The polypropylene wax modified by ultraviolet irradiation. The polypropylene-montmorillonite nanocomposiles were prepared by direct melting intercalation oj polypropylene powders. The structure of polypropylene , the ...The polypropylene wax modified by ultraviolet irradiation. The polypropylene-montmorillonite nanocomposiles were prepared by direct melting intercalation oj polypropylene powders. The structure of polypropylene , the polyproprlene irradiated, montmorillinote and polypropylene-montmorillonite composites were studied by XRD, 1R and DSC. The results show that the PP molecules can are oxidized during ultraviolet irradiation , melt polypropylene can intercalate into montmorillonite layer. As a result, the layered distance ( d0.01) of montmorillonite increases, and the melt absorption peak of polypropylene in layer is eliminated.展开更多
The montmorillonites (MMTs), layered, smectite-type silicates, were premodified by two different methods prior to the polymer melt intercalation. In one case MMTs were modified with cetyltrimethylammonium bromide (CTA...The montmorillonites (MMTs), layered, smectite-type silicates, were premodified by two different methods prior to the polymer melt intercalation. In one case MMTs were modified with cetyltrimethylammonium bromide (CTAB), and termed as organomontmorillonites (OMMTs); in the other case MMTs were modified by nylon, and the products were called modified montmorillonites (MMMTs). The effects of CTAB and nylon on the MMTs were investigated by using TG and WAXD. The results show that interlayer spacings of CTAB and nylon modified MMTs are larger than that of sodium MMTs. Then, polyamide 66 (PA 66)/MMT nanocomposites were obtained through the method of melt intercalation of polymers. The nanocomposites were characterized by WAXD, TEM and Molau experiments. The results indicate that the MMTs disperse homogeneously in the PA 66 matrix. The mechanical properties of nanocomposites, such as tensile properties and flexural properties, were also measured and show a tendency to increase with increase of MMT content and reach the maximum values at 5phr MMT content. The heat distortion temperature (HDT) of the nanocomposites (7 phr) is about 32 K higher than that of pure PA 66.展开更多
Phenolic resin/montmorillonite intercalation composites were prepared by using the methods of pressing intercalation and melt intercalation.Properties and structure of the composites were investigated by using XRD,TG ...Phenolic resin/montmorillonite intercalation composites were prepared by using the methods of pressing intercalation and melt intercalation.Properties and structure of the composites were investigated by using XRD,TG and test of softening point.It is indicated that both the pressing intercalation and melt intercalation can be used to prepare the phenolic resin/organo-montmorillonite intercalation nanocomposites.Compared with phenolic resin,the intercalation nanocomposites have better heat-resistance,higher decomposition temperatures and less thermal weight-loss.However,these two intercalation methods have different effects on the softening point of the intercalation nanocomposites.Pressing intercalation almost does not affect the softening point of the intercalation nanocomposites,while melt intercalation significantly increases the softening point of the intercalation nanocomposites, probably due to the chemical actions happening in the process of melt intercalation.展开更多
文摘The polypropylene wax modified by ultraviolet irradiation. The polypropylene-montmorillonite nanocomposiles were prepared by direct melting intercalation oj polypropylene powders. The structure of polypropylene , the polyproprlene irradiated, montmorillinote and polypropylene-montmorillonite composites were studied by XRD, 1R and DSC. The results show that the PP molecules can are oxidized during ultraviolet irradiation , melt polypropylene can intercalate into montmorillonite layer. As a result, the layered distance ( d0.01) of montmorillonite increases, and the melt absorption peak of polypropylene in layer is eliminated.
基金This project was supported by the Science Funds for Henan Province's Prominent Youth and the Science Funds for Henan Province's Creative Persons.
文摘The montmorillonites (MMTs), layered, smectite-type silicates, were premodified by two different methods prior to the polymer melt intercalation. In one case MMTs were modified with cetyltrimethylammonium bromide (CTAB), and termed as organomontmorillonites (OMMTs); in the other case MMTs were modified by nylon, and the products were called modified montmorillonites (MMMTs). The effects of CTAB and nylon on the MMTs were investigated by using TG and WAXD. The results show that interlayer spacings of CTAB and nylon modified MMTs are larger than that of sodium MMTs. Then, polyamide 66 (PA 66)/MMT nanocomposites were obtained through the method of melt intercalation of polymers. The nanocomposites were characterized by WAXD, TEM and Molau experiments. The results indicate that the MMTs disperse homogeneously in the PA 66 matrix. The mechanical properties of nanocomposites, such as tensile properties and flexural properties, were also measured and show a tendency to increase with increase of MMT content and reach the maximum values at 5phr MMT content. The heat distortion temperature (HDT) of the nanocomposites (7 phr) is about 32 K higher than that of pure PA 66.
文摘Phenolic resin/montmorillonite intercalation composites were prepared by using the methods of pressing intercalation and melt intercalation.Properties and structure of the composites were investigated by using XRD,TG and test of softening point.It is indicated that both the pressing intercalation and melt intercalation can be used to prepare the phenolic resin/organo-montmorillonite intercalation nanocomposites.Compared with phenolic resin,the intercalation nanocomposites have better heat-resistance,higher decomposition temperatures and less thermal weight-loss.However,these two intercalation methods have different effects on the softening point of the intercalation nanocomposites.Pressing intercalation almost does not affect the softening point of the intercalation nanocomposites,while melt intercalation significantly increases the softening point of the intercalation nanocomposites, probably due to the chemical actions happening in the process of melt intercalation.