar Tripathy P.K.Banerjee Nikkam Suresh 《International Journal of Minerals,Metallurgy and Materials》 SCIE EI CAS CSCD 2015年第7期661-673,共13页
In the present investigation, magnetic separation studies using an induced roll magnetic separator were conducted to beneficiate low-grade ferruginous manganese ore. The feed ore was assayed to contain 22.4% Mn and 35... In the present investigation, magnetic separation studies using an induced roll magnetic separator were conducted to beneficiate low-grade ferruginous manganese ore. The feed ore was assayed to contain 22.4% Mn and 35.9% SiO2, with a manganese-to-iron mass ratio (Mn:Fe ratio) of 1.6. This ore was characterized in detail using different techniques, including quantitative evaluation of minerals by scan- ning electron microscopy, which revealed that the ore is extremely siliceous in nature and that the associated gangue minerals are more or less evenly distributed in almost all of the size fractions in major proportion. Magnetic separation studies were conducted on both the as-received ore fines and the classified fines to enrich their manganese content and Mn:Fe ratio. The results indicated that the efficiency of separation for deslimed fines was better than that for the treated unclassified bulk sample. On the basis of these results, we proposed a proc- ess flow sheet for the beneficiation of low-grade manganese ore fines using a Floatex density separator as a pre-concentrator followed by two-stage magnetic separation. The overall recovery of manganese in the final product from the proposed flow sheet is 44.7% with an assay value of 45.8% and the Mn:Fe ratio of 3.1. 展开更多
关键词 manganese ore treatment MINERALOGY BENEFICIATION magnetic separation flow sheet analysis
下载PDF
Effect of reverse flotation on magnetic separation concentrates 被引量:5
11
作者 S.O. Bada A.S. Afolabi M.J. Makhula 《International Journal of Minerals,Metallurgy and Materials》 SCIE EI CAS CSCD 2012年第8期669-674,共6页
Reverse flotation studies on magnetite samples have revealed that the use of starch as a depressant of Fe-oxides has a hydrophilic effect on the surface of Fe-bearing silicates and significantly decreases Fe in the si... Reverse flotation studies on magnetite samples have revealed that the use of starch as a depressant of Fe-oxides has a hydrophilic effect on the surface of Fe-bearing silicates and significantly decreases Fe in the silica-rich stream when used in combination with an amine (Lilaflot D817M). In this study, the effect of reverse flotation on the optimization of products obtained fi'om magnetic separation was inves- tigated. Two different magnetic samples, zones 1 and 2, were milled to 〈75 btm and then subjected to low intensity magnetic separation (LIMS). The LIMS test conducted on the 〈75 ~m shown an upgrade of 46.40wt% Fe, 28.40wt% SiO2 and 2.61wt% MnO for zone 1 and 47.60wt% Fe, 29.17wt% SiO2 and 0.50wt% MnO for zone 2. Further milling of the ore to 〈25 ~tm resulted in a higher magnetic-rich product after magnetic separation. Reverse flotation tests were conducted on the agitated magnetic concentrate feed, and the result shows a significant upgrade of Fe compared to that obtained from the non-agitated feed. Iron concentrations greater than 69%, and SiO2 concentrations less than 2% with overall magnetite recoveries greater than 67% and 71% were obtained for zones 1 and 2, respectively. 展开更多
关键词 MAGNETITE FLOTATION magnetic separation STARCH AMINES
下载PDF
Incorporating the magnetic alignment of GO composites into Pebax matrix for gas separation 被引量:5
12
作者 Weifang Zhu Yun Qin +3 位作者 Zhongming Wang Jianshu Zhang Ruili Guo Xueqin Li 《Journal of Energy Chemistry》 SCIE EI CAS CSCD 2019年第4期1-10,共10页
The mixed matrix membranes(MMMs) were developed by incorporating graphite oxide(GO) flakes functionalized with iron oxide(Fe_3O_4) into Pebax matrix. The Pebax/Fe_3O_4–GO MMMs were used to separate CO_2/CH_4 and CO_2... The mixed matrix membranes(MMMs) were developed by incorporating graphite oxide(GO) flakes functionalized with iron oxide(Fe_3O_4) into Pebax matrix. The Pebax/Fe_3O_4–GO MMMs were used to separate CO_2/CH_4 and CO_2/N_2 gas mixture. The results showed that the MMMs with magnetic alignment presented the better gas separation performance than that of random arrangement of Pebax/Fe_3O_4–GO mixed matrix membranes. The reason was that the Fe_3O_4–GO flakes arranged magnetically in the membrane played a multiple role in improving the performance of MMMs. Firstly, under the action of the magnetic field,the magnetic alignment of Fe_3O_4–GO flakes in Pebax matrix constructed the shorter transfer path for gas molecule, increasing the CO_2 permeability. Secondly, the hydroxyl groups in GO flakes and the presence of Fe_3O_4 have stronger binding force for water, improving the CO_2 solubility selectivity. Thirdly, the better interaction between the magnetic alignment of GO composites and polymer matrix, reduced the interface defects. Especially, the optimum gas separation performance was obtained at the Fe_3O_4–GO flakes content of 3 wt% in Pebax matrix at vertical arrangement with selectivity of 47 and 75 for CO_2/CH_4 and CO_2/N_2, respectively, and CO_2 permeability of 538 Barrer at 0.2 MPa and room temperature. 展开更多
