To avoid slag sticking on the ladle immersion cover during the LATS refining and alloying process, the effect of Al2O3 on the melting point of the ladle slag was studied and the additives including CaF2, B2O3, Li2O, a...To avoid slag sticking on the ladle immersion cover during the LATS refining and alloying process, the effect of Al2O3 on the melting point of the ladle slag was studied and the additives including CaF2, B2O3, Li2O, and CaO were used to decrease the melting point of the ladle slag. The melting point was measured using the hemisphere method. The results show that the addition of Al2O3 to the ladle slag increases the melting point. The fluxing action is not remarkable if only CaF2 or CaO is used as the additive. The fluxing action of the composite additive obtained by the mixing of CaO and CaF2 in the mass proportion of ωCaO:ωCaF2=2 : 1 is preferred. The fluxing action of B2O3 is also notable. When the B2O3 content in mass percent is in the range from 2% to 10%, the corresponding melting point is 1 380 ℃ to 1 290℃. The fluxing action of Li2O is the most remarkable. When the Li2O content is up to 5%, the melting point of the slag is lower than 1 300 ℃.展开更多
Asymmetric plate impact experiments are conducted on LY12 aluminium alloy in a pressure range of 85-131 GPa. The longitudinal sound speeds axe obtained from the time-resolved particle speed profiles of the specimen me...Asymmetric plate impact experiments are conducted on LY12 aluminium alloy in a pressure range of 85-131 GPa. The longitudinal sound speeds axe obtained from the time-resolved particle speed profiles of the specimen measured with Velocity Interferometer System for Any Reflector (VISAR) technique, and they are shown to be good agreement with our previously reported data of this alloy in a pressure range of 20-70 GPa, and also with those of 2024 aluminium reported by McQueen. Using all of the longitudinal speeds and the corresponding bulk speeds calculated from the Gruneisen equation of state (EOS), shear moduli of LY12 aluminium alloy are obtained. A comparison of the shear moduli in the solid phase region with those estimated from the Steinberg model demonstrate that the latter are systematically lower than the measurements. By re-analysing the pressure effect on the shear modulus, a modified equation is proposed, in which the pressure term of P/η^1/3 in the Steinberg model is replaced by a linear term. Good agreement between experiments and the modified equation is obtained, which implies that the shear modulus of LY12 aluminium varies linearly both with pressure and with temperature throughout the whole solid phase region. On the other hand, shear modulus of aluminium in a solid-liquid mixed phrase region decreases gradually and smoothly, a feature that is very different from the drastic dropping at the melting point under static conditions.展开更多
Interaction rule between representative RE and Sn, Sb, Pb, Cu, S, P low melting point elements respectively in Fe , Cu , Al , Ni base liquid solutions including totally 34 ternary and quarternary systems was inve...Interaction rule between representative RE and Sn, Sb, Pb, Cu, S, P low melting point elements respectively in Fe , Cu , Al , Ni base liquid solutions including totally 34 ternary and quarternary systems was investigated. For each system some thermodynamic properties were obtained, such as the standard free energies of equilibrium reactions, activity interaction coefficients etc ..展开更多
This paper has constructed two kinds of atomic and electronic models for hexagonal β-Mo2C and orthorhombic α-Mo2C. The optimized lattice parameters, elastic constant matrixes and overlap population for Mo2C crystal ...This paper has constructed two kinds of atomic and electronic models for hexagonal β-Mo2C and orthorhombic α-Mo2C. The optimized lattice parameters, elastic constant matrixes and overlap population for Mo2C crystal cells have been obtained to realize the characterization of the hardness and melting point of the two structures by the first-principles plane wave pseudo potential method based on the density functional theory. The results reveal that the calculated lattice parameters of the Mo2C crystal cells agree with the experimental and other calculated data. The calculated melting point/hardness are 2715 K/11.38 GPa for β-Mo2C and 2699 K/10.57-12.67 GPa for α-Mo2C, respectively. The calculated results from the density of states (DOS) demonstrate that the hybridization effect between Mo-3d and C-2p states in α-Mo2C crystal cell is much stronger than that in β-Mo2C one.展开更多
To improve the properties of Sn10Sb8Cu solder alloy, two new solders (SnSbCuAg and SnSbCuNi) were formed by adding small amounts of Ag or Ni into the solder alloy. The results show that the melting point of the SnSb...To improve the properties of Sn10Sb8Cu solder alloy, two new solders (SnSbCuAg and SnSbCuNi) were formed by adding small amounts of Ag or Ni into the solder alloy. The results show that the melting point of the SnSbCuAg solder alloy decreases by 14.1℃ and the spreading area increases by 16.5% compared to the matrix solder. The melting point of the SnSbCuNi solder alloy decreases by 5.4℃ and the spreading area is slightly less than that of the matrix solder. Microstructure analysis shows that adding trace Ag makes the melting point decline due to the dispersed distribution of SnAg phase with low melting point. Adding trace Ni, Cu6Sn5 and (Cu, Ni)6Sn5 with polyhedron shape on the copper substrate can be easily seen in the SnSbCuNi solder alloy, which makes the viscosity of the melting solder increase and the spreading property of the solder decline.展开更多
