A medium wave(MW)640×512(25μm)Mercury Cadmium Telluride(HgCdTe)polarimetric focal plane array(FPA)was demonstrated.The micro-polarizer array(MPA)has been carefully designed in terms of line grating structure opt...A medium wave(MW)640×512(25μm)Mercury Cadmium Telluride(HgCdTe)polarimetric focal plane array(FPA)was demonstrated.The micro-polarizer array(MPA)has been carefully designed in terms of line grating structure optimization and crosstalk suppression.A monolithic fabrication process with low damage was explored,which was verified to be compatible well with HgCdTe devices.After monolithic integration of MPA,NETD<9.5 mK was still maintained.Furthermore,to figure out the underlying mechanism that dominat⁃ed the extinction ratio(ER),specialized MPA layouts were designed,and the crosstalk was experimentally vali⁃dated as the major source that impacted ER.By expanding opaque regions at pixel edges to 4μm,crosstalk rates from adjacent pixels could be effectively reduced to approximately 2%,and promising ERs ranging from 17.32 to 27.41 were implemented.展开更多
The potentiostatic deposition of cadmium-rich CMT films onto Ti, Mo, Ni substrates from an aqueous bath was carried out. The photoelectrochemical properties of film electrodes were investigated when used in a solid-li...The potentiostatic deposition of cadmium-rich CMT films onto Ti, Mo, Ni substrates from an aqueous bath was carried out. The photoelectrochemical properties of film electrodes were investigated when used in a solid-liquid junction photoelectrochemical cell (PEC). A.C. capacitance was determined.展开更多
The short-wave HgCdTe thin film material was grown by liquid phase epitaxy on CdTe substrate,Adopt n on p injection bonding and function and flip-flop mixing process,With a low noise readout circuit,sealed with a high...The short-wave HgCdTe thin film material was grown by liquid phase epitaxy on CdTe substrate,Adopt n on p injection bonding and function and flip-flop mixing process,With a low noise readout circuit,sealed with a high airtightness cellular-metal shell,Using a four-stage Thermo Electric Cooler(TEC),320×256 Short Wave Infrared Focal Plane Cooling Detecto r available to operate at near room temperature(210K).Its main photoelectric performance are signal-to-noise ratio greater than 400,nonuniformity equivalent to 4.69%,operability equivalent to 99.76%,frame rate equivalent to 115Hz,component weight less than 150grams.展开更多
基金Supported by the self-funded project of Kunming Institute of Physics。
文摘A medium wave(MW)640×512(25μm)Mercury Cadmium Telluride(HgCdTe)polarimetric focal plane array(FPA)was demonstrated.The micro-polarizer array(MPA)has been carefully designed in terms of line grating structure optimization and crosstalk suppression.A monolithic fabrication process with low damage was explored,which was verified to be compatible well with HgCdTe devices.After monolithic integration of MPA,NETD<9.5 mK was still maintained.Furthermore,to figure out the underlying mechanism that dominat⁃ed the extinction ratio(ER),specialized MPA layouts were designed,and the crosstalk was experimentally vali⁃dated as the major source that impacted ER.By expanding opaque regions at pixel edges to 4μm,crosstalk rates from adjacent pixels could be effectively reduced to approximately 2%,and promising ERs ranging from 17.32 to 27.41 were implemented.
文摘The potentiostatic deposition of cadmium-rich CMT films onto Ti, Mo, Ni substrates from an aqueous bath was carried out. The photoelectrochemical properties of film electrodes were investigated when used in a solid-liquid junction photoelectrochemical cell (PEC). A.C. capacitance was determined.
文摘The short-wave HgCdTe thin film material was grown by liquid phase epitaxy on CdTe substrate,Adopt n on p injection bonding and function and flip-flop mixing process,With a low noise readout circuit,sealed with a high airtightness cellular-metal shell,Using a four-stage Thermo Electric Cooler(TEC),320×256 Short Wave Infrared Focal Plane Cooling Detecto r available to operate at near room temperature(210K).Its main photoelectric performance are signal-to-noise ratio greater than 400,nonuniformity equivalent to 4.69%,operability equivalent to 99.76%,frame rate equivalent to 115Hz,component weight less than 150grams.