直接焚烧核燃料后处理过程中产生的磷酸三丁酯(TBP)和煤油(OK)有机废液会产生磷酸,会对设备造成一定程度的腐蚀,因此在采用热解焚烧工艺处理该废液时,需掺入合适比例的中和剂和表面活性剂等添加剂,将废液配制成均匀稳定的悬浮液。中和...直接焚烧核燃料后处理过程中产生的磷酸三丁酯(TBP)和煤油(OK)有机废液会产生磷酸,会对设备造成一定程度的腐蚀,因此在采用热解焚烧工艺处理该废液时,需掺入合适比例的中和剂和表面活性剂等添加剂,将废液配制成均匀稳定的悬浮液。中和剂在热解过程中可以固定P2O5,避免磷酸生成后对设备的腐蚀。本文通过不同单因素实验研究以Ca(OH)_(2)和Mg(OH)_(2)为中和剂对配制成的TBP/OK悬浮液性能的影响,为后处理厂热解焚烧系统提供新的悬浮液配方思路。试验结果显示:当TBP含量为30%和60%时,Mg(OH)_(2)在相同TBP含量下配制成的悬浮液的最终表面黏度远大于Ca(OH)_(2),Mg(OH)_(2)和Ca(OH)_(2)在30%TBP时的最终表面黏度分别为90.36 m Pa·s和43.42 mPa·s,在60%TBP时的最终表面黏度分别为95.24 m Pa·s和75.09 m Pa·s,同时Mg(OH)_(2)的乳化速度明显优于Ca(OH)_(2),并具有更好的流动性。以Mg(OH)_(2)为中和剂的悬浮液在不同核素和DBP含量下整体稳定性更好。展开更多
Preparation of superfine magnesium hydroxide with the bittern and ammonia was studied. The properties of the products were analyzed by laser granularity, X-ray diffraction, scanning electron microscope, the limiting o...Preparation of superfine magnesium hydroxide with the bittern and ammonia was studied. The properties of the products were analyzed by laser granularity, X-ray diffraction, scanning electron microscope, the limiting oxygen index and the wetting angle measurements. The results show that the mean particle size of the magnesium hydroxide is about 230 nm with a platelet shape and the specific surface area is about 48 m2/g when the temperature is 55 ℃ , and the ammonia and bittern are instilled simultaneously during the reaction process. After the modification, the limiting oxygen index and physical chemistry performance of the magnesium hydroxide were examined. The results show that the contact angle of magnesium hydroxide is 132.5? and the limiting oxygen index is 31.5 %, indicating that the modified magnesium hydroxide is an effective flame retardant and can be applied as flame retardant additives of the macromolecule compounds such as plastic, synthetic rubber and synthetic fibre.展开更多
Dendrite growth and thermal runaway induce serious safety hazards,impeding the practical applications of lithium metal batteries(LMBs).Although extensive advances have been attained in terms of LMB safety,most work on...Dendrite growth and thermal runaway induce serious safety hazards,impeding the practical applications of lithium metal batteries(LMBs).Although extensive advances have been attained in terms of LMB safety,most work only focus on a single aspect at a time.This paper reports a multifunctional separator coated by Mg(OH)2 nanoflakes with various excellent properties including electrolyte wettability,ionic conductivity,Li+ transference number,puncture strength,thermal stability and flame retardance.When used in LMBs,the Mg(OH)2 nanoflake coatings enable uniform Li+ distributing,which makes it homogeneous to deposit lithium,realizing effective dendrite suppression and less volume expansion.Meanwhile,Mg(OH)2 coatings can ensure LMBs are in normal conditions without thermal runaway until 140 ℃.A part of lithium can be converted into Li+ ions by Mg(OH)2 during repeated charge/discharge cycles,not only reducing the risk of separator damage and consequent short circuit,but also replenishing the capacity loss of LMBs.The Mg(OH)2 nanoflakes can coat on all kinds of commercial separators to improve their performances,which offers a facile but effective strategy for fabricating multifunctional separators and a comprehensive insight into enhancing LMB safety.展开更多
This study investigated the effects of torrefaction with Mg(OH)2 on the properties of bio-oil formed from the microwave-assisted catalytic fast co-pyrolysis of straw stalk and soapstock.The effects of torrefaction tem...This study investigated the effects of torrefaction with Mg(OH)2 on the properties of bio-oil formed from the microwave-assisted catalytic fast co-pyrolysis of straw stalk and soapstock.The effects of torrefaction temperature and residence time on the yield and composition of bio-oil were discussed.Results showed that the torrefaction temperature and residence time remarkably influenced the yield and composition of bio-oil.With the increase in temperature and time,the bio-oil yield and the proportion of oxygen-containing compounds decreased,while the proportion of aromatic compounds increased.When the feedstocks were subject to torrefaction reaction for 20 min at 260°C,the proportion of oxygen-containing compounds decreased from 29.89%to 16.49%.Meanwhile,Mg(OH)2 could render the deoxidization function of torrefaction process increasingly noticeable.The proportion of the oxygen-containing compounds reached a minimum(14.41%),when the biomass-to-Mg(OH)2 ratio was 1:1.展开更多