The polyoxometalate(POM)-imidazole ionic liquid(IL) [C8mim]2[Mo6O19](C8mim=1-methyl-3-octylimi- dazolium) with a low melting point of 82.6 °C was successfully prepared and characterized by FTIR, XPS, NMR, T...The polyoxometalate(POM)-imidazole ionic liquid(IL) [C8mim]2[Mo6O19](C8mim=1-methyl-3-octylimi- dazolium) with a low melting point of 82.6 °C was successfully prepared and characterized by FTIR, XPS, NMR, TG and so on. The polyoxomolybdate-based IL has high stability, and its decomposing temperature reaches 321 °C, which is higher than that of 1-alkyl-3-methylimidazolium halides IL. Further photocatalytic performances of the IL were measured via degrading dye rhodamine B(RB) in aqueous solution under the UV light irradiation. The experiments show that the conversion of RB reaches 80.5% after 90 min under UV-light and the degradation efficiency depends on the pH value of the solution, irradiation time and the dosage of the IL and so on.展开更多
Abnormal melting point depression of metal nanoparticles often occurs in heterogeneous catalytic reactions,which leads to a reduction in the stability of reactive nanoclusters.To study this abnormal phenomenon,the ori...Abnormal melting point depression of metal nanoparticles often occurs in heterogeneous catalytic reactions,which leads to a reduction in the stability of reactive nanoclusters.To study this abnormal phenomenon,the original and surface-energy modified Gibbs-Thomson equations were analyzed in this work and further modified by considering the effect of the substrate.The results revealed that the original Gibbs-Thomson equation was not suitable for the particles with radii smaller than 10 nm.Moreover,the performance of the surface-energy modified Gibbs-Thomson equation was improved,and the deviation was reduced to(-350-100)K,although further modification of the equation by considering the interfacial effect was necessary for the small particles(r<5 nm).The new model with the interfacial effect improved the model performance with a deviation of approximately-50 to 20 K,where the interfacial effect can be predicted quantitatively from the thermodynamic properties of the metal and substrate.Additionally,the micro-wetting parameterα_W can be used to qualitatively study the overall impact of the substrate on the melting point depression.展开更多
The relation between the melting point of Portland cement raw meal and its heating rate have been studied. The raw meal was burnt at different heating rate ranging from 10 similar to 900 degrees C/min Dy the following...The relation between the melting point of Portland cement raw meal and its heating rate have been studied. The raw meal was burnt at different heating rate ranging from 10 similar to 900 degrees C/min Dy the following methods: (A) in electric resistance furnace; (B) in DTA-TG analyzer with infrared ray focused heating; (C) in high temperature microscope with electron stream heating. Based on thermal analysis theory and melt theory and the tests above, it is found that melting point T-m of cement raw meal decreases with the increased heating rate Phi during burning in the following relation: T-m=1280-0.107 empty set.展开更多
The dispersion mechanism of low melting point metal (LMPM) particles in polymers was studied using Cox dilute emulsion model. The critical destruction shear stress sigma of LMPM droplets is sigma greater than 2 v/d. ...The dispersion mechanism of low melting point metal (LMPM) particles in polymers was studied using Cox dilute emulsion model. The critical destruction shear stress sigma of LMPM droplets is sigma greater than 2 v/d. When sigma is small, LMPM droplets were dispersed and deformed ellipsoidal or bar droplets whose orientation direction is always at an angle of 45 degree with the direction of shear rate. When sigma is very big and droplets are very fine, polymer melt elasticity behavior and big boundary tension between a polymer melt and LMPM droplets make further fining LMPM droplets become more difficult. Therefore, LMPM droplets produce tensile flow and form LMPM microfibrils in situ in polymer melt. SEM photographs have shown the results predicted using dilute emulsion model. (Author abstract) 7 Refs.展开更多
