A novel enviromental protective water based metallic coating were prepared on the surface of AZ91D magnesium alloy. The properties and structure of the coating were investigated by adhension test, hardness test, heat ...A novel enviromental protective water based metallic coating were prepared on the surface of AZ91D magnesium alloy. The properties and structure of the coating were investigated by adhension test, hardness test, heat resisting test, neutral salt spray test and scanning electron microscopy (SEM). The results show that the coating has a stepped structure which can achieve good adhesion of first-grade, heat resistance temperature of 400℃, hardness of HV_ 0.50/30210 and anti-corrosion time of 250h in salt spray test. Meanwhile, the film forming and corrosion mechanism of the coating were also put forward based on the results of the Fourier transform infrared spectroscopy (FTIR) test and electrochemical impedance spectroscopy (EIS) test.展开更多
目的评价羟基磷灰石(HA)涂层镁铝合金(AZ31B)的体外生物相容性。方法实验分为3组:HA涂层AZ31B浸提液组(H组)、阳性对照组(P组)和空白对照组(N组)。将L929细胞与各组混合液培养3、5和7 d,采用WST-1法检测细胞活力并进行细胞毒性分级。各...目的评价羟基磷灰石(HA)涂层镁铝合金(AZ31B)的体外生物相容性。方法实验分为3组:HA涂层AZ31B浸提液组(H组)、阳性对照组(P组)和空白对照组(N组)。将L929细胞与各组混合液培养3、5和7 d,采用WST-1法检测细胞活力并进行细胞毒性分级。各组混合液与稀释兔血混匀,测定吸光度(OD)并计算溶血率。采用各组混合液对白化豚鼠分别进行皮内诱导、局部诱导和激发,观察去除贴敷片24、48、72 h动物激发部位皮肤情况。结果 3、5和7 d N组和H组细胞毒性反应分级为0级,P组部分细胞毒性反应分级为3级;各时间点H组、N组细胞活力均高于P组,差异有统计学意义(P<0.05)。H组、P组和N组OD值分别为(0.004±0.001)、(0.648±0.050)和(0.008±0.003);H组溶血率为—0.6%,无溶血反应。去除贴敷片24、48、72 h H组皮肤无明显改变,P组可见中度至重度融合性红斑。结论体外实验提示HA涂层镁铝合金具有良好的体外生物相容性。展开更多
A cost-effective crystal growth method was studied to fabricate the relaxor ferroelectric single crystal of lead magnesium niobate -lead titanate (PMN-PT). The crystal of PMN-PT, 7mm in diameter was prepared, and its ...A cost-effective crystal growth method was studied to fabricate the relaxor ferroelectric single crystal of lead magnesium niobate -lead titanate (PMN-PT). The crystal of PMN-PT, 7mm in diameter was prepared, and its dielectric and piezoelectric properties measured are as follows:Tc ～170’℃ Ec～340V/mm, ε～3500 (25℃ and 1kHz), and d33 ～1040pC/N.展开更多
文摘A novel enviromental protective water based metallic coating were prepared on the surface of AZ91D magnesium alloy. The properties and structure of the coating were investigated by adhension test, hardness test, heat resisting test, neutral salt spray test and scanning electron microscopy (SEM). The results show that the coating has a stepped structure which can achieve good adhesion of first-grade, heat resistance temperature of 400℃, hardness of HV_ 0.50/30210 and anti-corrosion time of 250h in salt spray test. Meanwhile, the film forming and corrosion mechanism of the coating were also put forward based on the results of the Fourier transform infrared spectroscopy (FTIR) test and electrochemical impedance spectroscopy (EIS) test.
文摘目的评价羟基磷灰石(HA)涂层镁铝合金(AZ31B)的体外生物相容性。方法实验分为3组:HA涂层AZ31B浸提液组(H组)、阳性对照组(P组)和空白对照组(N组)。将L929细胞与各组混合液培养3、5和7 d,采用WST-1法检测细胞活力并进行细胞毒性分级。各组混合液与稀释兔血混匀,测定吸光度(OD)并计算溶血率。采用各组混合液对白化豚鼠分别进行皮内诱导、局部诱导和激发,观察去除贴敷片24、48、72 h动物激发部位皮肤情况。结果 3、5和7 d N组和H组细胞毒性反应分级为0级,P组部分细胞毒性反应分级为3级;各时间点H组、N组细胞活力均高于P组,差异有统计学意义(P<0.05)。H组、P组和N组OD值分别为(0.004±0.001)、(0.648±0.050)和(0.008±0.003);H组溶血率为—0.6%,无溶血反应。去除贴敷片24、48、72 h H组皮肤无明显改变,P组可见中度至重度融合性红斑。结论体外实验提示HA涂层镁铝合金具有良好的体外生物相容性。
文摘A cost-effective crystal growth method was studied to fabricate the relaxor ferroelectric single crystal of lead magnesium niobate -lead titanate (PMN-PT). The crystal of PMN-PT, 7mm in diameter was prepared, and its dielectric and piezoelectric properties measured are as follows:Tc ～170’℃ Ec～340V/mm, ε～3500 (25℃ and 1kHz), and d33 ～1040pC/N.