关键词 CO2 separation The mixed MATRIX membranes Fe3O4–GO FLAKES CO2 PERMEABILITY magnetic alignment
下载PDF
Preparation of ferronickel from nickel laterite via coal-based reduction followed by magnetic separation 被引量:6
13
作者 Lun-wei Wang Xue-ming +3 位作者 Mei Liu Zhi-xiong You Xue-wei Chen-guang Bai 《International Journal of Minerals,Metallurgy and Materials》 SCIE EI CAS CSCD 2018年第7期744-751,共8页
The sticking phenomenon between molten slag and refractory is one of the crucial problems when preparing ferronickel from laterite ore using rotary hearth fulnace or rotary kiln processes. This study aims to ameliorat... The sticking phenomenon between molten slag and refractory is one of the crucial problems when preparing ferronickel from laterite ore using rotary hearth fulnace or rotary kiln processes. This study aims to ameliorate sticking problems by using silicon dioxide (SiO2) to adjust the melting degree of file briquette during reduction roasting. Thermodynamic analysis indicates that the melting temperature of the slag gradually increases with an increase in the SiO2 proportion (SiO2/(SiO2 + A1203 + MgO) mass ratio). Experimental validations also prove that the briquette retains its original shape when the SiO2 proportion is greater than 75wt%, and sticking problems axe avoided during reduction. A ferronickel product with 8.33wt% Ni and 84.71wt% Fe was prepared via reductive roasting at 1500~C for 90 min with a SiO2 proportion of 75wt% and a C/O molar ratio of 1.0 followed by dry magnetic separation; the corresponding recoveries of Ni and Fe reached 75.70% and 77.97%, respectively. The micro stxucture and phase txmlsformation of reduced briquette reveals that the aggregation and growth of ferroinckel particles were not significantly affected after adding SiO2 to the reduction process. 展开更多
关键词 nickel laterite caxbot^ermal reduction FERRONICKEL magnetic separation
下载PDF
Carbothermic reduction characteristics of ludwigite and boron–iron magnetic separation 被引量:3
14
作者 Guang Wang Qing-guo Xue Jing-song Wang 《International Journal of Minerals,Metallurgy and Materials》 SCIE EI CAS CSCD 2018年第9期1000-1009,共10页
Ludwigite is a kind of complex iron ore containing boron, iron, and magnesium, and it is the most promising boron resource in China. Selective reduction of iron oxide is the key step for the comprehensive utilization ... Ludwigite is a kind of complex iron ore containing boron, iron, and magnesium, and it is the most promising boron resource in China. Selective reduction of iron oxide is the key step for the comprehensive utilization of ludwigite. In the present work, the reduction mechanism of ludwigite was investigated. The thermogravimetry and differential scanning calorimetry analysis and isothermal reduction of ludwigite/coal composite pellet were performed. Ludwigite yielded a lower reduction starting temperature and a higher final reduction degree compared with the traditional iron concentrates. Higher specific surface area and more fine cracks might be the main reasons for the better reducibility of ludwigite. Reducing temperature highly affected the reaction fraction and microstructure of the reduced pellets, which are closely related to the separation degree of boron and iron. Increasing reducing temperature benefited the boron and iron magnetic separation. Optimum magnetic separation results could be obtained when the pellet was reduced at 1300°C. The separated boron-rich non-magnetic concentrate presented poor crystalline structure, and its extraction efficiency for boron reached 64.3%. The obtained experimental results can provide reference for the determination of the comprehensive utilization flow sheet of ludwigite. 展开更多
关键词 complex IRON ORE BORON RESOURCE carbothermic reduction magnetic separation
下载PDF
Pretreatment study on chloridizing segregation and magnetic separation of low-grade nickel laterites 被引量:3
15
作者 刘婉蓉 李新海 +4 位作者 胡启阳 王志兴 古可专 李金辉 张琏鑫 《Transactions of Nonferrous Metals Society of China》 SCIE EI CAS CSCD 2010年第S1期82-86,共5页
The chloridizing segregation and magnetic separation of low-grade nickel laterites from Yunnan province of China was investigated.The nickel laterites were characterized by microscopic investigations,using X-ray diffr... The chloridizing segregation and magnetic separation of low-grade nickel laterites from Yunnan province of China was investigated.The nickel laterites were characterized by microscopic investigations,using X-ray diffractometry(XRD)and energy dispersive spectrometry(EDS)techniques.The pellets,which were prepared with magnesium chloride and coke as chloride agent and reductant respectively,were heated to a high temperature,and the pellets after cooling were crushed for magnetic separation.A series of experiments were conducted to examine the effect of chlorinating agent dosage,reductant dosage,chloridizing temperature and chloridizing time on enrichment grade of Ni and Co.The results indicate that the four factors have significant effects on the extractions of Ni and Co.The optimum conditions are as follows:the amounts of magnesium chloride and coke are 6%and 2%,respectively,chloridizing temperature is 1 253 K,and chloridizing time is 90 min.Under the conditions,extractions of Ni and Co reach 91.5%and 82.3%,respectively. 展开更多