The interest in refractory materials is increasing rapidly in recent decades due to the development of hypersonic vehicles.However,the substance that has the highest melting point(Tm)keeps a secret,since precise measu...The interest in refractory materials is increasing rapidly in recent decades due to the development of hypersonic vehicles.However,the substance that has the highest melting point(Tm)keeps a secret,since precise measurements in extreme conditions are overwhelmingly difficult.In the present work,an accurate deep potential(DP)model of a Hf-Ta-C-N system was first trained,and then applied to search for the highest melting point material by molecular dynamics(MD)simulation and Bayesian global optimization(BGO).The predicted melting points agree well with the experiments and confirm that carbon site vacancies can enhance the melting point of rock-saltstructure carbides.The solid solution with N is verified as another new and more effective melting point enhancing approach for HfC,while a conventional routing of the solid solution with Ta(e.g.,HfTa_(4)C_(5))is not suggested to result in a maximum melting point.The highest melting point(~4236 K)is achieved with the composition of HfCo.638No.271,which is~80 K higher than the highest value in a Hf-C binary system.Dominating mechanism of the N addition is believed to be unstable C-N and N-N bonds in liquid phase,which reduces liquid phase entropy and renders the liquid phase less stable.The improved melting point and less gas generation during oxidation by the addition of N provide a new routing to modify thermal protection materials for the hypersonic vehicles.展开更多
The pressure dependence of the molar volume was at constant temperatures close to the melting point in benzene. The molar volume of benzene was calculated using experimental data for the thermal expansivity for consta...The pressure dependence of the molar volume was at constant temperatures close to the melting point in benzene. The molar volume of benzene was calculated using experimental data for the thermal expansivity for constant temperatures of 25℃, 28.5℃, 40℃, and 51℃ at various pressures for both the solid and liquid phases. The predictions are in good agreement with the observed volumes in both the solid and liquid phases of benzene. The predicted values of the molar volume for a constant temperature of 28.5℃in the liquid phase of benzene agree well with experimental data in the literature.展开更多
The activity data of each component of a CaO–SiO2–Al2O3 system were calculated by thermodynamic software Factsage. The composition of low melting point inclusions in a CaO–SiO2–Al2O3–MgO system was analyzed by th...The activity data of each component of a CaO–SiO2–Al2O3 system were calculated by thermodynamic software Factsage. The composition of low melting point inclusions in a CaO–SiO2–Al2O3–MgO system was analyzed by thermodynamic calculation. The results show that the area of low melting point inclusions first increases then decreases with accumulating the alumina and magnesium oxide contents, respectively; the low melting area of CaO–SiO2–Al2O3–MgO inclusion is the biggest when the content of MgO and Al2O3 is 15%. To obtain low melting point inclusions, the alumina and magnesium contents should be approximately controlled to be 15%, and the CaO should be 40%.展开更多
sing the Average Lattice and Atom Modelsofthe Empirical Electron Theory of SolidsandMolecules( EET), the effects of interstitial impurities on valence electron structures and melting pointof Ti- Alalloysareanalyzed ....sing the Average Lattice and Atom Modelsofthe Empirical Electron Theory of SolidsandMolecules( EET), the effects of interstitial impurities on valence electron structures and melting pointof Ti- Alalloysareanalyzed .Becauseoftheeffectsofinterstitialimpurities,atoms hybridization statesincrease, bondstructuresareseriously anisotropic,andthe melting pointsare decreased .展开更多
Polyamide 1010 (PA1010)/thermoplastie poly (ether urethane) elastomer (ether-based TPU) blends were prepared via melt extrusion. The crystallization kinetics and melting behavior of PA1010/ether-based TPU blends...Polyamide 1010 (PA1010)/thermoplastie poly (ether urethane) elastomer (ether-based TPU) blends were prepared via melt extrusion. The crystallization kinetics and melting behavior of PA1010/ether-based TPU blends were systematically investigated using differential scanning calorimetry. The crystallization kinetics results show that the addition of ether-based TPU hinders the crystallization of PA1010, and the hindrance effect increases with the increase of the concentration of ether-based TPU. Both pure PA1010 and PA1010/ether-based TPU blends exhibit double melting peaks in the process of nonisothermal crystallization. The double melting peaks change differently with the variation of cooling rate and blend composition. The cooling rate only influences the lower melting peak; however, the blend composition influences not only the lower melting peak but also the higher melting peak. The reason for the phenomenon must be the interaction between the two compositions.展开更多