A novel flower-like hydrated magnesium carbonate hydroxide, Mg5 （CO3 ）4 （OH）2·4H2O, with micro-structure composed of individual thin nano-sheets was synthesized using a facile solution route without the use o...A novel flower-like hydrated magnesium carbonate hydroxide, Mg5 （CO3 ）4 （OH）2·4H2O, with micro-structure composed of individual thin nano-sheets was synthesized using a facile solution route without the use of template or organic surfactant. Reaction time has an important effect on the final morphology of the product. The micro-structure and morphology of Mg5 （CO3）4 （OH）2·4H2O were characterized by means of X-ray diffractometry （XRD）, fieldemission scanning electron microscopy（FE-SEM）. Brunauer-Emmett-Teller（BET） surface areas of the samples were also measured. The probable formation mechanism of flower-like micro-structure was discussed. It was found that Mg5 （CO3）4（ OH）2·4H2O with flower-like micro-structure was a novel and efficient catalyst for the synthesis of diphenyl carbonate （DPC） by transesterification of dimethyl carbonate （DMC） with phenol.展开更多
Spherical flower-like Mg(OH)_(2) was fabricated from MgSO_(4) effluent and its adsorption performance for heavy metal ions was evaluated.The appropriate fabrication conditions are as follows:Mg^(2+)/NH4OH molar ratio ...Spherical flower-like Mg(OH)_(2) was fabricated from MgSO_(4) effluent and its adsorption performance for heavy metal ions was evaluated.The appropriate fabrication conditions are as follows:Mg^(2+)/NH4OH molar ratio of 1:0.5,temperature of 120°C and time of 1 h at Mg^(2+)concentration of 2 mol/L.Spherical flower-like Mg(OH)_(2) composed of ultra-thin sheets exhibits an excellent adsorption ability for Ni^(2+),Cu^(2+),Zn^(2+),Pb^(2+),Fe^(3+)and Co^(2+),and the adsorption reaches the equilibrium in 6 min.The maximum adsorption capacities of the studied heavy metal ions onto Mg(OH)_(2) at 20°C are 58.55,85.84,44.94,485.44,625.00 and 27.86 mg/g,respectively.The adsorption is well fitted by the Langmuir model,indicating that the adsorption is monolayer.The adsorption kinetics follows the pseudo-second-order model.Chemisorption is the operative mechanism.Spherical flower-like Mg(OH)_(2) is a qualified candidate for heavy metal ions removal.展开更多
In this paper we describe a route to produce crystalline Mg（OH）2 nanopowders from serpentinite ore distributed in the Halilovskiy array （Russia, Orenburg region）. An efficient extraction route consisting of treatm...In this paper we describe a route to produce crystalline Mg（OH）2 nanopowders from serpentinite ore distributed in the Halilovskiy array （Russia, Orenburg region）. An efficient extraction route consisting of treatment on serpentinite in 40% HNO3 at 80 ℃followed by NH4OH titration for Mg（OH）2 precipitation was demonstrated. In this study, crystalline Mg（OH）2 nanopowders have been synthesized by solvothermal reaction method using （Mg（NO3）2·6H2O） which were obtained from serpentinite, NH4OH as a precipitator, and hydroxyethylated nonylphenol as surface-active substance. Microstructure and phase composition of samples were investigated employing scanning electron microscopy （SEM） and transmission electron microscopy （TEM）, X-ray phase analysis （XRD）, and inductively coupled plasma optical emission spectroscopy （ICP-OES）. XRD reveals that Mg（OH）2 nanopowder with high purity has the brucite structure. It was found that crystalline Mg（OH）2 nanopowders exclusively consist of lamellar-like structures and the sizes of Mg（OH）2 are 30-265 nm length or width.展开更多
