Effects of small amount of Ca doping in La site in LaCoO 3-based oxide on th e synthesis and electrical conductivity were investigated by using X-ray diffra ction (XRD), differential scanning calorimetry and thermogr...Effects of small amount of Ca doping in La site in LaCoO 3-based oxide on th e synthesis and electrical conductivity were investigated by using X-ray diffra ction (XRD), differential scanning calorimetry and thermogravimetry (DSC/TG), or dinary four-probe dc measurement methods. La 0.8Sr 0.2-xCa x Co 0.9Fe 0.1O 3-δ (LSCCF, 0≤x≤0.1) prepared by solid r eact ion synthesis is all of a single phase and the calcined process may be divided i nt o three stages: (1) decomposition of reactants; (2) formation of LaCoO 3-based oxides; and (3) formation of LSCCF solid solution. The maximum of electrical co nductivity of the LSCCF composites is above 100 S·cm -1 and the co nduction me chanism is attributed to the adiabatic-hopping of p-type small polarons.展开更多
Ti-Mo getters have been fabricated via metal injection molding (MIM) using three kinds of Ti powders with different mean particle sizes of 46 μm,35 μm and 26 μm,respectively. The surface morphology,porosity,and hyd...Ti-Mo getters have been fabricated via metal injection molding (MIM) using three kinds of Ti powders with different mean particle sizes of 46 μm,35 μm and 26 μm,respectively. The surface morphology,porosity,and hydrogen sorption properties of Ti-Mo getters formed by MIM using paraffin wax as a principal binder constituent were examined. It has been proven that the powder injection molding is a viable forming technique for porous Ti-Mo getters. The particle size of Ti powders and the powder loading influence the porosity of getters,and this affects the sorption capacity of Ti-Mo getters. Ti-Mo getters produced with the Ti powders possessing a mean particle size of 35 μm using a powder loading of 40 vol.% have a high porosity,resulting in a good sorption capacity.展开更多
La_(0.68)Pb_(0.32)FeO_3 samples annealed at different temperature were prepared using citrate sol-gel method. With increasing of annealing temperature from 200 to 1000 ℃, the samples crystallize to have single-phase ...La_(0.68)Pb_(0.32)FeO_3 samples annealed at different temperature were prepared using citrate sol-gel method. With increasing of annealing temperature from 200 to 1000 ℃, the samples crystallize to have single-phase perovskite structure. However, the sensitivity increases at first due to the improvement of crystallization of the perovskite phase, and finally drops attributed to the larger grain size. The optimal sensitivities for La_(0.68)Pb_(0.32)FeO_3 samples annealed at 400, 600, 800, and 1000 ℃ are 12.14, 14.77, 51.07, and 34.55, respectively.展开更多
文摘Effects of small amount of Ca doping in La site in LaCoO 3-based oxide on th e synthesis and electrical conductivity were investigated by using X-ray diffra ction (XRD), differential scanning calorimetry and thermogravimetry (DSC/TG), or dinary four-probe dc measurement methods. La 0.8Sr 0.2-xCa x Co 0.9Fe 0.1O 3-δ (LSCCF, 0≤x≤0.1) prepared by solid r eact ion synthesis is all of a single phase and the calcined process may be divided i nt o three stages: (1) decomposition of reactants; (2) formation of LaCoO 3-based oxides; and (3) formation of LSCCF solid solution. The maximum of electrical co nductivity of the LSCCF composites is above 100 S·cm -1 and the co nduction me chanism is attributed to the adiabatic-hopping of p-type small polarons.
文摘Ti-Mo getters have been fabricated via metal injection molding (MIM) using three kinds of Ti powders with different mean particle sizes of 46 μm,35 μm and 26 μm,respectively. The surface morphology,porosity,and hydrogen sorption properties of Ti-Mo getters formed by MIM using paraffin wax as a principal binder constituent were examined. It has been proven that the powder injection molding is a viable forming technique for porous Ti-Mo getters. The particle size of Ti powders and the powder loading influence the porosity of getters,and this affects the sorption capacity of Ti-Mo getters. Ti-Mo getters produced with the Ti powders possessing a mean particle size of 35 μm using a powder loading of 40 vol.% have a high porosity,resulting in a good sorption capacity.
基金Project supported by the National Natural Science Foundation of China (59772040)
文摘La_(0.68)Pb_(0.32)FeO_3 samples annealed at different temperature were prepared using citrate sol-gel method. With increasing of annealing temperature from 200 to 1000 ℃, the samples crystallize to have single-phase perovskite structure. However, the sensitivity increases at first due to the improvement of crystallization of the perovskite phase, and finally drops attributed to the larger grain size. The optimal sensitivities for La_(0.68)Pb_(0.32)FeO_3 samples annealed at 400, 600, 800, and 1000 ℃ are 12.14, 14.77, 51.07, and 34.55, respectively.