The experimental study on the melting of potassic basalt and eclogite with about 2% waterat 800-1300℃ and 1.0-3.5 GPa shows that the solidi of both rocks are significantly lower thanthose obtained from the previous e...The experimental study on the melting of potassic basalt and eclogite with about 2% waterat 800-1300℃ and 1.0-3.5 GPa shows that the solidi of both rocks are significantly lower thanthose obtained from the previous experiments of the same type of rocks under dry conditions,and the former which is enriched in potassium has a lower melting point than the latter. It is con-sistent with the previous study. The melting temperature of eclogite increases with pressure,whereas potassic basalt has similar properties only at 1.5—2.5 GPa and>3.0 GPa, and at 2.5—3.0 GPa the melting temperature decreases with pressure. This can be explained as follows: (1)eclogite only has one hydrous mineral amphibole and the dehydous temperature is lower than thewet solidus of the rock. (2) Amphibole exists in potassic basalt at the pressures lower than 2.5GPa and phlogopite exists at pressures higher than 2.5 GPa, and the special compositions of bothminerals determine that amphibole has a dehydration temperature higher than or close to that ofthe wet solidus of the rocks, while phlogopite has a dehydration temperature lower than that ofthe wet solidus. On the other hand the features of the continuous solidus in the experiment ofhydrous eclogite were produced by the fact that the dehydration temperature of its amphibolelower than or close to the melting temperature of the hydrous conditions. So the melting tempera-ture lowers at higher pressures. Therefore, the composition of the rocks in the lithosphere and thetypes of hydrous minerals and their stable P-T conditions are the important factors controllingthe solidi of rocks. It can quite well explain the partial melting of rocks and the origin of the lowvelocity zone in the deep lithosphere.展开更多
With the aid of a slip-disentanglemnt theory, a rheological equation has been deduced about the composite system of solid-state low melting point metal and polymer. By measuring some rheological properties of the comp...With the aid of a slip-disentanglemnt theory, a rheological equation has been deduced about the composite system of solid-state low melting point metal and polymer. By measuring some rheological properties of the composite system composed of low melt point metal and polypropylene (LMPM/PP), the results show that LMPM has a promoter flow action upon PP when using a small amount of LMPM and, if some coupled agents are added, the promoter flow action will be remarkable. Moreover, while LMPM being added into the composite, the temperature sensitivity of system will go rip. This indicates that the system's viscosity will drop further if its temperature is increased.展开更多
The low melting point metallic tin powder or alloy of tin and lead was blended with polypropylene. A kind of in situ composite has been prepared. The variations of torque were studied when the composites were mixed in...The low melting point metallic tin powder or alloy of tin and lead was blended with polypropylene. A kind of in situ composite has been prepared. The variations of torque were studied when the composites were mixed in Haake torque rheogeniometer. By way of capillary extrusion, effects upon rheology of the in situ composites of the low melting point metals (LMPM) and coupling agent for their different variety and content, were investigated. From flow curves, the results indicate that in situ composites mixed with the LMPM are a kind of pseudoplastic fluid. If the LMPM were melted, the higher the content of the LMPM, the lower apparent viscosity of composites. Meanwhile, when the coupling agent is added into composites , the viscosity of composite will go up first and drop then. This shows that the LMPM have a promoter flow action on the polypropylene.展开更多
Poly(ε-caprolactone) (PCL) with different molecular weights was synthesized and characterized by a gelpermeation chromatograph equipped with multiple detector. The melting behavior of PCL was also studied. It was fou...Poly(ε-caprolactone) (PCL) with different molecular weights was synthesized and characterized by a gelpermeation chromatograph equipped with multiple detector. The melting behavior of PCL was also studied. It was found thatthe equilibrium melting points (T_m^0) of PCL samples depend on their molecular weights. Wide angle X-ray diffractionmeasurements (WAXD) and DSC measurements showed that the crystals of the high molecular weight PCLs were moreperfect than those of the low molecular weigh ones. These results demonstrate that the concentration of the end groups ofPCL chains is the main factor that influences the melting behavior. The fusion enthalpy per repeating unit (ΔH_u) wasdetermined to be 11.3 kJ/mol for PCL.展开更多
With the Voter-Chen version of embedded-atom model (EAM) potential and molecular dynamics, the melting of Ni3Al alloy was simulated by one-phase (conventional) and two-phase approaches. It is shown that the simula...With the Voter-Chen version of embedded-atom model (EAM) potential and molecular dynamics, the melting of Ni3Al alloy was simulated by one-phase (conventional) and two-phase approaches. It is shown that the simulated melting point is dependent on the potential and the simulation method. The structures of the melts obtained by different simulation methods were analyzed by the pair correlation function, the coordination number, and the distribution of atom pair type (indexed by the Honeycutt-Andersen pair analysis technique). The results show that the structures are very similar.展开更多