The high activity of metallic magnesium and alloys limits its potential in biomedical applications;in recent years,extensive efforts have been devoted to modulating this reactivity.In this work,we present Mg(OH)_(2) a...The high activity of metallic magnesium and alloys limits its potential in biomedical applications;in recent years,extensive efforts have been devoted to modulating this reactivity.In this work,we present Mg(OH)_(2) and TiO_(2)barrier coatings to reduce the degradation of magnesium alloy(Mg-Ca-Zn)surfaces.These coatings were deposited by the anodization method and the spin-coating technique,respectively.The anodized layer was coated with TiO_(2)generated from the hydrolysis of 3%weight of TTIP(Ti[OCH(CH_(3))_(2)]_(4),Titanium(IV)isopropoxide)in 2-Propanol deposited by the spin-coating method.Studying the degradation in Ringer’s solution by electrochemical impedance spectroscopy and OCP revealed a 98%reduction in pittings in uncoated samples after 14 days of immersion.The p H measurements revealed that the TiO_(2)coating reduced the alkalization of the physiological environment,keeping the pH at 6.0 values.In vitro studies of two types of bacteria(E.coli and S.aureus)exhibited zones of inhibition in the agar and activity bactericidal(kill time test).The mechanisms behind the improved degradation resistance and enhanced antibacterial activity are presented and discussed here.Surface modification with Mg(OH)_(2)/TiO_(2)coatings is a promising strategy to control the biodegradation of magnesium implants for bone regeneration.展开更多
High-quality LDH-NO_3-CO_3 whiskers were synthesized via a liquid precipitation method using Mg(NO_3)_2·6H_2O and Al(NO_3)_3·9H_2O as raw materials and Na_2CO_3-NaHCO_3 buffer solutions as precipitant. The w...High-quality LDH-NO_3-CO_3 whiskers were synthesized via a liquid precipitation method using Mg(NO_3)_2·6H_2O and Al(NO_3)_3·9H_2O as raw materials and Na_2CO_3-NaHCO_3 buffer solutions as precipitant. The whiskers were characterized by X-ray diffraction, transmission electron microscope, and Brunauer-Emmett-Teller N_2 surface area measurement. The influence of buffer solution concentration on the characteristics of the sample was investigated. The results show that the buffer solution concentration has significant impact on whiskers with intercalated structure. Overall, LDH-NO_3-CO_3 whiskers with well-defined geometry, distinct intercalated structure, high quality, and good dispersion capability can be obtained under the following conditions: buffer solution volumetric ratio of 60%, reaction temperature of 55°C, and reaction time of 269 h.展开更多
文摘直接焚烧核燃料后处理过程中产生的磷酸三丁酯(TBP)和煤油(OK)有机废液会产生磷酸,会对设备造成一定程度的腐蚀,因此在采用热解焚烧工艺处理该废液时,需掺入合适比例的中和剂和表面活性剂等添加剂,将废液配制成均匀稳定的悬浮液。中和剂在热解过程中可以固定P2O5,避免磷酸生成后对设备的腐蚀。本文通过不同单因素实验研究以Ca(OH)_(2)和Mg(OH)_(2)为中和剂对配制成的TBP/OK悬浮液性能的影响,为后处理厂热解焚烧系统提供新的悬浮液配方思路。试验结果显示:当TBP含量为30%和60%时,Mg(OH)_(2)在相同TBP含量下配制成的悬浮液的最终表面黏度远大于Ca(OH)_(2),Mg(OH)_(2)和Ca(OH)_(2)在30%TBP时的最终表面黏度分别为90.36 m Pa·s和43.42 mPa·s,在60%TBP时的最终表面黏度分别为95.24 m Pa·s和75.09 m Pa·s,同时Mg(OH)_(2)的乳化速度明显优于Ca(OH)_(2),并具有更好的流动性。以Mg(OH)_(2)为中和剂的悬浮液在不同核素和DBP含量下整体稳定性更好。
基金Project(2002-G-101) supported by the Key Program of Science and Technology of Qinghai Province, China
文摘Preparation of superfine magnesium hydroxide with the bittern and ammonia was studied. The properties of the products were analyzed by laser granularity, X-ray diffraction, scanning electron microscope, the limiting oxygen index and the wetting angle measurements. The results show that the mean particle size of the magnesium hydroxide is about 230 nm with a platelet shape and the specific surface area is about 48 m2/g when the temperature is 55 ℃ , and the ammonia and bittern are instilled simultaneously during the reaction process. After the modification, the limiting oxygen index and physical chemistry performance of the magnesium hydroxide were examined. The results show that the contact angle of magnesium hydroxide is 132.5? and the limiting oxygen index is 31.5 %, indicating that the modified magnesium hydroxide is an effective flame retardant and can be applied as flame retardant additives of the macromolecule compounds such as plastic, synthetic rubber and synthetic fibre.
