This paper reports TiC–（Ni–Cr） metal ceramic alloy（ratio of components 50：50） with nanoscaled components formed in the surface layer and smoothly transformed into the initial inner structure throughout the mate...This paper reports TiC–（Ni–Cr） metal ceramic alloy（ratio of components 50：50） with nanoscaled components formed in the surface layer and smoothly transformed into the initial inner structure throughout the material under pulsed electron irradiation of the alloy surface. Principal changes in the surface layer are ascribed to the formation of gradient structure leading to the increase in wear resistance of the surface layer, drop of friction coefficient and improvement of specimen bending resistance when stressing on the irradiated surface side. The above changes of tribological and strength properties in the surface layer under pulsed electron irradiation become more apparent with increasing atomic mass of a plasma-forming inert gas.展开更多
The performances of mixed ceramic and sialon ceramic tools in machining nickel based alloy are tested.The negative cutting edge inclination and small tool lead angle are recommended for reducing ceramic tool failure....The performances of mixed ceramic and sialon ceramic tools in machining nickel based alloy are tested.The negative cutting edge inclination and small tool lead angle are recommended for reducing ceramic tool failure. So called“notching at depth of cut”is not actually at the depth of cutting line, but out of cutting area。 The real reason of notching is caused by shocking of “sawtooth”on sawtooth- shaped burr and fin- shaped edges of chip展开更多
文摘This paper reports TiC–（Ni–Cr） metal ceramic alloy（ratio of components 50：50） with nanoscaled components formed in the surface layer and smoothly transformed into the initial inner structure throughout the material under pulsed electron irradiation of the alloy surface. Principal changes in the surface layer are ascribed to the formation of gradient structure leading to the increase in wear resistance of the surface layer, drop of friction coefficient and improvement of specimen bending resistance when stressing on the irradiated surface side. The above changes of tribological and strength properties in the surface layer under pulsed electron irradiation become more apparent with increasing atomic mass of a plasma-forming inert gas.
文摘The performances of mixed ceramic and sialon ceramic tools in machining nickel based alloy are tested.The negative cutting edge inclination and small tool lead angle are recommended for reducing ceramic tool failure. So called“notching at depth of cut”is not actually at the depth of cutting line, but out of cutting area。 The real reason of notching is caused by shocking of “sawtooth”on sawtooth- shaped burr and fin- shaped edges of chip