Microstructural evolutions of the railway frog steel solidified under different pressure were studied using OM, FEGSEM, and TEM. The influences of pressure on the solidification, grain sizes, and morphology of carbide...Microstructural evolutions of the railway frog steel solidified under different pressure were studied using OM, FEGSEM, and TEM. The influences of pressure on the solidification, grain sizes, and morphology of carbides of the steel were analyzed. It is found that the melting point of the steel increases with the pressure and the solidified microstructure under high pressure does not vary significantly with the melting temperature. The experimental results show that the solidified microstructure consisting of complete equiaxed dendrites is remarkably refined through the increase of pressure, with the mean dendrite arm spacing of about 24, 18, and 8 μm under 3, 6, and 10 GPa, respectively. It is also revealed by TEM observation that the precipitates change from needle-like and rhombic carbide(M3C) forms during normal(atmospheric) pressure solidification into nodulized hexagonal precipitate M7C3 at 3 GPa, and M(23)C6 at 6 GPa and 10 GPa, which is associated with the undercooling and distribution of the trace elements. The diameter of the precipitates is between 80 nm and 200 nm.展开更多
基金Item Sponsored by National Natural Science Foundation of China (50474037) Natural Science Foundation of Jiangsu Higher Education Institutions of China (04KJB430022 ,05KJD450043)
文摘To avoid slag sticking on the ladle immersion cover during the LATS refining and alloying process, the effect of Al2O3 on the melting point of the ladle slag was studied and the additives including CaF2, B2O3, Li2O, and CaO were used to decrease the melting point of the ladle slag. The melting point was measured using the hemisphere method. The results show that the addition of Al2O3 to the ladle slag increases the melting point. The fluxing action is not remarkable if only CaF2 or CaO is used as the additive. The fluxing action of the composite additive obtained by the mixing of CaO and CaF2 in the mass proportion of ωCaO:ωCaF2=2 : 1 is preferred. The fluxing action of B2O3 is also notable. When the B2O3 content in mass percent is in the range from 2% to 10%, the corresponding melting point is 1 380 ℃ to 1 290℃. The fluxing action of Li2O is the most remarkable. When the Li2O content is up to 5%, the melting point of the slag is lower than 1 300 ℃.
基金Project supported by the National Natural Science Foundation of China (Grant Nos 10232040 and 10672149)the foundation of Laboratory for Shock Wave and Detonation Physics Research, China Academy of Engineering Physics (Grant No 9140C6702020603)
文摘Asymmetric plate impact experiments are conducted on LY12 aluminium alloy in a pressure range of 85-131 GPa. The longitudinal sound speeds axe obtained from the time-resolved particle speed profiles of the specimen measured with Velocity Interferometer System for Any Reflector (VISAR) technique, and they are shown to be good agreement with our previously reported data of this alloy in a pressure range of 20-70 GPa, and also with those of 2024 aluminium reported by McQueen. Using all of the longitudinal speeds and the corresponding bulk speeds calculated from the Gruneisen equation of state (EOS), shear moduli of LY12 aluminium alloy are obtained. A comparison of the shear moduli in the solid phase region with those estimated from the Steinberg model demonstrate that the latter are systematically lower than the measurements. By re-analysing the pressure effect on the shear modulus, a modified equation is proposed, in which the pressure term of P/η^1/3 in the Steinberg model is replaced by a linear term. Good agreement between experiments and the modified equation is obtained, which implies that the shear modulus of LY12 aluminium varies linearly both with pressure and with temperature throughout the whole solid phase region. On the other hand, shear modulus of aluminium in a solid-liquid mixed phrase region decreases gradually and smoothly, a feature that is very different from the drastic dropping at the melting point under static conditions.
基金Project Sponsored by the National Natural Science Foundation
文摘Interaction rule between representative RE and Sn, Sb, Pb, Cu, S, P low melting point elements respectively in Fe , Cu , Al , Ni base liquid solutions including totally 34 ternary and quarternary systems was investigated. For each system some thermodynamic properties were obtained, such as the standard free energies of equilibrium reactions, activity interaction coefficients etc ..
文摘This paper has constructed two kinds of atomic and electronic models for hexagonal β-Mo2C and orthorhombic α-Mo2C. The optimized lattice parameters, elastic constant matrixes and overlap population for Mo2C crystal cells have been obtained to realize the characterization of the hardness and melting point of the two structures by the first-principles plane wave pseudo potential method based on the density functional theory. The results reveal that the calculated lattice parameters of the Mo2C crystal cells agree with the experimental and other calculated data. The calculated melting point/hardness are 2715 K/11.38 GPa for β-Mo2C and 2699 K/10.57-12.67 GPa for α-Mo2C, respectively. The calculated results from the density of states (DOS) demonstrate that the hybridization effect between Mo-3d and C-2p states in α-Mo2C crystal cell is much stronger than that in β-Mo2C one.