关键词 nickel laterites NICKEL COBALT chloridizing segregation magnetic separation
下载PDF
Magnetic separation of pentlandite from serpentine by selective magnetic coating 被引量:2
16
作者 Ji-wei Lu Zhi-tao Yuan +2 位作者 Xiao-fei Guo Zhong-yun Tong Li-xia Li 《International Journal of Minerals,Metallurgy and Materials》 SCIE EI CAS CSCD 2019年第1期1-10,共10页
In this study, pentlandite was selectively separated from serpentine using magnetic coating technology by adjusting and optimizing pH, stirring speeds, magnetic field intensities, and dosages of sodium hexametaphospha... In this study, pentlandite was selectively separated from serpentine using magnetic coating technology by adjusting and optimizing pH, stirring speeds, magnetic field intensities, and dosages of sodium hexametaphosphate(SHMP) and sodium oleate(SO). A magnetic concentrate with Ni grade of 20.8% and Ni recovery of 80.5% was attained under the optimized operating conditions. Considering the above, the adsorption behaviors of SHMP and SO and the surface properties of minerals after the magnetic coating were studied by Fourier transform infrared(FTIR) spectroscopy, X-ray diffraction(XRD), and scanning electron microscopy(SEM). The results show that magnetite was preferentially coated on the pentlandite surfaces and sparingly coated on the serpentine surfaces in the presence of SHMP and SO. Furthermore, calculations by Derjaguin-Landau-Verwey-Overbeek(DLVO) theory indicate that the preferential adsorption of magnetite on the pentlandite surfaces is due to the presence of a hydrophobic interaction between the magnetite and pentlandite, which is much stronger than the interaction between magnetite and serpentine. 展开更多
关键词 DISPERSANT COAGULANT magnetic COATING magnetic separation hydrophobic interaction
下载PDF
Microwave-assisted reduction roasting–magnetic separation studies of two mineralogically different low-grade iron ores 被引量:4
17
作者 Subhnit K.Roy Deepak Nayak +2 位作者 Nilima Dash Nikhil Dhawan Swagat S.Rath 《International Journal of Minerals,Metallurgy and Materials》 SCIE EI CAS CSCD 2020年第11期1449-1461,共13页
The microwave-assisted reduction behaviours of two low-grade iron ores having a similar Fe content of 49wt%but distinctly different mineralogical and liberation characteristics were studied.Their performances in terms... The microwave-assisted reduction behaviours of two low-grade iron ores having a similar Fe content of 49wt%but distinctly different mineralogical and liberation characteristics were studied.Their performances in terms of the iron grade and recovery as obtained from statistically designed microwave(MW)roasting followed by low-intensity magnetic separation(LIMS)experiments were compared.At respective optimum conditions,the titano-magnetite ore(O1)could yield an iron concentrate of 62.57%Fe grade and 60.01%Fe recovery,while the goethitic ore(O2)could be upgraded to a concentrate of 64.4%Fe grade and 33.3%Fe recovery.Compared with the goethitic ore,the titanomagnetite ore responded better to MW heating.The characterization studies of the feed and roasted products obtained at different power and time conditions using X-ray diffraction,optical microscopy,vibrating-sample magnetometry,and electron-probe microanalysis explain the sequential reduction in the iron oxide phases.Finally,taking advantage of the MW absorbing character of the titano-magnetite ore,a blend of the same with the goethite-rich ore at a weight ratio of 60:40(O2:O1)was subjected to MW roasting that resulted in a concentrate of 61.57%Fe grade with a Fe recovery of 64.47%. 展开更多
关键词 MICROWAVE reduction roasting titano-magnetite ore goethitic ore magnetic separation
下载PDF
Recovery of iron from copper tailings via low-temperature direct reduction and magnetic separation: process optimization and mineralogical study 被引量:2
18
作者 Rui-min Jiao Peng Xing +2 位作者 Cheng-yan Wang Bao-zhong Ma Yong-Qiang Chen 《International Journal of Minerals,Metallurgy and Materials》 SCIE EI CAS CSCD 2017年第9期974-982,共9页
