Mesoporous molecular sieve MCM-41 has been synthesized in the extremely dense system (with H2O/Si<10) and characterized by XRD, N-2 adsorption isotherm as well as probe reactions of cracking of cumene and isomeriza...Mesoporous molecular sieve MCM-41 has been synthesized in the extremely dense system (with H2O/Si<10) and characterized by XRD, N-2 adsorption isotherm as well as probe reactions of cracking of cumene and isomerization of o-xylene.展开更多
Copper incorporated MCM-48 molecular sieve adsorbents with different Cu content have been hydrothermally synthesized. The samples have been characterized by various physicochemical methods, including X-ray diffraction...Copper incorporated MCM-48 molecular sieve adsorbents with different Cu content have been hydrothermally synthesized. The samples have been characterized by various physicochemical methods, including X-ray diffraction （XRD）, nitrogen adsorption （N2） and X-ray photoelectron spectroscopy （XPS）. The results reveal that Cu-MCM-48 with mass fraction of copper up to 10 % can still retain the uniform mesoporous framework of MCM-48. The copper in the framework of MCM-48 was easily auto-reduced to Cu（I） in N2 at high temperature, which did not alter the mesoporous structure of MCM-48. The adsorption equilibrium isotherms of ethylene and ethane on these molecular sieve adsorbents have been measured at 30℃. At 100 kPa, the adsorption capacities of ethylene on 5Cu-MCM-48 and 10Cu-MCM-48 are higher than those on MCM-48. The 10Cu-MCM-48 molecular sieve adsorbent has a higher selective adsorption ratio of ethylene to ethane, the separation factor is 3.8, and the amount of ethylene adsorbed is 11.1 ml·g ^-1.展开更多
Following hydrothermal synthesis process, MCM-41 was synthesized by using cetyltriethylammonium bromide as templating agent. The experimental results showed that MCM-41 with pore diameter in the range of 4-7 nm can be...Following hydrothermal synthesis process, MCM-41 was synthesized by using cetyltriethylammonium bromide as templating agent. The experimental results showed that MCM-41 with pore diameter in the range of 4-7 nm can be obtained by adjusting nsurf/nsi. It was proved that cetyltriethylammonium bromide is an effective templating agent for increasing pore diameter of molecular sieve MCM-41.展开更多
Mesoporous stannosilicate molecular sieves with MCM-48 structure have been synthesized by hydrothermal method and characterized by elemental analysis, XRD, N2 adsorption, UV-Visible, and FTIR. The results show that Sn...Mesoporous stannosilicate molecular sieves with MCM-48 structure have been synthesized by hydrothermal method and characterized by elemental analysis, XRD, N2 adsorption, UV-Visible, and FTIR. The results show that Sn in the synthesis gel can be incorporated into the tetrahedral lattice site of mesoporous MCM-48. The prepared SnMCM-48 exhibits catalytic performance different from Sn/MCM-48 prepared by impregnation in phenol hydroxylation.展开更多
文摘Mesoporous molecular sieve MCM-41 has been synthesized in the extremely dense system (with H2O/Si<10) and characterized by XRD, N-2 adsorption isotherm as well as probe reactions of cracking of cumene and isomerization of o-xylene.
基金Supported by the National Natural Science Foundation of China （20276029） and the Specialized Research Fund for the Doctoral Program of Higher Education of China （20040291005）.
文摘Copper incorporated MCM-48 molecular sieve adsorbents with different Cu content have been hydrothermally synthesized. The samples have been characterized by various physicochemical methods, including X-ray diffraction （XRD）, nitrogen adsorption （N2） and X-ray photoelectron spectroscopy （XPS）. The results reveal that Cu-MCM-48 with mass fraction of copper up to 10 % can still retain the uniform mesoporous framework of MCM-48. The copper in the framework of MCM-48 was easily auto-reduced to Cu（I） in N2 at high temperature, which did not alter the mesoporous structure of MCM-48. The adsorption equilibrium isotherms of ethylene and ethane on these molecular sieve adsorbents have been measured at 30℃. At 100 kPa, the adsorption capacities of ethylene on 5Cu-MCM-48 and 10Cu-MCM-48 are higher than those on MCM-48. The 10Cu-MCM-48 molecular sieve adsorbent has a higher selective adsorption ratio of ethylene to ethane, the separation factor is 3.8, and the amount of ethylene adsorbed is 11.1 ml·g ^-1.
文摘Following hydrothermal synthesis process, MCM-41 was synthesized by using cetyltriethylammonium bromide as templating agent. The experimental results showed that MCM-41 with pore diameter in the range of 4-7 nm can be obtained by adjusting nsurf/nsi. It was proved that cetyltriethylammonium bromide is an effective templating agent for increasing pore diameter of molecular sieve MCM-41.
文摘Mesoporous stannosilicate molecular sieves with MCM-48 structure have been synthesized by hydrothermal method and characterized by elemental analysis, XRD, N2 adsorption, UV-Visible, and FTIR. The results show that Sn in the synthesis gel can be incorporated into the tetrahedral lattice site of mesoporous MCM-48. The prepared SnMCM-48 exhibits catalytic performance different from Sn/MCM-48 prepared by impregnation in phenol hydroxylation.