基金supported by the Program for Science & Technology Innovation Talents in Universities of Henan Province (No.2010HASTIT032)the City Key Technologies R & D Program of Luoyang (No.0801038A), China
文摘To improve the properties of Sn10Sb8Cu solder alloy, two new solders (SnSbCuAg and SnSbCuNi) were formed by adding small amounts of Ag or Ni into the solder alloy. The results show that the melting point of the SnSbCuAg solder alloy decreases by 14.1℃ and the spreading area increases by 16.5% compared to the matrix solder. The melting point of the SnSbCuNi solder alloy decreases by 5.4℃ and the spreading area is slightly less than that of the matrix solder. Microstructure analysis shows that adding trace Ag makes the melting point decline due to the dispersed distribution of SnAg phase with low melting point. Adding trace Ni, Cu6Sn5 and (Cu, Ni)6Sn5 with polyhedron shape on the copper substrate can be easily seen in the SnSbCuNi solder alloy, which makes the viscosity of the melting solder increase and the spreading property of the solder decline.
基金Supported by the National Natural Science Foundation of China(Nos.2067101120731002+3 种基金20801004 10876002 20801005)the Specialized Research Fund for the Doctoral Program of Higher Education of China(No.200800070015).
文摘The polyoxometalate(POM)-imidazole ionic liquid(IL) [C8mim]2[Mo6O19](C8mim=1-methyl-3-octylimi- dazolium) with a low melting point of 82.6 °C was successfully prepared and characterized by FTIR, XPS, NMR, TG and so on. The polyoxomolybdate-based IL has high stability, and its decomposing temperature reaches 321 °C, which is higher than that of 1-alkyl-3-methylimidazolium halides IL. Further photocatalytic performances of the IL were measured via degrading dye rhodamine B(RB) in aqueous solution under the UV light irradiation. The experiments show that the conversion of RB reaches 80.5% after 90 min under UV-light and the degradation efficiency depends on the pH value of the solution, irradiation time and the dosage of the IL and so on.
基金Financial supports from Key Project(21838004)Joint Research Fund for Overseas Chinese,Hong Kong,Macao Young Scientists of National Natural Science Foundation(21729601)of China+1 种基金the Swedish Research Councilthe Kempe Foundation for financial support。
文摘Abnormal melting point depression of metal nanoparticles often occurs in heterogeneous catalytic reactions,which leads to a reduction in the stability of reactive nanoclusters.To study this abnormal phenomenon,the original and surface-energy modified Gibbs-Thomson equations were analyzed in this work and further modified by considering the effect of the substrate.The results revealed that the original Gibbs-Thomson equation was not suitable for the particles with radii smaller than 10 nm.Moreover,the performance of the surface-energy modified Gibbs-Thomson equation was improved,and the deviation was reduced to(-350-100)K,although further modification of the equation by considering the interfacial effect was necessary for the small particles(r<5 nm).The new model with the interfacial effect improved the model performance with a deviation of approximately-50 to 20 K,where the interfacial effect can be predicted quantitatively from the thermodynamic properties of the metal and substrate.Additionally,the micro-wetting parameterα_W can be used to qualitatively study the overall impact of the substrate on the melting point depression.
文摘The relation between the melting point of Portland cement raw meal and its heating rate have been studied. The raw meal was burnt at different heating rate ranging from 10 similar to 900 degrees C/min Dy the following methods: (A) in electric resistance furnace; (B) in DTA-TG analyzer with infrared ray focused heating; (C) in high temperature microscope with electron stream heating. Based on thermal analysis theory and melt theory and the tests above, it is found that melting point T-m of cement raw meal decreases with the increased heating rate Phi during burning in the following relation: T-m=1280-0.107 empty set.
文摘The dispersion mechanism of low melting point metal (LMPM) particles in polymers was studied using Cox dilute emulsion model. The critical destruction shear stress sigma of LMPM droplets is sigma greater than 2 v/d. When sigma is small, LMPM droplets were dispersed and deformed ellipsoidal or bar droplets whose orientation direction is always at an angle of 45 degree with the direction of shear rate. When sigma is very big and droplets are very fine, polymer melt elasticity behavior and big boundary tension between a polymer melt and LMPM droplets make further fining LMPM droplets become more difficult. Therefore, LMPM droplets produce tensile flow and form LMPM microfibrils in situ in polymer melt. SEM photographs have shown the results predicted using dilute emulsion model. (Author abstract) 7 Refs.