Currently, the majority of copper tailings are not effectively developed. Worldwide, large amounts of copper tailings generated from copper production are continuously dumped, posing a potential environmental threat. ... Currently, the majority of copper tailings are not effectively developed. Worldwide, large amounts of copper tailings generated from copper production are continuously dumped, posing a potential environmental threat. Herein, the recovery of iron from copper tailings via low-temperature direct reduction and magnetic separation was conducted; process optimization was carried out, and the corresponding mineralogy was investigated. The reduction time, reduction temperature, reducing agent (coal), calcium chloride additive, grinding time, and magnetic field intensity were examined for process optimization. Mineralogical analyses of the sample, reduced pellets, and magnetic concentrate under various conditions were performed by X-ray diffraction, optical microscopy, and scanning electron microscopy-energy-dispersive X-ray spectrometry to elucidate the iron reduction and growth mechanisms. The results indicated that the optimum parameters of iron recovery include a reduction temperature of 1150A degrees C, a reduction time of 120 min, a coal dosage of 25%, a calcium chloride dosage of 2.5%, a magnetic field intensity of 100 mT, and a grinding time of 1 min. Under these conditions, the iron grade in the magnetic concentrate was greater than 90%, with an iron recovery ratio greater than 95%. 展开更多
关键词 copper tailings IRON direct reduction magnetic separation RECOVERY process optimization
下载PDF
Recovering limonite from Australia iron ores by flocculation-high intensity magnetic separation 被引量:5
19
作者 罗立群 张泾生 余永富 《Journal of Central South University of Technology》 EI 2005年第6期682-687,共6页
Successful recovery of limonite from iron fines was achieved by using flocculation-high intensity magnetic separation (FIMS) and adding hydrolyzed and causticized flocculants according to the characteristic of iron ... Successful recovery of limonite from iron fines was achieved by using flocculation-high intensity magnetic separation (FIMS) and adding hydrolyzed and causticized flocculants according to the characteristic of iron fines. The separation results of the three iron samples are as follows: iron grade 66.77%- 67.98% and the recovery of iron 69.26%-70.70% by the FIMS process with flocculants. The comparative results show that under the same separation conditions the F1MS process can effectively increase the recovery of iron by 10. 97%- 15.73%. The flowsheet results confirm the reliability of the process in a SHP high intensity magnetic separator. The concentrate product can he used as raw materials for direct reduction iron-smelting. The hydrolyzed and causticized flocculants can selectively flocculate fine feebly-magnetic iron mineral particles to increase their apparent separation sizes. The larger the separation size, the stronger the magnetic force. By comparing the separation results of the three samples it is found that among the three samples the higher the limonite content, the better the separation result. This means that the separation result relates closely to the flocculation process and the adding pattern of the flocculant. 展开更多
关键词 Australia iron ores FLOCCULATION high intensity magnetic separation LIMONITE
下载PDF
Testing the robustness of particle-based separation models for the magnetic separation of a complex skarn ore 被引量:3
20
作者 Lucas Pereira Max Frenzel +4 位作者 Markus Buchmann Marius Kern Raimon Tolosana-Delgado K.Gerald van den Boogaart Jens Gutzmer 《International Journal of Mining Science and Technology》 SCIE EI CAS CSCD 2022年第3期645-655,共11页
Physical separation processes are best understood in terms of the behaviour of individual ore particles.Yet,while different empirical particle-based separation modelling approaches have been developed,their predictive... Physical separation processes are best understood in terms of the behaviour of individual ore particles.Yet,while different empirical particle-based separation modelling approaches have been developed,their predictive performance has never been tested under variable process conditions.Here,we investigated the predictive performance of a state-of-the-art particle-based separation model under variable feed composition for a laboratory-scale magnetic separation of a skarn ore.Two scenarios were investigated:one in which the mass flow of the different processing streams could be measured and one in which it had to be estimated from data.In both scenarios,the predictive models were sufficiently general to predict the process outcomes of new samples of variable composition.Nevertheless,the scenario in which mass flow could be measured was4%more precise in predicting mass balances.The process behaviour of minerals present at concentrations above 0.1%by weight could be accurately predicted.Our findings indicate the potential use of this method to minimize the costs of metallurgical testwork while providing in-depth understanding of the recovery behaviour of individual ore particles.Moreover,the method may be used to establish powerful tools to forecast mineral recoveries for partly new ore types at a running mining operation. 展开更多
关键词 Metallurgical tests Particle-based separation modelling magnetic separation Cassiterite recovery