A decorated ruthenium catalyst was prepared by the coprecipitation method and used for the selective hydrogenation of maleic anhydride(MA) to γ-butyrolactone(GBL). The as-prepared catalyst was characterized by XRD, T...A decorated ruthenium catalyst was prepared by the coprecipitation method and used for the selective hydrogenation of maleic anhydride(MA) to γ-butyrolactone(GBL). The as-prepared catalyst was characterized by XRD, TGDTG and N2 adsorption techniques. The characterization tests revealed that the catalyst carrier was composed of monoclinic zirconia(m-ZrO2) and hydroxyl cobalt oxide(CoO(OH)). The hydrogenation results showed that the content of CoO(OH), the reaction temperature, the hydrogen pressure and the reaction time significantly affected the catalytic selectivity to GBL. The promotional effect of CoO(OH) was remarkable, which led to an obvious increase in GBL selectivity. An 100% MA conversion and 92.0% selectivity to GBL were achieved over the Ru/ZrO2-CoO(OH)(35%) catalyst in water solvent under the conditions involving a reaction temperature of 180 ℃, a hydrogen pressure of 3.0 MPa, and a reaction time of 6 h.展开更多
Pd catalysts suffered from poor selectivity and stability for liquid-phase hydrogenation of maleic anhydride（MA） to gamma-butyrolactone（GBL）.Thus,Pd/C catalysts modified with different Sn loadings were synthesized...Pd catalysts suffered from poor selectivity and stability for liquid-phase hydrogenation of maleic anhydride（MA） to gamma-butyrolactone（GBL）.Thus,Pd/C catalysts modified with different Sn loadings were synthesized,and characterized by XRD,XPS,TEM and elemental mapping.The types of alloy phase and the amounts of the surface Pd-SnOx sites altered along with Sn/Pd mass ratios from 0-1.0synthesized in the process of preparation.The maximum reaction rate was 0.57 mol-GBL/（mol-Pd min）and selectivity was 95.94%when the Sn/Pd mass ratio was 0.6.It might be attributed to the formation of Pd2Sn alloy and less amounts of Pd-SnOx sites.展开更多
基金the financial support from the Natural Science Foundation of China(No.21303139)the Key Fund Project of Educational Department of Sichuan Province(No.14ZA0126)the Open Project of Chemical Synthesis and Pollution Control Key Laboratory of Sichuan Province(No.CSPC2013-1)
文摘A decorated ruthenium catalyst was prepared by the coprecipitation method and used for the selective hydrogenation of maleic anhydride(MA) to γ-butyrolactone(GBL). The as-prepared catalyst was characterized by XRD, TGDTG and N2 adsorption techniques. The characterization tests revealed that the catalyst carrier was composed of monoclinic zirconia(m-ZrO2) and hydroxyl cobalt oxide(CoO(OH)). The hydrogenation results showed that the content of CoO(OH), the reaction temperature, the hydrogen pressure and the reaction time significantly affected the catalytic selectivity to GBL. The promotional effect of CoO(OH) was remarkable, which led to an obvious increase in GBL selectivity. An 100% MA conversion and 92.0% selectivity to GBL were achieved over the Ru/ZrO2-CoO(OH)(35%) catalyst in water solvent under the conditions involving a reaction temperature of 180 ℃, a hydrogen pressure of 3.0 MPa, and a reaction time of 6 h.
基金supported by the National Natural Science Foundation,China(Nos.21506138,21606199,21575097 and21375092)the Natural Science Foundation of Zhejiang Province,China(No.LQ15B060001)the China Postdoctoral Science Foundation(No.2016M592015)
文摘Pd catalysts suffered from poor selectivity and stability for liquid-phase hydrogenation of maleic anhydride（MA） to gamma-butyrolactone（GBL）.Thus,Pd/C catalysts modified with different Sn loadings were synthesized,and characterized by XRD,XPS,TEM and elemental mapping.The types of alloy phase and the amounts of the surface Pd-SnOx sites altered along with Sn/Pd mass ratios from 0-1.0synthesized in the process of preparation.The maximum reaction rate was 0.57 mol-GBL/（mol-Pd min）and selectivity was 95.94%when the Sn/Pd mass ratio was 0.6.It might be attributed to the formation of Pd2Sn alloy and less amounts of Pd-SnOx sites.