基金supports by the National Natural Science Foundation of China(Nos.52032002,51972081,and U2130103)University Nursing Program for Young Scholars with Creative Talents in Heilongjiang Province(No.UNPYSCT-2020052)+1 种基金Heilongjiang Touyan Team Programsupported by Bohrium Cloud Platform of DP Technology.
文摘The interest in refractory materials is increasing rapidly in recent decades due to the development of hypersonic vehicles.However,the substance that has the highest melting point(Tm)keeps a secret,since precise measurements in extreme conditions are overwhelmingly difficult.In the present work,an accurate deep potential(DP)model of a Hf-Ta-C-N system was first trained,and then applied to search for the highest melting point material by molecular dynamics(MD)simulation and Bayesian global optimization(BGO).The predicted melting points agree well with the experiments and confirm that carbon site vacancies can enhance the melting point of rock-saltstructure carbides.The solid solution with N is verified as another new and more effective melting point enhancing approach for HfC,while a conventional routing of the solid solution with Ta(e.g.,HfTa_(4)C_(5))is not suggested to result in a maximum melting point.The highest melting point(~4236 K)is achieved with the composition of HfCo.638No.271,which is~80 K higher than the highest value in a Hf-C binary system.Dominating mechanism of the N addition is believed to be unstable C-N and N-N bonds in liquid phase,which reduces liquid phase entropy and renders the liquid phase less stable.The improved melting point and less gas generation during oxidation by the addition of N provide a new routing to modify thermal protection materials for the hypersonic vehicles.
文摘The pressure dependence of the molar volume was at constant temperatures close to the melting point in benzene. The molar volume of benzene was calculated using experimental data for the thermal expansivity for constant temperatures of 25℃, 28.5℃, 40℃, and 51℃ at various pressures for both the solid and liquid phases. The predictions are in good agreement with the observed volumes in both the solid and liquid phases of benzene. The predicted values of the molar volume for a constant temperature of 28.5℃in the liquid phase of benzene agree well with experimental data in the literature.
文摘The activity data of each component of a CaO–SiO2–Al2O3 system were calculated by thermodynamic software Factsage. The composition of low melting point inclusions in a CaO–SiO2–Al2O3–MgO system was analyzed by thermodynamic calculation. The results show that the area of low melting point inclusions first increases then decreases with accumulating the alumina and magnesium oxide contents, respectively; the low melting area of CaO–SiO2–Al2O3–MgO inclusion is the biggest when the content of MgO and Al2O3 is 15%. To obtain low melting point inclusions, the alumina and magnesium contents should be approximately controlled to be 15%, and the CaO should be 40%.
文摘sing the Average Lattice and Atom Modelsofthe Empirical Electron Theory of SolidsandMolecules( EET), the effects of interstitial impurities on valence electron structures and melting pointof Ti- Alalloysareanalyzed .Becauseoftheeffectsofinterstitialimpurities,atoms hybridization statesincrease, bondstructuresareseriously anisotropic,andthe melting pointsare decreased .
基金Supported by the Science and Technology Council of Jilin Province(No 20020337)
文摘Polyamide 1010 (PA1010)/thermoplastie poly (ether urethane) elastomer (ether-based TPU) blends were prepared via melt extrusion. The crystallization kinetics and melting behavior of PA1010/ether-based TPU blends were systematically investigated using differential scanning calorimetry. The crystallization kinetics results show that the addition of ether-based TPU hinders the crystallization of PA1010, and the hindrance effect increases with the increase of the concentration of ether-based TPU. Both pure PA1010 and PA1010/ether-based TPU blends exhibit double melting peaks in the process of nonisothermal crystallization. The double melting peaks change differently with the variation of cooling rate and blend composition. The cooling rate only influences the lower melting peak; however, the blend composition influences not only the lower melting peak but also the higher melting peak. The reason for the phenomenon must be the interaction between the two compositions.
基金Note:This study was supported by China National Natural Science Foundation Grant No.49070087.