基金supported by the Natural Science Project from Science and Technology Department of Henan Province (172102410034)National Natural Science Foundation of China (NSFC-U1604120)。
文摘Dendrite growth and thermal runaway induce serious safety hazards,impeding the practical applications of lithium metal batteries(LMBs).Although extensive advances have been attained in terms of LMB safety,most work only focus on a single aspect at a time.This paper reports a multifunctional separator coated by Mg(OH)2 nanoflakes with various excellent properties including electrolyte wettability,ionic conductivity,Li+ transference number,puncture strength,thermal stability and flame retardance.When used in LMBs,the Mg(OH)2 nanoflake coatings enable uniform Li+ distributing,which makes it homogeneous to deposit lithium,realizing effective dendrite suppression and less volume expansion.Meanwhile,Mg(OH)2 coatings can ensure LMBs are in normal conditions without thermal runaway until 140 ℃.A part of lithium can be converted into Li+ ions by Mg(OH)2 during repeated charge/discharge cycles,not only reducing the risk of separator damage and consequent short circuit,but also replenishing the capacity loss of LMBs.The Mg(OH)2 nanoflakes can coat on all kinds of commercial separators to improve their performances,which offers a facile but effective strategy for fabricating multifunctional separators and a comprehensive insight into enhancing LMB safety.
基金financial support from the National Natural Science Foundation of China (No. 21766019)the Key Research and Development Program of Jiangxi Province (20171BBF60023)+2 种基金the International Science & Technology Cooperation Project of China (2015DFA60170-4)the Science and Technology Research Project of Jiangxi Province Education Department (No. GJJ150213)the Guangdong Provincial Key Laboratory of New and Renewable Energy Research and Development Program (No. Y707sb1001)
文摘This study investigated the effects of torrefaction with Mg(OH)2 on the properties of bio-oil formed from the microwave-assisted catalytic fast co-pyrolysis of straw stalk and soapstock.The effects of torrefaction temperature and residence time on the yield and composition of bio-oil were discussed.Results showed that the torrefaction temperature and residence time remarkably influenced the yield and composition of bio-oil.With the increase in temperature and time,the bio-oil yield and the proportion of oxygen-containing compounds decreased,while the proportion of aromatic compounds increased.When the feedstocks were subject to torrefaction reaction for 20 min at 260°C,the proportion of oxygen-containing compounds decreased from 29.89%to 16.49%.Meanwhile,Mg(OH)2 could render the deoxidization function of torrefaction process increasingly noticeable.The proportion of the oxygen-containing compounds reached a minimum(14.41%),when the biomass-to-Mg(OH)2 ratio was 1:1.
基金Supported by the National Natural Science Foundation of China(Nos.20671011,20331010,90406002and90406024)the 111 Project(No.B07012)the Key Laboratory of Structural Chemistry Foundation(No.060017).
文摘A novel flower-like hydrated magnesium carbonate hydroxide, Mg5 （CO3 ）4 （OH）2·4H2O, with micro-structure composed of individual thin nano-sheets was synthesized using a facile solution route without the use of template or organic surfactant. Reaction time has an important effect on the final morphology of the product. The micro-structure and morphology of Mg5 （CO3）4 （OH）2·4H2O were characterized by means of X-ray diffractometry （XRD）, fieldemission scanning electron microscopy（FE-SEM）. Brunauer-Emmett-Teller（BET） surface areas of the samples were also measured. The probable formation mechanism of flower-like micro-structure was discussed. It was found that Mg5 （CO3）4（ OH）2·4H2O with flower-like micro-structure was a novel and efficient catalyst for the synthesis of diphenyl carbonate （DPC） by transesterification of dimethyl carbonate （DMC） with phenol.
基金supported by the National Natural Science Foundation of China (Nos. 51774070 and 52004165)the Science and Technology Project of Yunnan Province, China (No. 202101AS070029)
文摘Spherical flower-like Mg(OH)_(2) was fabricated from MgSO_(4) effluent and its adsorption performance for heavy metal ions was evaluated.The appropriate fabrication conditions are as follows:Mg^(2+)/NH4OH molar ratio of 1:0.5,temperature of 120°C and time of 1 h at Mg^(2+)concentration of 2 mol/L.Spherical flower-like Mg(OH)_(2) composed of ultra-thin sheets exhibits an excellent adsorption ability for Ni^(2+),Cu^(2+),Zn^(2+),Pb^(2+),Fe^(3+)and Co^(2+),and the adsorption reaches the equilibrium in 6 min.The maximum adsorption capacities of the studied heavy metal ions onto Mg(OH)_(2) at 20°C are 58.55,85.84,44.94,485.44,625.00 and 27.86 mg/g,respectively.The adsorption is well fitted by the Langmuir model,indicating that the adsorption is monolayer.The adsorption kinetics follows the pseudo-second-order model.Chemisorption is the operative mechanism.Spherical flower-like Mg(OH)_(2) is a qualified candidate for heavy metal ions removal.
基金the state on behalf of the Ministry of Education and Science of the Russian Federation of the Agreement (No. 14.577.21.0111 (22 September 2014))The unique identifier of the applied research (No. RFMEFI57714X0111)
文摘In this paper we describe a route to produce crystalline Mg（OH）2 nanopowders from serpentinite ore distributed in the Halilovskiy array （Russia, Orenburg region）. An efficient extraction route consisting of treatment on serpentinite in 40% HNO3 at 80 ℃followed by NH4OH titration for Mg（OH）2 precipitation was demonstrated. In this study, crystalline Mg（OH）2 nanopowders have been synthesized by solvothermal reaction method using （Mg（NO3）2·6H2O） which were obtained from serpentinite, NH4OH as a precipitator, and hydroxyethylated nonylphenol as surface-active substance. Microstructure and phase composition of samples were investigated employing scanning electron microscopy （SEM） and transmission electron microscopy （TEM）, X-ray phase analysis （XRD）, and inductively coupled plasma optical emission spectroscopy （ICP-OES）. XRD reveals that Mg（OH）2 nanopowder with high purity has the brucite structure. It was found that crystalline Mg（OH）2 nanopowders exclusively consist of lamellar-like structures and the sizes of Mg（OH）2 are 30-265 nm length or width.
基金financed by the FOMIX-Yucatán 2008-108160,CONACYT LAB-2009-01-123913,292692,294643,188345,and 204822 projectsthe financial support received from CONACYT。
文摘The high activity of metallic magnesium and alloys limits its potential in biomedical applications;in recent years,extensive efforts have been devoted to modulating this reactivity.In this work,we present Mg(OH)_(2) and TiO_(2)barrier coatings to reduce the degradation of magnesium alloy(Mg-Ca-Zn)surfaces.These coatings were deposited by the anodization method and the spin-coating technique,respectively.The anodized layer was coated with TiO_(2)generated from the hydrolysis of 3%weight of TTIP(Ti[OCH(CH_(3))_(2)]_(4),Titanium(IV)isopropoxide)in 2-Propanol deposited by the spin-coating method.Studying the degradation in Ringer’s solution by electrochemical impedance spectroscopy and OCP revealed a 98%reduction in pittings in uncoated samples after 14 days of immersion.The p H measurements revealed that the TiO_(2)coating reduced the alkalization of the physiological environment,keeping the pH at 6.0 values.In vitro studies of two types of bacteria(E.coli and S.aureus)exhibited zones of inhibition in the agar and activity bactericidal(kill time test).The mechanisms behind the improved degradation resistance and enhanced antibacterial activity are presented and discussed here.Surface modification with Mg(OH)_(2)/TiO_(2)coatings is a promising strategy to control the biodegradation of magnesium implants for bone regeneration.
文摘High-quality LDH-NO_3-CO_3 whiskers were synthesized via a liquid precipitation method using Mg(NO_3)_2·6H_2O and Al(NO_3)_3·9H_2O as raw materials and Na_2CO_3-NaHCO_3 buffer solutions as precipitant. The whiskers were characterized by X-ray diffraction, transmission electron microscope, and Brunauer-Emmett-Teller N_2 surface area measurement. The influence of buffer solution concentration on the characteristics of the sample was investigated. The results show that the buffer solution concentration has significant impact on whiskers with intercalated structure. Overall, LDH-NO_3-CO_3 whiskers with well-defined geometry, distinct intercalated structure, high quality, and good dispersion capability can be obtained under the following conditions: buffer solution volumetric ratio of 60%, reaction temperature of 55°C, and reaction time of 269 h.