文摘The experimental study on the melting of potassic basalt and eclogite with about 2% waterat 800-1300℃ and 1.0-3.5 GPa shows that the solidi of both rocks are significantly lower thanthose obtained from the previous experiments of the same type of rocks under dry conditions,and the former which is enriched in potassium has a lower melting point than the latter. It is con-sistent with the previous study. The melting temperature of eclogite increases with pressure,whereas potassic basalt has similar properties only at 1.5—2.5 GPa and>3.0 GPa, and at 2.5—3.0 GPa the melting temperature decreases with pressure. This can be explained as follows: (1)eclogite only has one hydrous mineral amphibole and the dehydous temperature is lower than thewet solidus of the rock. (2) Amphibole exists in potassic basalt at the pressures lower than 2.5GPa and phlogopite exists at pressures higher than 2.5 GPa, and the special compositions of bothminerals determine that amphibole has a dehydration temperature higher than or close to that ofthe wet solidus of the rocks, while phlogopite has a dehydration temperature lower than that ofthe wet solidus. On the other hand the features of the continuous solidus in the experiment ofhydrous eclogite were produced by the fact that the dehydration temperature of its amphibolelower than or close to the melting temperature of the hydrous conditions. So the melting tempera-ture lowers at higher pressures. Therefore, the composition of the rocks in the lithosphere and thetypes of hydrous minerals and their stable P-T conditions are the important factors controllingthe solidi of rocks. It can quite well explain the partial melting of rocks and the origin of the lowvelocity zone in the deep lithosphere.
文摘With the aid of a slip-disentanglemnt theory, a rheological equation has been deduced about the composite system of solid-state low melting point metal and polymer. By measuring some rheological properties of the composite system composed of low melt point metal and polypropylene (LMPM/PP), the results show that LMPM has a promoter flow action upon PP when using a small amount of LMPM and, if some coupled agents are added, the promoter flow action will be remarkable. Moreover, while LMPM being added into the composite, the temperature sensitivity of system will go rip. This indicates that the system's viscosity will drop further if its temperature is increased.
基金Supported by Foundation for University Key Teacher by the Ministry of Education
文摘The low melting point metallic tin powder or alloy of tin and lead was blended with polypropylene. A kind of in situ composite has been prepared. The variations of torque were studied when the composites were mixed in Haake torque rheogeniometer. By way of capillary extrusion, effects upon rheology of the in situ composites of the low melting point metals (LMPM) and coupling agent for their different variety and content, were investigated. From flow curves, the results indicate that in situ composites mixed with the LMPM are a kind of pseudoplastic fluid. If the LMPM were melted, the higher the content of the LMPM, the lower apparent viscosity of composites. Meanwhile, when the coupling agent is added into composites , the viscosity of composite will go up first and drop then. This shows that the LMPM have a promoter flow action on the polypropylene.
文摘Poly(ε-caprolactone) (PCL) with different molecular weights was synthesized and characterized by a gelpermeation chromatograph equipped with multiple detector. The melting behavior of PCL was also studied. It was found thatthe equilibrium melting points (T_m^0) of PCL samples depend on their molecular weights. Wide angle X-ray diffractionmeasurements (WAXD) and DSC measurements showed that the crystals of the high molecular weight PCLs were moreperfect than those of the low molecular weigh ones. These results demonstrate that the concentration of the end groups ofPCL chains is the main factor that influences the melting behavior. The fusion enthalpy per repeating unit (ΔH_u) wasdetermined to be 11.3 kJ/mol for PCL.
基金This study was financially supported by the National Natural Science Foundation of China (No.50431030).
文摘With the Voter-Chen version of embedded-atom model (EAM) potential and molecular dynamics, the melting of Ni3Al alloy was simulated by one-phase (conventional) and two-phase approaches. It is shown that the simulated melting point is dependent on the potential and the simulation method. The structures of the melts obtained by different simulation methods were analyzed by the pair correlation function, the coordination number, and the distribution of atom pair type (indexed by the Honeycutt-Andersen pair analysis technique). The results show that the structures are very similar.
基金Funded by the National Science and Technology Key Project(2011ZX06004-002)the Fundamental Research Funds for the Central Universities(No.YWF-10-01-B20)
文摘Microstructural evolutions of the railway frog steel solidified under different pressure were studied using OM, FEGSEM, and TEM. The influences of pressure on the solidification, grain sizes, and morphology of carbides of the steel were analyzed. It is found that the melting point of the steel increases with the pressure and the solidified microstructure under high pressure does not vary significantly with the melting temperature. The experimental results show that the solidified microstructure consisting of complete equiaxed dendrites is remarkably refined through the increase of pressure, with the mean dendrite arm spacing of about 24, 18, and 8 μm under 3, 6, and 10 GPa, respectively. It is also revealed by TEM observation that the precipitates change from needle-like and rhombic carbide(M3C) forms during normal(atmospheric) pressure solidification into nodulized hexagonal precipitate M7C3 at 3 GPa, and M(23)C6 at 6 GPa and 10 GPa, which is associated with the undercooling and distribution of the trace elements. The diameter of the precipitates is between 80 nm and 200 nm.